Method of producing metal alloys with high modulus of elasticity
Assignee: Individual
•
Filing: 1984-03-02
•
Granted: 1985-05-21
•
Expires: 2004-03-02
Abstract
Abstract A method for producing metal alloys with improved properties such as a high modulus of elasticity, includes: (a) mixing fine metal powders and blending and milling said mix to a homogeneous condition, (b) forming the mix to a preliminary powder shape, said forming including exerting pressure on the mix, (c) and heating and transferring said powder shape to a hot refractory particle matrix and pressurizing said matrix so as to consolidate and densify the powder shape and to diffusion bond the powders into a solid body, (d) whereby the body may be subjected to a subsequent heat treatment serving to develop the uniformity, the grain structure, and the properties required in the alloy body.
Inventors
- 👤 Robert W. Hailey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 02:16
CPC Classifications
B; B30; B30B; B30B15/00; B30B15/30; B22; B22F; B22F1/00; B22F1/12; B22F3/00; B22F3/12; B22F3/14; B22F3/15; B30B11/00; B30B11/02; B30B11/04
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
182 words
A method for producing metal alloys with improved properties such a substantially increased moduli of elasticity, that includes (a) mixing fine metal and non-metal powders to provide an alloy mix, with the major alloying constituent by weight selected from the group that consists essentially of iron, cobalt and nickel, and with the non-metal minor alloying constituent selected from the group that consists essentially of carbon, boron and silicon, (b) milling said mix in a controlled atmosphere to a homogeneous condition that provides the desired breakdown, distribution and alloying characteristics of the powders, as well as desired handling and pressing characteristics, (c) forming the mix to a preliminary powder shape, said forming including exerting pressure on the mix, (d) and heating and transferring said powder shape to a hot refractory particle matrix and pressurizing said matrix so as to consolidate and densify the powder shape and to diffusion bond the powders to a solid body, (e) whereby the body may be subjected to a subsequent heat treatment serving to develop the uniformity, the grain structure, and the properties required in the alloy body.
Claim 2
Independent Claim
182 words
A method for producing metal alloys with improved properties such a substantially increased moduli of elasticity, that includes (a) mixing fine metal and non-metal powders to provide an alloy mix, with the major alloying constituent by weight selected from the group that consists essentially of iron, cobalt and nickel, and with the non-metal minor alloying constituent selected from the group that consists essentially of carbon, boron and silicon, (b) milling said mix in a controlled atmosphere to a homogeneous condition that provides the desired breakdown, distribution and alloying characteristics of the powders, as well as desired handling and pressing characteristics, (c) forming the mix to a preliminary powder shape, said forming including exerting pressure on the mix, (d) and heating and transferring said powder shape to a hot refractory particle matrix and pressurizing said matrix so as to consolidate and densify the powder shape and to diffusion bond the powders to a solid body, (e) whereby the body may be subjected to a subsequent heat treatment serving to develop the uniformity, the grain structure, and the properties required in the alloy body.
Claim 3
Dependent Claim
58 words
The method of claim 1 including adding to the mix minor metal alloy constituents selected from the group that includes titanium, vanadium, chromium, manganese, scandium, yttrium, zirconium, niobium, molybdenum, hafnium, tantalum, tungsten, rhenium, iron, cobalt, nickle, copper, aluminum, zinc, gallium, germanium, cadmium, indium, tin, antimony, thallium, lead, lithium, beryllium, sodium, magnesium, potassium, calcium, rubidium, strontium, cesium, and barium.
Claim 4
Dependent Claim
26 words
The method of claim 2 wherein said non-metal powder is added to the mix, in an amount between 0.10 and 3.00 weight percent of the mix.
Claim 5
Dependent Claim
31 words
The method of claim 3 wherein the mix powder includes constituents selected from the group that includes metal carbides, and oxides of the metals in the group recited in claim 3.
Claim 6
Dependent Claim
19 words
The method of claim 1 wherein said (d) step is carried out in a controlled inert or reducing atmosphere.
Claim 7
Dependent Claim
19 words
The method of claim 1 wherein said (a) step is carried out in a controlled inert or reducing atmosphere.
Claim 8
Dependent Claim
19 words
The method of claim 1 wherein said (c) step is carried out in a controlled inert or reducing atmosphere.
Claim 9
Dependent Claim
29 words
The method of claim 1 wherein said (d) step is carried out in a die containing said powder shape and matrix, the powder shape being enclosed by the matrix.
Claim 10
Dependent Claim
24 words
The method of claim 1 wherein the powders, when formed in the sub-paragraph (c) step, have particle cross dimensions less than about 30 microns.
References Cited (Backward Citations)
US3356496A
Cited
US3689259A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-20 | 1988-11-19 | 1989-05-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-20 | 1992-11-19 | 1993-05-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-20 | 1996-11-19 | 1997-05-21 | $7700.00 | Window Closed / Lapsed |