Method of making thin film photoluminescent articles
Assignee: GIMMEL GERALD K PERSONAL REPRESENTATIVE OF ESTATE OF JOSEPH LINDMAYER
•
Filing: 1988-04-21
•
Granted: 1990-04-10
•
Expires: 2008-04-21
Abstract
Abstract An article, having particular use as an optical memory medium, includes a thin electron trapping photoluminescent film upon a substrate. In one preferred embodiment, a selected material is prepared in bulk, then applied in a relatively thin film to a substrate, and then heated to a sufficient temperature for a sufficient period of time such that the selected material acquires electron trapping characteristics and becomes photoluminescent. Some preferred methods of depositing the material are electron-beam deposition and sputtering. Some preferred methods of heating the material include photo crystallization and laser crystallization.
Inventors
- 👤 Joseph Lindmayer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 15:36
CPC Classifications
G; G11; G11C; G11C13/00; G11C13/04; C; C09; C09K; C09K11/00; C09K11/08; C09K11/77; C09K11/7766; C09K11/7767; C09K11/7768; C09K11/7783; C09K11/7784; C09K11/7786; C09K11/88; C09K11/881; C09K11/886; G01; G01T; G01T1/00; G01T1/02; G01T1/10; G01T1/11; G01T1/16; G01T1/20; G01T1/2012; G11B; G11B7/00; G11B7/004; G11B7/0045; G11B7/00453; G11B7/24; G11B7/26; G11C7/00; G11C7/005
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
102 words
A process for preparing a photoluminescent article, comprising the steps of: mixing, a base material selected from the group of alkaline earth metal sulfides and mixtures thereof, a first dopant for establishing a election trapping level, and a second dopant for establishing an communication ban for luminescence; depositing the mixture in a thickness on the order of microns such a non-interactive substrate using a vapor deposition technique; and heating the mixture and substrate to a temperature at which crystallization of said mixture occurs without degrading the integrity of the substrate, to form a continuous thin film electron trapping storage type photoluminescent article.
Claim 2
Dependent Claim
102 words
A process for preparing a photoluminescent article, comprising the steps of: mixing, a base material selected from the group of alkaline earth metal sulfides and mixtures thereof, a first dopant for establishing a election trapping level, and a second dopant for establishing an communication ban for luminescence; depositing the mixture in a thickness on the order of microns such a non-interactive substrate using a vapor deposition technique; and heating the mixture and substrate to a temperature at which crystallization of said mixture occurs without degrading the integrity of the substrate, to form a continuous thin film electron trapping storage type photoluminescent article.
Claim 3
Dependent Claim
26 words
A process as recited in claim 1, further comprising the step of providing an interlayer upon said substrate before said step of depositing said selected material.
Claim 4
Dependent Claim
23 words
A process as recited in claim 1, further comprising the step of providing an overcoat upon said material after said step of crystallization.
Claim 5
Dependent Claim
22 words
A process as recited in claim 1, wherein said temperature is in the range of about 400 to about 2000 degrees Centigrade.
Claim 6
Dependent Claim
19 words
A process as recited in claim 1, wherein said time is from about 15 seconds to about 5 minutes.
Claim 7
Dependent Claim
21 words
A process as recited in claim 1, wherein the thickness of said photoluminescent material upon said substrate is about 1 micron.
Claim 8
Dependent Claim
25 words
A process as recited in claim 1 wherein the thickness of said photoluminescent material upon said substrate is about 1 micron to about 4 microns.
Claim 9
Dependent Claim
44 words
A process as recited in claim 1, wherein said first dopant consists of about 50 to about 600 parts per million samarium; and said second dopant is a material selected from the group consisting of europium oxide, europium fluoride, europium sulfide, and cerium oxide.
Claim 10
Dependent Claim
37 words
A process as recited in claim 8, wherein said second dopant consists of about 300 to about 800 parts per million of a material selected from the group consisting of europium oxide, europium fluoride, and europium sulfide.
Claim 11
Dependent Claim
23 words
A process as recited in claim 8, wherein said second dopant consists of about 300 to about 1500 parts per million cerium oxide.
Claim 12
Dependent Claim
34 words
A process for preparing a photoluminescent article as recited in claim 1, wherein said step of mixing further comprises the mixing of lithium fluoride with the base material and the first and second dopants.
References Cited (Backward Citations)
US31847A
Cited
CA599073A
Cited
US2527365A
Cited
US2468452A
Cited
US2468714A
Cited
US2522074A
Cited
US2521124A
Cited
US2523306A
Cited
US2485903A
Cited
US2979467A
Cited
US3347693A
Cited
US3700479A
Cited
USRE31847E
Cited
US3894164A
Cited
US4348299A
Cited
US4507562A
Cited
US4510388A
Cited
WO1985000089A1
Cited
US4769549A
Cited
US4741993A
Cited
US4705952A
Cited
US4830875A
Cited
US4725344A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-09 | 1993-10-09 | 1994-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-09 | 1997-10-09 | 1998-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-09 | 2001-10-09 | 2002-04-10 | $7700.00 | Window Closed / Lapsed |