Abstract The present invention provides a dewaxing process for metal powder compact which comprises the steps of embeding in alumina powder an injection-molded metal powder compact consisting of metal powder and an organic binder including low melting point substances; heating the embeded compact to a temperature of 200° C. in a chemically inert atmosphere in a dewaxing furnace, thereby removing the low melting point substances from the compact without deformation of the compact; placing the compact in a closed sintering vessel so as to keep the surrounding temperature constant and disposing the vessel in a vacuum furnace; evacuating the vacuum furnace; and removing the organic binder by heating to a temperature of 550° to 650° C. at a heating rate of 300° to 600° C./hr while supplying an inert gas into the vacuum furnace. According to the dewaxing process, the organic binder can be removed at low cost and in a reduced processing time without causing problems, like blistering and cracking.
A dewaxing process for a metal powder compact made by injection molding, the process comprising the steps of: embedding in alumina powder a compact made by injection molding a mixed molding material consisting of metal powder and an organic binder including low melting point substances; heating said embedded compact to a temperature of 200° C. in a chemically inert atmosphere in a dewaxing furnace, thereby removing said low melting point substances incorporated into said organic binder from said compact without causing deformation of said compact; placing said compact in a closed sintering vessel so as to keep the surrounding temperature of said compact constant and disposing said vessel in a vacuum furnace; evacuating said vacuum furnace; and removing said organic binder by heating to a temperature of 550° to 650° C. at a heating rate of 300° to 600° C./hr while supplying an inert gas into said vacuum furnace.
Claim 2
Dependent Claim
149 words
A dewaxing process for a metal powder compact made by injection molding, the process comprising the steps of: embedding in alumina powder a compact made by injection molding a mixed molding material consisting of metal powder and an organic binder including low melting point substances; heating said embedded compact to a temperature of 200° C. in a chemically inert atmosphere in a dewaxing furnace, thereby removing said low melting point substances incorporated into said organic binder from said compact without causing deformation of said compact; placing said compact in a closed sintering vessel so as to keep the surrounding temperature of said compact constant and disposing said vessel in a vacuum furnace; evacuating said vacuum furnace; and removing said organic binder by heating to a temperature of 550° to 650° C. at a heating rate of 300° to 600° C./hr while supplying an inert gas into said vacuum furnace.