Zinc-aluminum-phosphorus-silicon-oxide molecular sieve compositions

Claim 2

Crystalline molecular sieves having three-dimensional microporous framework structures of ZnO 2 , AlO 2 , PO 2 and SiO 2 tetrahedral units having an empirical chemical composition on an anhydrous basis expressed by the formula: Mr:(Zn.sub.w Al.sub.x P.sub.y Si.sub.z)O.sub.2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Zn w Al x P y Si z )O 2 and has a value of zero (0) to about 0.3; and "w", "x", "y" and "z" represent the mole fractions of zinc, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides, said mole fractions being such that they are within the pentagonal compositional area defined by points A, B, C, D, and E of FIG. 1 and each has a value of at least 0.01.

Claim 3

Crystalline molecular sieves according to claim 1 wherein the mole fractions of zinc, aluminum, phosphorus and silicon present as tetrahedral oxides are within the tetragonal compositional area defined by points a, b, c and d of FIG. 2.

Claim 4

The crystalline molecular sieves of claims 1 or 2 having a characteristic x-ray powder deffraction pattern which contains at least the d-spacings set forth in Table A.

Claim 5

The crystalline molecular sieves of claims 1 or 2 having a characteristic x-ray powder diffraction pattern which contains at least the d-spacings set forth in Table B.

Claim 6

The crystalline molecular sieves of claim 1 or 2 having a characteristic x-ray powder diffraction pattern which contains at least the d-spacings set forth in Table C.

Claim 7

The crystalline molecular sieves of claims 1 or 2 having a characteristic x-ray powder diffraction pattern which contains at least the d-spacings set forth in Table D.

Claim 8

The crystalline molecular sieves of claims 1 or 2 having a characteristic x-ray powder diffraction pattern which contains at least the d-spacings set forth in Table E.

Claim 9

The crystalline molecular sieves of claims 1 or 2 having a characteristic x-ray powder diffraction pattern which contains at least the d-spacings set forth in the Table F.

Claim 10

The crystalline molecular sieves of claims 1 or 2 having a characteristic x-ray powder diffraction pattern which contains at least the d-spacings set forth in Table G.

Claim 11

The crystalline molecular sieves of claims 1 or 2 having a characteristic x-ray powder diffraction pattern which contains at least the d-spacings set forth in Table H.

Claim 12

The crystalline molecular sieves of claims 1 or 2 having a characteristic x-ray powder diffraction pattern which contains at least the d-spacings set forth in Table J.

Claim 13

The crystalline molecular sieves of claims 1 or 2 having a characteristic x-ray powder diffraction pattern which contains at least the d-spacings set forth in Table K.

Claim 14

The crystalline molecular sieves of claims 1 or 2 having a characteristic x-ray powder diffractions pattern which contains at least one d-spacing set forth in Table L.

Claim 15

The crystalline molecular sieves of claims 1 or 2 having a characteristic x-ray powder diffraction pattern which contains at least the d-spacings set forth in Table M.

Claim 16

Process for preparing crystalline molecular sieves having three-dimensional microporous framework structures of ZnO 2 , AlO 2 , PO 2 , and SiO 2 tetrahedral units and having an empirical chemical composition on an anhydrous basis expressed by the formula: mR:(Zn.sub.w Al.sub.x P.sub.y Si.sub.z)O.sub.2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Zn w Al x P y Si z )O 2 and has a value between zero (0) to about 0.3; and "w", "x", "y", and "z" represent the mole fractions of zinc, aluminum, phosphorus, and silicon, respectively, present as tetrahedral oxides, said mole fractions being such that they are within the pentagonal compositional area defined by points A, B, C, D, and E of FIG. 1 and each has a value of at least 0.01; which comprises providing at an effective temperature and for an effective time a reaction mixture composition expressed in terms of molar oxide ratios as follows: aR:(Zn.sub.r Al.sub.s P.sub.t Si.sub.y)O.sub.2 :bH.sub.2 O wherein "R" is an organic templating agent; "a" is the amount of "R" and is an effective amount greater than zero to about 6.0; "b" has a value of from zero to about 500; and "r", "s", "t" and u represent mole fractions, respectively, of zinc, aluminum, phosphorus, and silicon in the (Zn r Al s P t Si y ) constituent, and each has a value of at least 0.01.

Claim 17

Process for preparing crystalline molecular sieves having three-dimensional microporous framework structures of ZnO 2 , AlO 2 , PO 2 , and SiO 2 tetrahedral units and having an empirical chemical composition on an anhydrous basis expressed by the formula: mR:(Zn.sub.w Al.sub.x P.sub.y Si.sub.z)O.sub.2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Zn w Al x P y Si z )O 2 and has a value between zero (0) to about 0.3; and "w", "x", "y", and "z" represent the mole fractions of zinc, aluminum, phosphorus, and silicon, respectively, present as tetrahedral oxides, said mole fractions being such that they are within the pentagonal compositional area defined by points A, B, C, D, and E of FIG. 1 and each has a value of at least 0.01; which comprises providing at an effective temperature and for an effective time a reaction mixture composition expressed in terms of molar oxide ratios as follows: aR:(Zn.sub.r Al.sub.s P.sub.t Si.sub.y)O.sub.2 :bH.sub.2 O wherein "R" is an organic templating agent; "a" is the amount of "R" and is an effective amount greater than zero to about 6.0; "b" has a value of from zero to about 500; and "r", "s", "t" and u represent mole fractions, respectively, of zinc, aluminum, phosphorus, and silicon in the (Zn r Al s P t Si y ) constituent, and each has a value of at least 0.01.

Claim 18

Process according to claim 15 wherein "r", "s", "t" and "u" are within the area defined by points F, G, H, I and J of FIG. 3.

Claim 19

Process according to claim 15 wherein the source of phosphorus in the reaction mixture is orthophosphoric acid.

Claim 20

Process according to claim 15 wherein the source of phosphorus in the reaction mixture is orthophosphoric acid and the source of aluminum is at least one compound selected from the group consisting of pseudo-boehmite and aluminum alkoxide.

Claim 21

Process according to claim 18 wherein the aluminum alkoxide is aluminum isopropoxide.

Claim 22

Process according to claim 15 wherein the source of silicon is silica.

Claim 23

Process according to claim 15 wherein the source of zinc is selected from the group consisting of oxides, hydroxides, alkoxides, acetates, nitrates, sulfates, carboxylates, organometallic zinc compounds and mixtures thereof.

Claim 24

Process according to claim 15 wherein the organic templating agent is a quaternary ammonium or quaternary phosphonium compound having the formula: R.sub.4 X.sup.+ wherein X is nitrogen or phosphorus and each R is an alkyl or aryl group containing from 1 to 8 carbon atoms.

Claim 25

Process according to claim 15 wherein the organic templating agent is an amine.

Claim 26

Process according to claim 15 wherein the templating agent is selected from the group consisting of tetrapropylammonium ion; tetraethylammonium ion; tripropylamine; triethylamine; triethanolamine; piperidine; cyclohexylamine; 2-methyl pyridine; N,N-dimethylbenzylamine; N,N-dimethylethanolamine; choline; N,N-dimethypiperazine; 1,4-diazabicyclo-(2,2,2) octane; N-methyldiethanolamine; N-methylethanolamine; n-methylpiperidine; 3-methylpiperidine; N-methylcyclohexylamine; 3-methylpyridine; 4-methylpyridine; quinuclidine; N,N'-dimethyl-1,4-diazabicyclo (2,2,2) octane ion; tetramethylammonium ion; tetrabutylammonium ion; tetrapentylammonium ion; di-n-butylamine; neopentylamine; di-n-pentylamine; isopropylamine; t-butylamine; ethylenediamine; pyrrolidine; 2-imidazolidone: di-n-propylamine; and a polymeric quaternary ammonium salt [(C 14 H 32 N 2 )(OH) 2 ] x wherein x is a value of at least 2.

Claim 27

Molecular sieve prepared by calcining the composition of claim 1 or claim 2 at a temperature sufficiently high to remove at least some of the organic templating agent present in the intracrystalline pore system.

Claim 28

The crystalline molecular sieves of claims 1 or 2 wherein the values of "w" and "z" have the following mole fraction values: "w" is ≧0.03; and "z" is ≧0.02.

Claim 29

The process of claim 15 wherein "b" has a value of from about 2 to about 500.

Claim 30

The process of claim 27 wherein "b" has a value of from about 2 to about 300.