SrTiO3 barrier layer capacitor
Assignee: MRA Laboratories Inc
•
Filing: 1981-05-06
•
Granted: 1983-12-06
•
Expires: 2001-05-06
Abstract
Abstract Formulations for a variety of air sintered ceramic barrier layer capacitors are provided wherein from 0.3 to 1.7 mole % of donor material is added to a strontium titanate and the relative amounts of strontium and titanium have been adjusted so that large-small cation balance and charge balance may be achieved by strontium vacancies, e.g. <IMAGE>
Inventors
- 👤 Ian Burn
- 👤 Stephen M. Neirman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 06:33
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1272; H01G4/1281; C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/47; H01G4/005; H01G4/008; H01G4/0085
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
173 words
A method for making an intergranular barrier layer type capacitor without heating in a reduced atmosphere comprising: (a) preparing a ceramic start mixture consisting essentially of strontium, titanium and strontium-titanate donor compounds, said donors being selected from large cations A, small cations B and combinations thereof, said start mixture being adjusted to form during sintering a ceramic compound selected from ##EQU6## and combinations thereof, to wit ##EQU7## wherein x, y and w are the atomic proportions, respectively, of said donor cations having a charge of +3, +5 and +6, so that both charge balance and large/small cation balance may be established by strontium vacancies, (V Sr )1/2x+1/2y+w therein, and wherein x+y+w is from 0.003 to 0.017; (b) forming a body of said mixture; (c) sintering said body in air to maturity to form in said body semiconductive grains and interstitial dielectric barrier layers; (d) diffusing oxidizing agents containing bismuth into said body to increase the insulation resistance of said interstitial barrier layers; and (e) forming two spaced electrodes in contact with said body.
Claim 2
Independent Claim
173 words
A method for making an intergranular barrier layer type capacitor without heating in a reduced atmosphere comprising: (a) preparing a ceramic start mixture consisting essentially of strontium, titanium and strontium-titanate donor compounds, said donors being selected from large cations A, small cations B and combinations thereof, said start mixture being adjusted to form during sintering a ceramic compound selected from ##EQU6## and combinations thereof, to wit ##EQU7## wherein x, y and w are the atomic proportions, respectively, of said donor cations having a charge of +3, +5 and +6, so that both charge balance and large/small cation balance may be established by strontium vacancies, (V Sr )1/2x+1/2y+w therein, and wherein x+y+w is from 0.003 to 0.017; (b) forming a body of said mixture; (c) sintering said body in air to maturity to form in said body semiconductive grains and interstitial dielectric barrier layers; (d) diffusing oxidizing agents containing bismuth into said body to increase the insulation resistance of said interstitial barrier layers; and (e) forming two spaced electrodes in contact with said body.
Claim 3
Dependent Claim
12 words
The method of claim 1 wherein said sum x+y+w is about 0.007.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein said sintering is about 1450° C. for at least 10 hours.
Claim 5
Dependent Claim
17 words
The method of claim 1 wherein said oxidizing agent is comprised of oxides of bismuth and copper.
Claim 6
Dependent Claim
37 words
The method of claim 1 wherein said forming said electrodes comprises, during said forming a body, interleaving between layers of said mixture, films of an electroding paste prior to said sintering, to produce a monolithic type capacitor.
Claim 7
Dependent Claim
24 words
The method of claim 5 wherein said electroding paste is comprised of an organic vehicle and metal selected from silver, palladium and combinations thereof.
Claim 8
Dependent Claim
60 words
The method of claim 5 wherein said forming of said body includes placing dummy electrode material in said body prior to said sintering, driving off said dummy material during said sintering; and wherein said forming of said electrodes includes filling the cavities left by said disappeared dummy electrodes with said electroding paste and firing said body to cure said electrodes.
Claim 9
Dependent Claim
29 words
The method of claim 7 wherein said electroding paste metal consists essentially of silver, wherein said firing is at a temperature less than the melting temperature of said metal.
Claim 10
Dependent Claim
28 words
The method of claim 7 wherein said electroding paste is additionally comprised of said oxidizing agent to simultaneously effect said forming said electrodes and diffusing said oxidizing agents.
Claim 11
Dependent Claim
20 words
The method of claim 9 wherein said electroding metal is silver and said firing is accomplished at about 900° C.
Claim 12
Dependent Claim
23 words
The method of claim 1 additionally comprising, after said sintering in air to maturity, cooling said bodies in a predominantly inert gas atmosphere.
References Cited (Backward Citations)
US3074804A
Cited
US3124478A
Cited
US3473958A
Cited
US3386856A
Cited
US3569802A
Cited
US3570113A
Cited
US3859403A
Cited
US4030004A
Cited
US3933668A
Cited
US3995300A
Cited
US4143207A
Cited
US4283753A
Cited
US4347167A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-05 | 1987-06-06 | 1987-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-05 | 1991-06-06 | 1991-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-05 | 1995-06-06 | 1995-12-06 | $7700.00 | Window Closed / Lapsed |