Low firing monolithic ceramic capacitor with high dielectric constant
Assignee: MRA Laboratories Inc
•
Filing: 1979-09-28
•
Granted: 1981-08-11
•
Expires: 1999-09-28
Abstract
Abstract The ceramic body of a monolithic ceramic capacitor consists of a granular barium titanate phase and a relatively low temperature melting intergranular phase. The body is capable of exhibiting a very high dielectric constant, e.g., over 5000, a Curie temperature of near 25 DEG C., and may be fired to maturity at 1150 DEG C. or lower and contain low cost buried electrodes. These properties obtain from a narrow range of compositions for which charge balance and large/small cation stoichiometry in the total formulation are found to be very critical. Cd, Zn, Cu, Li and Na are found to enter the grains as large acceptor cations on Ba sites and may be charge compensated by the small donor cations of charge +5, Bi, Sb, Nb and Ta or by the small donor cations of charge +6, W and Mo, on the Ti sites. At least 0.3 mole percent of glass-former cations are desirable for establishing a low melting flux during sintering but more than 2.2 mole percent glass-formers tends to reduce the dielectric constant.
Inventors
- 👤 Ian Burn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:16
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/468; C04B35/4682; C04B35/4684; H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1209; H01G4/1218; H01G4/1227
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
163 words
A ceramic capacitor comprising: a dielectric ceramic body, at least two spaced metal electrodes in contact with said body having a dielectric constant at 25° C. of at least 5000, said body containing a major portion of barium titanate, the positive ions in said body consisting essentially of: a number N D of large divalent ions selected from Ba, Pb, Sr, Ca, and combinations thereof, a number N Q of small quadravalent ions selected from Ti, Zr, Sn, Mn, and combinations thereof, a number N X of donor ions capable of having a valence of greater than +4 as a small cation selected from Bi, Nb, Sb, Ta, W, Mo, and combinations thereof, a number N CC of charge compensating acceptor ions capable of having a valence of +1 as a large cation selected from Cd, Zn, Cu, Li, Na, and combinations thereof, and a number N G of glass-forming ions selected from B, Si, Ge, P, V, and combinations thereof wherein ##EQU7##
Claim 2
Dependent Claim
163 words
A ceramic capacitor comprising: a dielectric ceramic body, at least two spaced metal electrodes in contact with said body having a dielectric constant at 25° C. of at least 5000, said body containing a major portion of barium titanate, the positive ions in said body consisting essentially of: a number N D of large divalent ions selected from Ba, Pb, Sr, Ca, and combinations thereof, a number N Q of small quadravalent ions selected from Ti, Zr, Sn, Mn, and combinations thereof, a number N X of donor ions capable of having a valence of greater than +4 as a small cation selected from Bi, Nb, Sb, Ta, W, Mo, and combinations thereof, a number N CC of charge compensating acceptor ions capable of having a valence of +1 as a large cation selected from Cd, Zn, Cu, Li, Na, and combinations thereof, and a number N G of glass-forming ions selected from B, Si, Ge, P, V, and combinations thereof wherein ##EQU7##
Claim 3
Dependent Claim
25 words
The capacitor of claim 1 wherein said electrodes are buried within said body and said metal has a melting temperature of less than 1175° C.
Claim 4
Dependent Claim
19 words
The capacitor of claim 1 wherein said metal is a palladium-silver alloy of more than 30 weight percent silver.
Claim 5
Dependent Claim
13 words
The capacitor of claim 1 wherein N X '/N G ≦1 and ##EQU8##
Claim 6
Dependent Claim
12 words
The capacitor of claim 1 wherein N X '/N G ≦1, ##EQU9##
Claim 7
Dependent Claim
14 words
The capacitor of claim 1 wherein |N D -N Q |≦3 N G .
Claim 8
Dependent Claim
18 words
The capacitor of claim 1 wherein the Curie temperature of said body is from 0° to 45° C.
Claim 9
Dependent Claim
153 words
A monolithic ceramic capacitor comprising: a dielectric ceramic body having a dielectric constant at 25° C. of at least 5000, at least two spaced electrodes in contact with said body, said body containing a major portion of barium titanate, the positive ions in said body consisting essentially of: a number N D of large divalent ions selected from Ba, Pb Sr, Ca, and combinations thereof, a number N Q of small quadravalent ions selected from Ti, Zr, Sn, Mn, and combinations thereof, a number N X of donor ions capable of having a valence of greater than +4 as a small cation selected from Bi, Nb, Ta, Sb, W, Mo, and combinations thereof, a number N Cd of charge compensating cadmium ions capable of having a valence of +1 as a large cation, and a number N G of glass-forming ions selected from B, Si, Ge, P, V, and combinations thereof wherein ##EQU10##
Claim 10
Dependent Claim
153 words
A monolithic ceramic capacitor comprising: a dielectric ceramic body having a dielectric constant at 25° C. of at least 5000, at least two spaced electrodes in contact with said body, said body containing a major portion of barium titanate, the positive ions in said body consisting essentially of: a number N D of large divalent ions selected from Ba, Pb Sr, Ca, and combinations thereof, a number N Q of small quadravalent ions selected from Ti, Zr, Sn, Mn, and combinations thereof, a number N X of donor ions capable of having a valence of greater than +4 as a small cation selected from Bi, Nb, Ta, Sb, W, Mo, and combinations thereof, a number N Cd of charge compensating cadmium ions capable of having a valence of +1 as a large cation, and a number N G of glass-forming ions selected from B, Si, Ge, P, V, and combinations thereof wherein ##EQU10##
Claim 11
Dependent Claim
42 words
The capacitor of claim 8 wherein N Cd may be partially replaced on a one for one basis by other ions capable of having a valence of 30 1 as a large cation selected from Zn, Cu, Li, Na, and combinations thereof.
Claim 12
Dependent Claim
19 words
The capacitor of claim 8 wherein the Curie temperature of said body lies between 0° C. and 45° C.
Claim 13
Dependent Claim
31 words
The capacitor of claim 8 wherein at least one of said metal electrodes is buried within said body, said buried metal electrode having a melting temperature of less than 1175° C.
Claim 14
Dependent Claim
26 words
The capacitor of claim 11 wherein said electrodes metal is a palladium silver alloy, said silver amounting to at least 30 weight percent of said alloy.
References Cited (Backward Citations)
US3811937A
Cited
US3609483A
Cited
US3900773A
Cited
US3845365A
Cited
US3977887A
Cited
US3885941A
Cited
US4081857A
Cited
US3997457A
Cited
US4106075A
Cited
US4066426A
Cited
US4101952A
Cited
US4120677A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-10 | 1985-02-09 | 1985-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-10 | 1989-02-09 | 1989-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-10 | 1993-02-09 | 1993-08-11 | $7700.00 | Window Closed / Lapsed |