Manufacture of nitrogen-containing crystalline metal silicates having a zeolite structure
Assignee: BASF SE
•
Filing: 1979-06-04
•
Granted: 1984-06-26
•
Expires: 1999-06-04
Abstract
Abstract A process for the manufacture of a nitrogen-containing crystalline metal silicate having a zeolite structure from silicon dioxide and a metal oxide and/or metal hydroxide, wherein the crystallization is carried out in the absence of an alkali metal in an aqueous solution of hexamethylenediamine, preferably under the autogeneous pressure of the solution at from 100° to 200° C. The zeolites are preferably used as catalysts for the reaction of methanol and/or dimethyl ether to give unsaturated hydrocarbons, the oligomerization of olefins, the alkylation of aromatics, and other conversions of hydrocarbons.
Inventors
- 👤 Laszlo Marosi
- 👤 Joachim Stabenow
- 👤 Matthias Schwarzmann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:18
CPC Classifications
C; C01; C01B; C01B33/00; C01B33/20; C01B33/26; C01B33/28; C01B33/2807; C01B33/2876; B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/70; B01J29/86; C01B35/00; C01B35/08; C01B35/10; C01B35/1009; C07; C07C; C07C1/00; C07C1/20; C07C2/00; C07C2/02; C07C2/04; C07C2/06; C07C2/08; C07C2/12; C07C2/54; C07C2/64; C07C2/66; C10; C10G; C10G3/00; C10G3/42; C10G3/44; C10G3/48; C10G3/49; C07C2529/00; C07C2529/04; C07C2529/06; C07C2529/86; C10G2400/00; C10G2400/20; C10G2400/22; Y; Y02; Y02P; Y02P30/00; Y02P30/20; Y10; Y10S; Y10S423/00; Y10S423/22; Y10S423/34
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
113 words
A process for the manufacture of a nitrogen-containing crystalline metal silicate having a zeolite structure which comprises: adding a metal oxide, metal hydroxide, metal sulfate, metal nitrate or hydrated metal oxide and a silicon dioxide source that is essentially free of alkali metal to a 5 to 90% strength aqueous solution of hexamethylenediamine to form a mixture that is essentially free of alkali metal; stirring the mixture to form a homogeneous gel; and thereafter heating the gel to form the crystalline metal silicate; wherein said metal is selected from the group consisting of aluminum, boron, arsenic, antimony, vanadium, iron and chromium, and whereby said crystalline metal silicate is essentially free of alkali metal.
Claim 2
Dependent Claim
113 words
A process for the manufacture of a nitrogen-containing crystalline metal silicate having a zeolite structure which comprises: adding a metal oxide, metal hydroxide, metal sulfate, metal nitrate or hydrated metal oxide and a silicon dioxide source that is essentially free of alkali metal to a 5 to 90% strength aqueous solution of hexamethylenediamine to form a mixture that is essentially free of alkali metal; stirring the mixture to form a homogeneous gel; and thereafter heating the gel to form the crystalline metal silicate; wherein said metal is selected from the group consisting of aluminum, boron, arsenic, antimony, vanadium, iron and chromium, and whereby said crystalline metal silicate is essentially free of alkali metal.
Claim 3
Dependent Claim
27 words
A process as set forth in claim 1, wherein the crystallization is carried out under the atuogenous pressure of the solution, at from 100° to 200° C.
Claim 4
Dependent Claim
21 words
A process as set forth in claim 1 , wherein a hexamethylenediamine solution of from 20 to 75% strength is used.
Claim 5
Dependent Claim
31 words
A process as set forth in claims 1, 2 or 3, wherein the crystalline metal silicate having a zeolite structure is calcined to remove hexamethylenediamine from the pores of the silicate.
Claim 6
Dependent Claim
16 words
A process as set forth in claims 1, 2, or 3, wherein the metal is aluminum.
Claim 7
Dependent Claim
16 words
A process as set forth in claims 1, 2, or 3, wherein the metal is boron.
Claim 8
Dependent Claim
22 words
A process as set forth in claims 1, 2 or 3, wherein pyrogenic silica is used as the source of silicon dioxide.
Claim 9
Dependent Claim
32 words
A process as set forth in claims 1, 2 or 3, wherein the source of silicon dioxide is a silica gel prepared by precipitating waterglass and washing the precipitate free of sodium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-26 | 1987-12-26 | 1988-06-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-26 | 1991-12-26 | 1992-06-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-26 | 1995-12-26 | 1996-06-26 | $7700.00 | Window Closed / Lapsed |