Synthesis of zeolite ZSM-5
Assignee: Mobil Oil AS
•
Filing: 1977-04-22
•
Granted: 1979-02-13
•
Expires: 1997-04-22
Abstract
Abstract As synthesized by conventional technique, zeolite ZSM-5 is crystallized in the presence of substantial amount of tetraalkylammonium cations, the alkyl groups of which contain 2 to 5 carbon atoms, such as, for example, tetrapropylammonium. When synthesized in the conventional way, ZSM-5 contains tetraalkylammonium cations as well as substantial amount of sodium ions. To obtain a more catalytically active form of ZSM-5, the sodium ions must be exchanged to very low levels. By synthesizing zeolite ZSM-5 according to the present method, i.e. in the presence of one or more diamines and with a specifically defined reaction mixture composition, ZSM-5 having different organic nitrogen-containing cations but the same crystal structure as conventionally prepared ZSM-5 is obtained. The ZSM-5 prepared in accordance hereto is very low in sodium content as synthesized.
Inventors
- 👤 Louis D. Rollmann
- 👤 Ernest W. Valyocsik
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 16:51
CPC Classifications
B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/40; B01J29/061; C; C01; C01B; C01B39/00; C01B39/02; C01B39/36; C01B39/38; C01B39/40; B01J2229/00; B01J2229/10; B01J2229/26; B01J2229/30; B01J2229/42; Y; Y10; Y10S; Y10S423/00; Y10S423/22
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
81 words
A synthetic crystalline aluminosilicate zeolite having, as synthesized, a formula in terms of mole ratios of oxides in the anhydrous state as follows: (0.5-10.0)R:(0-0.5)M.sub.2 O:Al.sub.2 O.sub.3 :xSiO.sub.2 wherein M is an alkali metal ion, R is an alkyldiamine selected from the group consisting of pentanediamine, hexanediamine and combinations thereof or an organic nitrogen-containing cation derived from said alkyldiamine, and x is at least 5, and having the X-ray powder diffraction pattern substantially as set forth in Table I of the specification.
Claim 2
Dependent Claim
81 words
A synthetic crystalline aluminosilicate zeolite having, as synthesized, a formula in terms of mole ratios of oxides in the anhydrous state as follows: (0.5-10.0)R:(0-0.5)M.sub.2 O:Al.sub.2 O.sub.3 :xSiO.sub.2 wherein M is an alkali metal ion, R is an alkyldiamine selected from the group consisting of pentanediamine, hexanediamine and combinations thereof or an organic nitrogen-containing cation derived from said alkyldiamine, and x is at least 5, and having the X-ray powder diffraction pattern substantially as set forth in Table I of the specification.
Claim 3
Dependent Claim
11 words
The zeolite of claim 1 wherein said alkali metal is sodium.
Claim 4
Dependent Claim
126 words
The method for preparing the crystalline aluminosilicate zeolite defined in claim 1 which comprises preparing a mixture containing sources of an alkali metal oxide, an organic nitrogen-containing oxide, an oxide of aluminum, an oxide of silicon and water and having a composition, in terms of mole ratios of oxides, within the following ranges: SiO 2 /Al 2 O 3 = 5-1000 H 2 o/siO 2 = 5-200 Oh - /siO 2 = 10 -10 -1.0 M/siO 2 = 0.01-3.0 R/siO 2 = 0.01-2.0 wherein R is an alkyldiamine selected from the group consisting of pentanediamine, hexanediamine and combinations thereof and M is an alkali metal ion, and maintaining the mixture at a temperature of at least 100° F. until the crystals of said aluminosilicate are formed.
Claim 5
Dependent Claim
19 words
The method according to claim 3 wherein the temperature is maintained between about 100° F. and about 400° F.
Claim 6
Dependent Claim
16 words
The zeolite of claim 1 wherein R is 1,6-hexanediamine or an organic nitrogen-containing cation derived therefrom.
Claim 7
Dependent Claim
16 words
The zeolite of claim 1 wherein R is 1,5-pentanediamine or an organic nitrogen-containing cation derived therefrom.
Claim 8
Dependent Claim
51 words
The method of claim 3 wherein said composition, in terms of mole ratios of oxides, is within the following ranges: SiO 2 /Al 2 O 3 = 10-500 H 2 o/siO 2 = 10-100 Oh - /siO 2 = 10 -8 14 0.8 M/siO 2 = 0.1-2.0 R/siO 2 = 0.05-1.0
Claim 9
Dependent Claim
50 words
The method of claim 3 wherein said composition, in terms of mole ratios of oxides, is within the following ranges: SiO 2 /Al 2 O 3 = 20-100 H 2 o/siO 2 = 15-60 Oh - /siO 2 = 10 -6 -0.6 M/siO 2 = 0.2-1.0 R/siO 2 = 0.1-1.0
Claim 10
Dependent Claim
177 words
The method for preparing the crystalline aluminosilicate zeolite defined in claim 1 which comprises preparing a mixture containing sources of an alkali metal oxide, an organic nitrogen-containing oxide, an oxide of aluminum, an oxide of silicon and water and having a composition, in terms of mole ratios of oxides, within the following ranges: SiO 2 /Al 2 O 3 = 5-1000 H 2 o/siO 2 = 5-200 Oh - /siO 2 = 10 -10 -1.0 M/siO 2 = 0.01-3.0 R/siO 2 = 0.01-2.0 wherein R is an alkyldiamine selected from the group consisting of pentanediamine, hexanediamine and combinations thereof and M is an alkali metal ion, maintaining the mixture at a temperature of at least 100° F. until the crystals of said aluminosilicate are formed and replacing original cations thereof, at least in part, by ion exchange with a cation or mixture of cations selected from the group consisting of hydrogen and hydrogen precursors, rare earth metals, and metals from Groups IIA, IIIA, IVA, IB, IIB, IIIB, IVB, VIB and VIII of the Periodic Table of Elements.
Claim 11
Dependent Claim
15 words
The method of claim 9 wherein said replacing ion is hydrogen or a hydrogen precursor.
Claim 12
Dependent Claim
177 words
The method for preparing the crystalline aluminosilicate zeolite defined in claim 1 which comprises preparing a mixture containing sources of an alkali metal oxide, an organic nitrogen-containing oxide, an oxide of aluminum, an oxide of silicon and water and having a composition, in terms of mole ratios of oxides, within the following ranges: SiO 2 /Al 2 O 3 = 10-500 H 2 o/siO 2 = 10-100 Oh - /siO 2 = 10 -8 -0.8 M/siO 2 = 0.1-2.0 R/siO 2 = 0.05-1.0 wherein R is an alkyldiamine selected from the group consisting of pentanediamine, hexanediamine and combinations thereof and M is an alkali metal ion, maintaining the mixture at a temperature of at least 100° F. until the crystals of said aluminosilicate are formed and replacing original cations thereof, at least in part, by ion exchange with a cation or mixture of cations selected from the group consisting of hydrogen and hydrogen precursors, rare earth metals, and metals from Groups IIA, IIIA, IVA, IB, IIB, IIIB, IVB, VIB and VIII of the Periodic Table of Elements.
Claim 13
Dependent Claim
177 words
The method for preparing the crystalline aluminosilicate zeolite defined in claim 1 which comprises preparing a mixture containing sources of an alkali metal oxide, an organic nitrogen-containing oxide, an oxide of aluminum, an oxide of silicon and water and having a composition, in terms of mole ratios of oxides, within the following ranges: SiO 2 /Al 2 O 3 = 20-100 H 2 o/siO 2 = 15-60 Oh - /siO 2 = 10 -6 -0.6 M/siO 2 = 0.2-1.0 R/siO 2 = 0.1-1.0 wherein R is an alkyldiamine selected from the group consisting of pentanediamine, hexanediamine and combinations thereof and M is an alkali metal ion, maintaining the mixture at a temperature of at least 100° F. until the crystals of said aluminosilicate are formed and replacing original cations thereof, at least in part, by ion exchange with a cation or mixture of cations selected from the group consisting of hydrogen and hydrogen precursors, rare earth metals, and metals from Groups IIA, IIIA, IVA, IB, IIB, IIIB, IVB, VIB and VIII of the Periodic Table of Elements.
Claim 14
Dependent Claim
15 words
The method of claim 11 wherein said replacing ion is hydrogen or a hydrogen precursor.
Claim 15
Dependent Claim
15 words
The method of claim 12 wherein said replacing ion is hydrogen or a hydrogen precursor.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-12 | 1982-08-14 | 1983-02-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-12 | 1986-08-14 | 1987-02-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-12 | 1990-08-14 | 1991-02-13 | $7700.00 | Window Closed / Lapsed |