US4923532A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Heat treatment for aluminum-lithium based metal matrix composites
Assignee: Honeywell International Inc
•
Filing: 1988-09-12
•
Granted: 1990-05-08
•
Expires: 2008-09-12
Abstract
Abstract An aluminum based metal matrix composite is produced from a charge containing a rapidly solidified aluminum alloy and particles of a reinforcing material present in an amount ranging from about 0.1 to 50 percent by volume of the charge. The charge is ball milled energetically to enfold metal matrix material around each of the particles while maintaining the charge in a pulverant state. Upon completion of the ball milling step, the charge is consolidated to provide a powder compact having a formable, substantially void free mass. The mass is then subject to a heat treatment during which it is solutionized at a temperature above the solvus temperature of the alloy, quenched and age hardened at a temperature below the solvus temperature of the alloy to promote precipitation of a primary strengthening Al3(Li,Zr) phase and to precipitate substantially all of the Al3(Li,Zr) phase into the metal matrix. The composite is especially suited for use in aerospace, automotive, electronic, wear resistance critical components and the like.
Inventors
- 👤 Michael S. Zedalis
- 👤 Paul S. Gilman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 22:33
CPC Classifications
C; C22; C22C; C22C32/00; C22C32/0047; C22C32/0052; C22C32/0063; B; B22; B22F; B22F3/00; B22F3/24; C22C1/00; C22C1/10
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
151 words
A process for producing a composite having a metal matrix and a reinforcing phase, comprising the steps of: (a) forming a charge containing, as ingredients, a rapidly solidified aluminum-lithium based alloy and particles of a reinforcing material present in an amount ranging from about 0.1 to 50 percent by volume of said charge; (b) ball milling the charge energetically to enfold metal matrix material around each of said particles while maintaining the charge in a pulverulant state; (c) consolidating said charge to provide a mechanically formable, substantially void-free mass; (d) subjecting said mass to a heat treatment comprising the steps of: (i) solutionizing said mass at a temperature above the solvus temperature of said alloy; (ii) rapid cooling said mass; (iii) age hardening said mass at a temperature below the solvus temperature of said alloy to promote precipitation of a primary strengthening Al 3 (Li, Zr) phase into said metal matrix.
Claim 2
Dependent Claim
151 words
A process for producing a composite having a metal matrix and a reinforcing phase, comprising the steps of: (a) forming a charge containing, as ingredients, a rapidly solidified aluminum-lithium based alloy and particles of a reinforcing material present in an amount ranging from about 0.1 to 50 percent by volume of said charge; (b) ball milling the charge energetically to enfold metal matrix material around each of said particles while maintaining the charge in a pulverulant state; (c) consolidating said charge to provide a mechanically formable, substantially void-free mass; (d) subjecting said mass to a heat treatment comprising the steps of: (i) solutionizing said mass at a temperature above the solvus temperature of said alloy; (ii) rapid cooling said mass; (iii) age hardening said mass at a temperature below the solvus temperature of said alloy to promote precipitation of a primary strengthening Al 3 (Li, Zr) phase into said metal matrix.
Claim 3
Dependent Claim
51 words
A process as recited in claim 1, wherein said rapidly solidified aluminum-lithium based alloy is prepared by a process comprising the steps of forming a melt of the aluminum-lithium based alloy and quenching the melt on a moving chill surface at a rate of at least about 10 5 ° C./sec.
Claim 4
Dependent Claim
21 words
A process as recited in claim 1, wherein, during heat treatment, said mass is rapidly cooled in an ice water bath.
Claim 5
Dependent Claim
26 words
A process as recited in claim 3, wherein said ball milling step is continued until said particles are enveloped in and bonded to said matrix material.
Claim 6
Dependent Claim
35 words
A process as recited in claim 4, wherein said consolidation step is carried out at a temperature ranging from about 250° to 550° C. said temperature being below the solidus temperature of said metal matrix.
Claim 7
Dependent Claim
25 words
A process as recited in claim 5, wherein said consolidation step comprises vacuum hot pressing at a temperature ranging from about 275° to 475° C.
Claim 8
Dependent Claim
94 words
A process as recited in claim 1, wherein said rapidly solidified aluminum-lithium based alloy is selected from the group consisting essentially of the formula Al bal Zr a Li b Mg c T d , wherein T is at least one element selected from the group consisting of Cu, Si, Sc, Ti, B, Hf, Be, Cr, Mn, Fe, Co and Ni, "a" ranges from about 0.05-0.75 at.%, "b" ranges from about 9.0-17.75 at.%, "c" ranges from about 0.45-8.5 at.% and "d" ranges from about 0.05-13 at.%, and the balance being aluminum plus incidental impurities.
Claim 9
Dependent Claim
69 words
A process as recited in claim 1, wherein said rapidly solidified aluminum-lithium based alloy is selected from the group consisting essentially of the formula Al bal Zr a Li b Mg c Cu d , wherein "a" ranges from about 0.05-0.75 at.%, "b" ranges from about 9.0-17.75 at.%, "c" rages from abut 0.45-8.5 at.% and "d" ranges from about 0.05-13 at. %, the balance being aluminum plus incidental impurities.
Claim 10
Dependent Claim
24 words
A process as recited in claim 4 wherein said particles are selected from the group consisting of carbides, borides, nitrides, oxides and intermetallic compounds.
Claim 11
Dependent Claim
23 words
A process as recited in claim 9, wherein said particles are selected from the group consisting of silicon carbide and boron carbide particles.
Claim 12
Dependent Claim
21 words
A process as recited in claim 4, wherein said particles of reinforcing material are substantially uniformly distributed within said matrix material.
Claim 13
Dependent Claim
45 words
A process as recited in claim 3, wherein said solutionizing heat treatment step is carried out at a temperature ranging from about 425° C. to 600° C. for a period of time sufficient to substantially homogenize the alloy, disolving most of the intermetallic particles therein.
Claim 14
Dependent Claim
16 words
A process as recited in claim 12, further comprising the step of stretching said solutionized alloy.
Claim 15
Dependent Claim
20 words
A process as recited in claim 3, wherein said age hardening is carried out by natural aging at ambient temperatures.
Claim 16
Dependent Claim
35 words
A process as recited in claim 3, wherein said age hardening is carried out at a temperature ranging from about 100° to 200° C. for a period of time sufficient to achieve the desired properties.
Claim 17
Dependent Claim
37 words
A process as recited in claim 15, wherein said age hardened aluminum-lithium metal matrix has an Al 3 (Li, Zr) phase and said age hardening is carried out for a time period sufficient to achieve desired properties.
Claim 18
Dependent Claim
78 words
A process as recited in claim 15, wherein the time necessary to achieve a maximum combination of hardness, strength and ductility for a composite containing 5 and 15 vol. % reinforcing particles or fibers corresponds to 0.5t to 0.65t and 0.0t to 0.2t, respectively, where t corresponds to the time necessary to achieve peak hardness and strength during aging of a monolithic alloy composed of said metal matrix at a temperature ranging from about 100° to 200° C.
Claim 19
Dependent Claim
22 words
A process as recited in claim 17, wherein said time period of said solutionizing step ranges from about 1 to 24 hours.
Claim 20
Dependent Claim
64 words
A process as recited in claim 15, wherein the time necessary to achieve a maximum combination of hardness, strength and ductility for said composite is some fraction of the time necessary to achieve peak hardness and strength during aging of a monolithic alloy composed of said metal matrix at a temperature ranging from about 100° to 200° C., said fraction being less than 1.
References Cited (Backward Citations)
DE1458349A1
Cited
US4409038A
Cited
US4532106A
Cited
US4515866A
Cited
US4452865A
Cited
US4443249A
Cited
US4594222A
Cited
US4600556A
Cited
US4518441A
Cited
US4643780A
Cited
US4801339A
Cited
US4627959A
Cited
US4624705A
Cited
US4753690A
Cited
US4770848A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-07 | 1993-11-06 | 1994-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-07 | 1997-11-06 | 1998-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-07 | 2001-11-06 | 2002-05-08 | $7700.00 | Window Closed / Lapsed |