Process for joining ceramic parts with a reactive conducting material
Assignee: Forschungszentrum Jülich
•
Filing: 1989-06-06
•
Granted: 1990-05-29
•
Expires: 2009-06-06
Abstract
Abstract A thin metal foil or an array of fine wires or a graphite web, mat or the ke, having electrical conductivity was interposed between clean polished surfaces of ceramic parts which are to be joined, with application of pressure. A high current electrical discharge with very short duration puts so much energy into the conducting material that it explosively vaporizes and penetrates interacts with the ceramic before the ceramic can absorb an appreciable amount of heat and before the hot material can undesirably react with the surrounding atmosphere, so that an inert atmosphere is not necessary for the process. Metals that form silicides and/or carbides are for e.g. desirable for connecting SiC parts and conducting forms of carbon such as graphite are also suitable. Precoating the surfaces to be joined, with reactive or reaction-promoting material as well as a thermal treatment of the joint may be favorable.
Inventors
- 👤 Martin Gat-Liquornik
- 👤 Aristides Naoumidis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 04:52
CPC Classifications
C; C04; C04B; C04B37/00; C04B37/003; C04B37/005; C04B2235/00; C04B2235/65; C04B2235/66; C04B2235/666; C04B2237/00; C04B2237/02; C04B2237/04; C04B2237/08; C04B2237/083; C04B2237/12; C04B2237/122; C04B2237/30; C04B2237/32; C04B2237/36; C04B2237/365; C04B2237/50; C04B2237/60; C04B2237/70; C04B2237/708; C04B2237/72
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
207 words
A thermal bonding process for joining ceramic parts which does not require an inert surrounding atmosphere, comprising the steps of: cleaning and polishing respective surfaces at which two ceramic parts are to be joined; fitting together said parts at said surfaces with insertion of between said surfaces a conducting material in a form selected from the group consisting of foils, wire arrays, webs and mats in each case of a thickness not exceeding 50 μm, said conducting material being selected from the group consisting of graphite and metallic materials; connecting said conducting material, by portions thereof accessible in the vicinity of boundaries of said fitted-together surfaces, into an electric circuit for passage of electric current through said conducting material interposed between said surfaces, and subjecting said conducting material to electric and thermal shock by passing therethrough an intense pulse of electric current of less than 100 microseconds duration, of such intensity that said conducting material interposed between said surfaces, as well as said surfaces are heated to reactive bonding temperature for said surfaces and of such brevity that said ceramic parts do not absorb enough energy through said surfaces to lower the bonding temperature and reaction of said conducting material with a surrounding atmosphere is likewise inhibited.
Claim 2
Dependent Claim
207 words
A thermal bonding process for joining ceramic parts which does not require an inert surrounding atmosphere, comprising the steps of: cleaning and polishing respective surfaces at which two ceramic parts are to be joined; fitting together said parts at said surfaces with insertion of between said surfaces a conducting material in a form selected from the group consisting of foils, wire arrays, webs and mats in each case of a thickness not exceeding 50 μm, said conducting material being selected from the group consisting of graphite and metallic materials; connecting said conducting material, by portions thereof accessible in the vicinity of boundaries of said fitted-together surfaces, into an electric circuit for passage of electric current through said conducting material interposed between said surfaces, and subjecting said conducting material to electric and thermal shock by passing therethrough an intense pulse of electric current of less than 100 microseconds duration, of such intensity that said conducting material interposed between said surfaces, as well as said surfaces are heated to reactive bonding temperature for said surfaces and of such brevity that said ceramic parts do not absorb enough energy through said surfaces to lower the bonding temperature and reaction of said conducting material with a surrounding atmosphere is likewise inhibited.
Claim 3
Dependent Claim
64 words
A process as defined in claim 1, wherein the duration of said electric pulse is not less than 1 μs and not more than 30 μs and the current intensity of said pulse and its duration are such as to release in the form of heat at least 3 kiloJoules of energy per gram of said conducting material interposed between said fitted together surfaces.
Claim 4
Dependent Claim
26 words
A process as defined in claim 1, in which said electrically conducting material is a metal and is provided in the form of a metal foil.
Claim 5
Dependent Claim
25 words
A process as defined in claim 1, in which said electrically conducting material is a metal and is provided in the form of a wire.
Claim 6
Dependent Claim
34 words
A process as defined in claim 1, wherein the thickness of said electrically conducting material interposed between said clean polished surfaces is not less than 1 μm thick nor more than 25 μm thick.
Claim 7
Dependent Claim
23 words
A process as defined in claim 1, wherein said ceramic parts are pressed together with a compressive force of at least 1 MPa.
Claim 8
Dependent Claim
52 words
A process as defined in claim 1, wherein said ceramic parts are of silicon carbide and said electrically conducting material consists essentially of an element which is capable of forming a carbide, or of forming a silicide, or both in the heat produced when said conducting material is subjected to electric shock.
Claim 9
Dependent Claim
26 words
A process as defined in claim 7, wherein said electric conducting material is selected from the group consisting of graphite, titanium, zirconium, hafnium, tantalum and tungsten.
Claim 10
Dependent Claim
39 words
A process as defined in claim 1, wherein at least one of said clean and polished surfaces, before being fitted together with the other of said cleaned and polished surfaces, is coated with a reactive or reaction promoting material.
Claim 11
Dependent Claim
47 words
A process as defined in claim 9, wherein said ceramic parts are of silicon carbide and said cleaned and polished surfaces thereof are precoated with silicon and said electrically conducting material is graphite in a form selected from the group consisting of foils, webs, mats and fibers.
Claim 12
Dependent Claim
39 words
A process as defined in claim 1, wherein following the subjecting of said conducting material to electric and thermal shock by passing an intense pulse of electric current therethrough, a following heat-treatment is provided for improving the joint strength.
References Cited (Backward Citations)
DE1571297A1
Cited
SU623240A1
Cited
DE3011907A1
Cited
DE3003186A1
Cited
EP0209672A2
Cited
US4762269A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-28 | 1993-11-27 | 1994-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-28 | 1997-11-27 | 1998-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-28 | 2001-11-27 | 2002-05-29 | $7700.00 | Window Closed / Lapsed |