Method for forming metallic silicide films on silicon substrates by ion beam deposition
Assignee: United States Department of Energy
•
Filing: 1989-01-24
•
Granted: 1990-03-13
•
Expires: 2009-01-24
Abstract
Abstract Metallic silicide films are formed on silicon substrates by contacting the substrates with a low-energy ion beam of metal ions while moderately heating the substrate. The heating of the substrate provides for the diffusion of silicon atoms through the film as it is being formed to the surface of the film for interaction with the metal ions as they contact the diffused silicon. The metallic silicide films provided by the present invention are contaminant free, of uniform stoichiometry, large grain size, and exhibit low resistivity values which are of particular usefulness for integrated circuit production.
Inventors
- 👤 Raymond A. Zuhr
- 👤 Orin W. Holland
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:39
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
222 words
A method for forming a film of metallic silicide of essentially uniform stoichiometry on the surface of a silicon substrate, comprising the steps of contacting an exposed surface of a silicon substrate with a beam of metal ions for depositing metal ions on the surface of the substrate, with said ions being at an energy level sufficiently low to substantially minimize metal ion loss by sputtering upon said contact and to effect penetration by said metal ions into the surface of the silicon substrate to a maximum depth of less than about 2 nm, heating the silicon substrate during the contacting thereof with the beam of metal ions to a temperature sufficient to effect diffusion of silicon atoms from said substrate to contact the metal ions as they are being deposited on said surface to essentially athermally interact therewith for continuously forming a film of metallic silicide on the surface of said silicon substrate, and maintaining said contacting of said surface with said metal ions and said heating of the substrate to continue the diffusion of silicon atoms through formed portions of said film and thereby continue the metallic-silicide forming interaction for a duration sufficient to provide said film of the metallic silicide on the surface of the silicon substrate with a thickness in the range of about 1 to 300 nm.
Claim 2
Independent Claim
222 words
A method for forming a film of metallic silicide of essentially uniform stoichiometry on the surface of a silicon substrate, comprising the steps of contacting an exposed surface of a silicon substrate with a beam of metal ions for depositing metal ions on the surface of the substrate, with said ions being at an energy level sufficiently low to substantially minimize metal ion loss by sputtering upon said contact and to effect penetration by said metal ions into the surface of the silicon substrate to a maximum depth of less than about 2 nm, heating the silicon substrate during the contacting thereof with the beam of metal ions to a temperature sufficient to effect diffusion of silicon atoms from said substrate to contact the metal ions as they are being deposited on said surface to essentially athermally interact therewith for continuously forming a film of metallic silicide on the surface of said silicon substrate, and maintaining said contacting of said surface with said metal ions and said heating of the substrate to continue the diffusion of silicon atoms through formed portions of said film and thereby continue the metallic-silicide forming interaction for a duration sufficient to provide said film of the metallic silicide on the surface of the silicon substrate with a thickness in the range of about 1 to 300 nm.
Claim 3
Dependent Claim
40 words
The method claimed in claim 1, wherein said metal ion beam is at an energy level in the range of about 10 to 1000 eV at a current density in the range of about 1 to 100 micro-amps/cm 2 .
Claim 4
Dependent Claim
20 words
The method claimed in claim 1 wherein said temperature is in the range of about 400° to about 600° C.
Claim 5
Dependent Claim
32 words
The method claimed in claim 1, wherein the metal providing said metal ions is characterized by being less mobile than the silicon atoms in the metallic silicide film during the formation thereof.
Claim 6
Dependent Claim
23 words
The method claimed in claim 4, wherein the metal providing the metal ions is selected from titanium, iron, tungsten, molybdenum, tantalum and vanadiums.
Claim 7
Dependent Claim
72 words
The method claimed in claim 1, wherein the metal forming the metal ions is titanium, wherein the energy level is in the range of about 100 to 200 eV, wherein the substrate is heated to a temperature in the range of about 450° to 500° C., and wherein the metallic silicide film formed by the interaction of the titanium ions and silicon atoms on the surface of the substrate is titanium disilicide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-12 | 1993-09-11 | 1994-03-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-12 | 1997-09-11 | 1998-03-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-12 | 2001-09-11 | 2002-03-13 | $7700.00 | Window Closed / Lapsed |