US4921725A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for coating carbon fibers with a carbide
Assignee: Centre National de la Recherche Scientifique
•
Filing: 1989-04-17
•
Granted: 1990-05-01
•
Expires: 2009-04-17
Abstract
Abstract A process for continuously coating a strand of continuous carbon filaments by means of a refractory carbide by reactive technique which includes the step of causing the strand to travel under mechanical tension with a hermetic enclosure, simultaneously, introducing into the said enclosure a carbon free gas mixture consisting of hydrogen and of a volatile compound of an element capable of forming a refractory carbide; and heating the reaction mixture consisting of the strand and the gas mixture under controlled conditions so that the formation of the carbide deposit on the filaments takes place by a chemical reaction between the carbon in the filaments and the gas mixture. Under these controlled conditions, the reaction is self-regulated to produce a thin homogenous passivation coating on each filament.
Inventors
- 👤 Jean Bouix
- 👤 Jean C. Viala
- 👤 Henri Vincent
- 👤 Christiane Vincent
- 👤 Jean L. Ponthenier
- 👤 Jacques Dazord
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 02:28
CPC Classifications
D; D01; D01F; D01F11/00; D01F11/10; D01F11/12; D01F11/126; C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/32; C23C16/44; C23C16/54; C23C16/545; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2918; Y10T428/292; Y10T428/2933; Y10T428/2938; Y10T428/294; Y10T428/2958; Y10T428/30
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
177 words
A self-regulating reactive chemical vapor deposition (RCVD) process for producing a protective passivation overlayer upon individual carbon filaments in a multi-filament strand that includes the steps of placing one or more multi-filament strands of carbon in a reaction chamber, exposing the strands in the chamber to a carbon-free gas mixture containing hydrogen and a volatile compound which is capable of reacting with each carbon filament to form a carbide passivation overlayer on said filament, maintaining the total pressure within the reaction chamber at about atmospheric pressure, heating the strands to a desired reaction temperature at which the gas phase of the volatile compound reacts with each filament to form a thin homogeneous carbide passivation overlayer over the filament surface, said reaction temperature being below the temperature at which the gas phase reacts to form brittle crystals on said filaments, controlling the time that the strands are exposed to the gas mixture to prevent carbon from diffusing through the protective passivation overlayer and further reacting with the gas mixture so that each filament retains substantially its original characteristics.
Claim 2
Dependent Claim
177 words
A self-regulating reactive chemical vapor deposition (RCVD) process for producing a protective passivation overlayer upon individual carbon filaments in a multi-filament strand that includes the steps of placing one or more multi-filament strands of carbon in a reaction chamber, exposing the strands in the chamber to a carbon-free gas mixture containing hydrogen and a volatile compound which is capable of reacting with each carbon filament to form a carbide passivation overlayer on said filament, maintaining the total pressure within the reaction chamber at about atmospheric pressure, heating the strands to a desired reaction temperature at which the gas phase of the volatile compound reacts with each filament to form a thin homogeneous carbide passivation overlayer over the filament surface, said reaction temperature being below the temperature at which the gas phase reacts to form brittle crystals on said filaments, controlling the time that the strands are exposed to the gas mixture to prevent carbon from diffusing through the protective passivation overlayer and further reacting with the gas mixture so that each filament retains substantially its original characteristics.
Claim 3
Dependent Claim
32 words
The process of claim 1 that includes the further step of adding an inert gas to the gas mixture to control the partial pressure of the volatile compound in the gas mixture.
Claim 4
Dependent Claim
32 words
The process of claim 1 wherein the volatile compound is a halide of an element selected from a group of elements consisting of titanium silicon, boron, tantalum, molybdenum, tungsten, hafnium and zirconium.
Claim 5
Dependent Claim
20 words
The process of claim 1 wherein the strands are exposed to the gas mixture for between 1.0 and 1.5 minutes.
Claim 6
Dependent Claim
21 words
The process of claim 1 wherein the strands are heated to a temperature in a range of between 1200K and 1800K.
Claim 7
Dependent Claim
27 words
The process of claim 1 that includes the further step of drawing the strands through the reaction chamber so that the filaments are under a mechanical tension.
Claim 8
Dependent Claim
11 words
The process of claim 6 wherein the strands are inductively heated.
Claim 9
Dependent Claim
41 words
The process of claim 6 that further includes the steps of mounting the filaments of each strand about a pair of spaced conductive pulleys and applying an electrical voltage over the pulleys to resistively heat each filament to the desired temperature.
Claim 10
Dependent Claim
18 words
The process of claim 8 that includes the further step of placing said pulley within the reaction chamber.
Claim 11
Dependent Claim
22 words
The process of claim 1 wherein the passivation overlayer formed on the surface of each filament is between 0.1 and 0.01 microns.
Claim 12
Dependent Claim
27 words
The process of claim 1 of cooling the gas mixture to a predetermined temperature to maintain the partial pressure of the volatile compound at a desired level.
Claim 13
Dependent Claim
18 words
The process of claim 3 wherein the volatile compound contains more than one metal of the selected group.
Claim 14
Dependent Claim
14 words
The process of claim 2 wherein the volatile compound further contains nitrogen or oxygen.
References Cited (Backward Citations)
US2929741A
Cited
US3028256A
Cited
DE1471421A1
Cited
US3369920A
Cited
US3459504A
Cited
US3679475A
Cited
US3811940A
Cited
US3692577A
Cited
US3811917A
Cited
DE2131407A1
Cited
US3897542A
Cited
US4045597A
Cited
US4066821A
Cited
JPS49101694A
Cited
JPS49101693A
Cited
US3860443A
Cited
US4131697A
Cited
US4180428A
Cited
US4343836A
Cited
US4397901A
Cited
US4686117A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-30 | 1993-10-30 | 1994-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-30 | 1997-10-30 | 1998-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-30 | 2001-10-30 | 2002-05-01 | $7700.00 | Window Closed / Lapsed |