Method for coating a continuous train of synthetic resin with a scratch resistant coating
Assignee: Roehm GmbH Darmstadt
•
Filing: 1988-10-26
•
Granted: 1990-05-01
•
Expires: 2008-10-26
Abstract
Abstract A scratch resistant coating is applied to one or both surfaces of an extruded thermoplastic synthetic resin web by passing the web through a polishing roll stack wherein at least one of the rolls has thereon a film of a material forming such a scratch resistant coating, the coating being in this way transferred from the roll to the surface of the web.
Inventors
- 👤 Heinz Vetter
- 👤 Werner Siol
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 05:47
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/02; B05D7/04; B29; B29C; B29C37/00; B29C37/0025; B29C43/00; B29C43/22; B29C43/30; B29C37/0028; B29C2037/0035; B29C43/24; B29C48/00; B29C48/03; B29C48/05; B29K; B29K2105/00; B29K2105/0002
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
227 words
A method for providing a scratch resistant coating on a continuous synthetic resin web, which method comprises (a) shaping a thermoplastic synthetic resin molding composition into said continuous web in a polishing roll stack; (b) supplying a material forming said scratch resistant coating to at least one of the rolls of said stack to form a film of said material on said roll, said material being a liquid mixture of (1) at least one monomer susceptible of free radical polymerization and having more than one polymerizable double bond and of (2) an initiator which forms free radicals under ultraviolet radiation or at a temperature at or above the temperature of said coating roll and at or below the temperature of said thermoplastic synthetic resin molding composition; (c) contacting said continuous web of thermoplastic synthetic resin molding composition and said film of material formed on said roll when the monomer or monomers in the film on said roll has been partially polymerized; (d) wrapping said web, in contact with said film of material, partially around the circumference of said roll; (e) curing said film, in contact with said web and said roll, until said web has cooled to a temperature below the softening point of said thermoplastic synthetic resin molding composition; and (f) removing said cooled web, having said cured film thereon, from the surface of said roll.
Claim 2
Independent Claim
227 words
A method for providing a scratch resistant coating on a continuous synthetic resin web, which method comprises (a) shaping a thermoplastic synthetic resin molding composition into said continuous web in a polishing roll stack; (b) supplying a material forming said scratch resistant coating to at least one of the rolls of said stack to form a film of said material on said roll, said material being a liquid mixture of (1) at least one monomer susceptible of free radical polymerization and having more than one polymerizable double bond and of (2) an initiator which forms free radicals under ultraviolet radiation or at a temperature at or above the temperature of said coating roll and at or below the temperature of said thermoplastic synthetic resin molding composition; (c) contacting said continuous web of thermoplastic synthetic resin molding composition and said film of material formed on said roll when the monomer or monomers in the film on said roll has been partially polymerized; (d) wrapping said web, in contact with said film of material, partially around the circumference of said roll; (e) curing said film, in contact with said web and said roll, until said web has cooled to a temperature below the softening point of said thermoplastic synthetic resin molding composition; and (f) removing said cooled web, having said cured film thereon, from the surface of said roll.
Claim 3
Dependent Claim
28 words
A method as in claim 1 wherein said liquid mixture is applied to said coating roll when the latter has a temperature between 40° C. and 150° C.
Claim 4
Dependent Claim
15 words
A method as in claim 1 wherein said liquid mixture contains a volatile organic liquid.
Claim 5
Dependent Claim
22 words
A method as in claim 3 wherein said liquid has a boiling point below the boiling point of said monomer or monomers.
Claim 6
Dependent Claim
17 words
A method as in claim 4 wherein said organic liquid is not susceptible to free radical polymerization.
Claim 7
Dependent Claim
42 words
A method as in claim 3 wherein said mixture containing an organic liquid is sprayed onto the surface of said coating roll and said coating roll is brought into contact with said thermoplastic molding composition after said liquid has been substantially volatilized.
Claim 8
Dependent Claim
25 words
A method as in claim 1 wherein said monomer having more than one polymerizable double bond is a compound having more than one acryloyl group.
Claim 9
Dependent Claim
26 words
A method as in claim 7 wherein said liquid mixture wherein at least 70 mole percent of said polymerizable double bonds are present as acryloyl groups.
Claim 10
Dependent Claim
26 words
A method as in claim 7 wherein at least of portion of said acryloyl groups are present in a compounds having at least three acryloyl groups.
Claim 11
Dependent Claim
18 words
A method as in claim 1 wherein said monomer or monomers has a boiling point above 140° C.
Claim 12
Dependent Claim
20 words
A method as in claim 1 wherein said initiator has a half-life of less than two minutes at 100° C.
Claim 13
Dependent Claim
13 words
A method as in claim 11 wherein said initiator is an aliphatic peroxydicarbonate.
Claim 14
Dependent Claim
26 words
A method as in claim 1 wherein said thermoplastic molding composition has a temperature between 80° C. and 350° C. when contacted with said coating roll.
Claim 15
Dependent Claim
30 words
A method as in claim 1 wherein the monomer or monomers present in the film of material on said coating roll is exposed to atmospheric oxygen during its partial polymerization.
Claim 16
Dependent Claim
42 words
A method as in claim 1 wherein said thermoplastic molding composition is brought into contact with said coating roll from 1 to 20 seconds after said film of polymerizable monomer or monomers has been applied to the surface of said coating roll.
References Cited (Backward Citations)
US3996328A
Cited
CA967436A
Cited
DE2058504A1
Cited
US3812074A
Cited
US3848045A
Cited
DE2164176A1
Cited
DE2455175A1
Cited
GB1466405A
Cited
US3978178A
Cited
US4021172A
Cited
DE2448477A1
Cited
US4100243A
Cited
DE2803144A1
Cited
GB2013132A
Cited
US4271103A
Cited
US4294782A
Cited
DE3028562A1
Cited
DE3203540A1
Cited
US4386042A
Cited
US4415509A
Cited
DE3140316A1
Cited
EP0123374A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-30 | 1993-10-30 | 1994-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-30 | 1997-10-30 | 1998-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-30 | 2001-10-30 | 2002-05-01 | $7700.00 | Window Closed / Lapsed |