Method for finishing resinous surface coverings
Assignee: Congoleum Corp
•
Filing: 1972-02-17
•
Granted: 1976-12-07
•
Expires: 1992-02-17
Abstract
Abstract A method for finishing resinous sheet material wherein the sheet material is adhered to a support surface and is passed through a pressure nip having an upper hard, very smooth, resiliently backed finishing surface and a lower support surface, the outer surface of the sheet material being maintained between about 100° F and 300° F while moving through the nip, the heat being provided from previous processing steps, without adding any additional heat at the finishing step, and subsequently cooling the sheet material after it has passed through the nip.
Inventors
- 👤 Robert E. Coffin
- 👤 Anthony N. Piacente
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 14:27
CPC Classifications
B; B29; B29C; B29C59/00; B29C59/02
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
252 words
A method for finishing resinous sheet material in a thermoplastic state comprising: a. adhering the resinous sheet material to a carrier support web, to which said resinous sheet material will adhere and from which it can be stripped, by pressing said resinous sheet material against said web at an elevated temperature within the range of 100°-375° F at which said resinous sheet material is heat softened, b. moving said adhered resinous sheet material and said carrier support web between a smooth, resiliently backed stationary finishing surface and a stationary support surface so that said finishing surface contacts the surface of said adhered resinous sheet material, c. forming a pressure nip between said surfaces by applying a pressure force perpendicular to said sheet material, d. maintaining the surface of said resinous sheet material at a temperature at which it is in a thermoplastic state while being moved through said pressure nip without the addition of heat to the resinous sheet material at said pressure nip, e. whereby said perpendicularly applied pressure force causes the material closest to the surface of said resinous sheet material to be displaced longitudinally from the material just below it thereby producing a plastic deformation of the surface of said sheet material by the sliding action of the surface of the sheet material relative to the material directly below it, f. cooling said resinous sheet material subsequent to movement through said pressure nip, and g. stripping said resinous sheet material from said carrier support web subsequent to said cooling.
Claim 2
Independent Claim
252 words
A method for finishing resinous sheet material in a thermoplastic state comprising: a. adhering the resinous sheet material to a carrier support web, to which said resinous sheet material will adhere and from which it can be stripped, by pressing said resinous sheet material against said web at an elevated temperature within the range of 100°-375° F at which said resinous sheet material is heat softened, b. moving said adhered resinous sheet material and said carrier support web between a smooth, resiliently backed stationary finishing surface and a stationary support surface so that said finishing surface contacts the surface of said adhered resinous sheet material, c. forming a pressure nip between said surfaces by applying a pressure force perpendicular to said sheet material, d. maintaining the surface of said resinous sheet material at a temperature at which it is in a thermoplastic state while being moved through said pressure nip without the addition of heat to the resinous sheet material at said pressure nip, e. whereby said perpendicularly applied pressure force causes the material closest to the surface of said resinous sheet material to be displaced longitudinally from the material just below it thereby producing a plastic deformation of the surface of said sheet material by the sliding action of the surface of the sheet material relative to the material directly below it, f. cooling said resinous sheet material subsequent to movement through said pressure nip, and g. stripping said resinous sheet material from said carrier support web subsequent to said cooling.
Claim 3
Dependent Claim
24 words
A method as in claim 1 and wherein: a. said cooling effects a release of said resinous sheet material from said carrier support web.
Claim 4
Dependent Claim
31 words
A method as in claim 1 and including: a. maintaining the outer surface of said sheet material at a temperature of at least 100° F during passage through said pressure nip.
Claim 5
Dependent Claim
18 words
A method as in claim 1 and wherein: a. said resinous sheet is formed of a thermosetting resin.
Claim 6
Dependent Claim
28 words
A method as in claim 4 and including: a. heating said sheet material after passage through said nip and prior to said cooling for curing said thermosetting resin.
Claim 7
Dependent Claim
19 words
A method as in claim 1 and wherein: a. said resinous sheet material is formed of a thermoplastic resin.
Claim 8
Dependent Claim
35 words
A method as in claim 6 and including: a. maintaining said sheet material at a temperature of above about 150° F and below the melting point of said thermoplastic resin during passage through said nip.
Claim 9
Dependent Claim
35 words
A method as in claim 4 and including: a. maintaining said sheet material at a temperature of above about 150° F and below the setting temperature of said thermosetting resin during passage through said nip.
Claim 10
Dependent Claim
38 words
A method as in claim 1 and including: a. maintaining a pressure contact area of about one inch in the direction of travel of said sheet of said finishing surface on said resinous sheet material at said nip.
Claim 11
Dependent Claim
35 words
A method as in claim 1 and including: a. moving said resinous sheet material and said carrier support web at a speed of between about 20 feet per minute and about 150 feet per minute.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-12-07 | 1980-06-07 | 1980-12-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-12-07 | 1984-06-07 | 1984-12-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-12-07 | 1988-06-07 | 1988-12-07 | $7700.00 | Window Closed / Lapsed |