Selective area nucleation and growth method for metal chemical vapor deposition using focused ion beams
Assignee: Raytheon Co
•
Filing: 1988-05-23
•
Granted: 1990-03-13
•
Expires: 2008-05-23
Abstract
Abstract A method for depositing metallic lines on an IC chip or mask is described using a focused ion beam (FIB) with a much lower ion dosage than previously required, on the order of 10 14 -10 15 ions/cm 2 . A substrate is scanned with the FIB to produce a series of nucleation sites on the substrate surface. These nucleation sites can be in an adlayer or can be produced by lattice damage or sputtering directly in the substrate material. The substrate is then exposed to a source gas containing the material to be deposited, while heated to a temperature slightly less than the spontaneous thermal decomposition temperature of the source gas. This results in a well-defined line of materials being deposited from the source gas along the line defined by the nucleation sites. The ratio of the spontaneous activation energy to the autocatalytic activation energy for the gases is preferably at least about an order of magnitude, and the FIB is preferably moved in multiple scans across the desired line. In a particular embodiment both the adlayer and source gas comprise iron pentacarbonyl, an ion dosage of 3×10 14 ions/cm 2 is used, and the substrate is heated to approximately 130° C. The ion dosage is low enough that the system is compatible with other FIB processes, such as lithography, implantation and sputtering. Applications include the fabrication and repair of both ICs and masks.
Inventors
- 👤 Randall L. Kubena
- 👤 Thomas M. Mayer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:43
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; C; C23; C23C; C23C16/00; C23C16/04; C23C16/047; C23C16/44; C23C16/48; C23C16/486; H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/067; Y; Y10; Y10S; Y10S977/00; Y10S977/84; Y10S977/89
Claims Analysis
Total Claims: 51
Claim 1
Independent Claim
119 words
A method of depositing a material along a desired locus on a substrate, comprising: scanning the substrate along said locus with a focused ion beam (FIB) at an ion dosage on the order of about 10 12 -10 16 ions cm 2 to form nucleation sites on the substrate along said locus, heating the substrate, and exposing the heated substrate to a gas which includes said material, said substrate being heated to a temperature high enough for said material to grow upon said nucleation sites from said gas and form a substantially continuous deposit along said locus, but below the gas' spontaneous thermal decomposition temperature for the period of time said substrate is heated and exposed to said gas.
Claim 2
Independent Claim
119 words
A method of depositing a material along a desired locus on a substrate, comprising: scanning the substrate along said locus with a focused ion beam (FIB) at an ion dosage on the order of about 10 12 -10 16 ions cm 2 to form nucleation sites on the substrate along said locus, heating the substrate, and exposing the heated substrate to a gas which includes said material, said substrate being heated to a temperature high enough for said material to grow upon said nucleation sites from said gas and form a substantially continuous deposit along said locus, but below the gas' spontaneous thermal decomposition temperature for the period of time said substrate is heated and exposed to said gas.
Claim 3
Dependent Claim
40 words
The method of claim 1, wherein the FIB scanning is terminated after an initial period of time, and the heating of the substrate and exposure of the substrate to said gas is continued after the termination of the FIB scanning.
Claim 4
Dependent Claim
16 words
The method of claim 2, wherein said substrate is exposed to multiple scans by said FIB.
Claim 5
Dependent Claim
22 words
The method of claim 1, wherein the substrate temperature during FIB scanning is less than its temperature when said material is grown.
Claim 6
Dependent Claim
15 words
The method of claim 4, wherein the substrate is at room temperature during FIB scanning.
Claim 7
Dependent Claim
11 words
The method of claim 1, wherein said material comprises a metal.
Claim 8
Dependent Claim
15 words
The method of claim 6, wherein said metal comprises aluminum and said gas comprises triisobutylaluminum.
Claim 9
Dependent Claim
18 words
The method of claim 7, wherein said substrate is heated to approximately 360° C. during said gas exposure.
Claim 10
Dependent Claim
16 words
The method of claim 6, wherein said metal comprises iron, and said gas comprises iron pentacarbonyl.
Claim 11
Dependent Claim
16 words
The method of claim 9, wherein said substrate is heated to approximately 130° C. during growth.
Claim 12
Dependent Claim
22 words
The method of claim 1, wherein the FIB ion dosage is on the order of 10 14 -10 16 ions/cm 2 .
Claim 13
Dependent Claim
47 words
The method of claim 1, wherein said FIB scanning is terminated after an initial period of time, and the heating of the substrate and exposure of the substrate to said gas is continued after the termination of the FIB scanning for a total of about 5-20 min.
Claim 14
Dependent Claim
29 words
The method of claim 1, wherein the ratio of the spontaneous activation energy to the autocatalytic activation energy for said gas is at least about an order of magnitude.
Claim 15
Independent Claim
157 words
A method of depositing a material along a desired locus on a substrate, comprising: exposing the substrate to a gas to form an adlayer of said gas on the substrate, scanning said adlayer along said locus with a focused ion beam (FIB) at an ion dosage on the order of about 10 12 -10 16 ions cm 2 to form nucleation sites in said adlayer upon the substrate along said locus, terminating said FIB scanning, heating said substrate, and exposing the heated substrate to a source gas which contains said material after the termination of said FIB scanning, said substrate being heated during source gas exposure to a temperature high enough for said material to grow upon said nucleation sites from said source gas and form a substantially continuous deposit along said locus, but below the source gas' spontaneous thermal decomposition temperature for the period of time said substrate is heated and exposed to said source gas.
Claim 16
Independent Claim
157 words
A method of depositing a material along a desired locus on a substrate, comprising: exposing the substrate to a gas to form an adlayer of said gas on the substrate, scanning said adlayer along said locus with a focused ion beam (FIB) at an ion dosage on the order of about 10 12 -10 16 ions cm 2 to form nucleation sites in said adlayer upon the substrate along said locus, terminating said FIB scanning, heating said substrate, and exposing the heated substrate to a source gas which contains said material after the termination of said FIB scanning, said substrate being heated during source gas exposure to a temperature high enough for said material to grow upon said nucleation sites from said source gas and form a substantially continuous deposit along said locus, but below the source gas' spontaneous thermal decomposition temperature for the period of time said substrate is heated and exposed to said source gas.
Claim 17
Dependent Claim
19 words
The method of claim 14, wherein said adlayer is scanned with multiple scans along said locus by said FIB.
Claim 18
Dependent Claim
11 words
The method of claim 14, wherein said material comprises a metal.
Claim 19
Dependent Claim
16 words
The method of claim 16, wherein said metal comprises iron, and said gas comprises iron pentacarbonyl.
Claim 20
Dependent Claim
19 words
The method of claim 17, wherein said substrate is heated to approximately 130° C. during said source gas exposure.
Claim 21
Dependent Claim
22 words
The method of claim 14, wherein the FIB ion dosage is on the order of 10 14 -10 15 ions/cm 2 .
Claim 22
Dependent Claim
48 words
The method of claim 14, wherein said FIB scanning is terminated after an initial period of time, and the heating of the substrate and exposure of the substrate to said source gas is continued after the termination of the FIB scanning for a total of about 1-2 min.
Claim 23
Dependent Claim
29 words
The method of claim 14, wherein the ratio of the spontaneous activation energy to the autocatalytic activation energy for said gases is at least about an order of magnitude.
Claim 24
Dependent Claim
25 words
The method of claim 14, wherein said substrate is heated to a temperature slightly below the spontaneous nucleation temperature of said gases during said scanning.
Claim 25
Dependent Claim
21 words
The method of claim 14, wherein the same type of gas is used for the adlayer gas and the source gas.
Claim 26
Dependent Claim
16 words
The method of claim 14, wherein different gases are used for the adlayer and source gases.
Claim 27
Dependent Claim
166 words
A focused ion beam (FIB) processing method, comprising: scanning a substrate along a desired locus with a FIB, at an ion dosage on the order of about 10 12 -10 16 ions/cm 2 to form nucleation sites on the substrate along said locus, terminating the FIB scanning, heating the substrate, exposing the heated substrate to a gas which includes a material to be deposited along said locus, said substrate being heated during said gas exposure to a temperature high enough for said material to grow upon said nucleation sites from said gas and form a substantially continuous deposit along said locus, but below the gas' spontaneous thermal decomposition temperature for the period of time said substrate is heated and exposed to said gas, and processing the substrate with at least one additional FIB process at an ion dosage on the same order of magnitude as the dosage used for scanning along said desired locus, said at least one additional FIB process comprising implantation, lithography and/or sputtering.
Claim 28
Dependent Claim
166 words
A focused ion beam (FIB) processing method, comprising: scanning a substrate along a desired locus with a FIB, at an ion dosage on the order of about 10 12 -10 16 ions/cm 2 to form nucleation sites on the substrate along said locus, terminating the FIB scanning, heating the substrate, exposing the heated substrate to a gas which includes a material to be deposited along said locus, said substrate being heated during said gas exposure to a temperature high enough for said material to grow upon said nucleation sites from said gas and form a substantially continuous deposit along said locus, but below the gas' spontaneous thermal decomposition temperature for the period of time said substrate is heated and exposed to said gas, and processing the substrate with at least one additional FIB process at an ion dosage on the same order of magnitude as the dosage used for scanning along said desired locus, said at least one additional FIB process comprising implantation, lithography and/or sputtering.
Claim 29
Dependent Claim
16 words
The method of claim 25, wherein said material comprises iron, and said gas comprises iron pentacarbonyl.
Claim 30
Dependent Claim
18 words
The method of claim 26, wherein said substrate is heated to approximately 130° C. during said gas exposure.
Claim 31
Dependent Claim
22 words
The method of claim 25, wherein the FIB ion dosage is on the order of 10 14 -10 16 ions/cm 2 .
Claim 32
Dependent Claim
132 words
An in-situ method of forming a circuit connection during the fabrication of an IC chip, comprising: scanning the chip along the path of the desired circuit connection with a focused ion beam (FIB) at an ion dosage on the order of about 10 12 -10 16 ions/cm 2 to form nucleation sites on the chip along said path, heating the chip, and exposing the heated chip to a gas which includes a conductive material, said chip being heated during said gas exposure to a temperature high enough for said conductive material to grow upon said nucleation sites from said gas and form a substantially continuous conductive deposit along said path, but below the gas' spontaneous thermal decomposition temperature for the period of time said chip is heated and exposed to said gas.
Claim 33
Dependent Claim
132 words
An in-situ method of forming a circuit connection during the fabrication of an IC chip, comprising: scanning the chip along the path of the desired circuit connection with a focused ion beam (FIB) at an ion dosage on the order of about 10 12 -10 16 ions/cm 2 to form nucleation sites on the chip along said path, heating the chip, and exposing the heated chip to a gas which includes a conductive material, said chip being heated during said gas exposure to a temperature high enough for said conductive material to grow upon said nucleation sites from said gas and form a substantially continuous conductive deposit along said path, but below the gas' spontaneous thermal decomposition temperature for the period of time said chip is heated and exposed to said gas.
Claim 34
Dependent Claim
17 words
The method of claim 29, wherein said conductive material comprises iron, and said gas comprises iron pentacarbonyl.
Claim 35
Dependent Claim
18 words
The method of claim 30, wherein said chip is heated to approximately 130° C. during said gas exposure.
Claim 36
Dependent Claim
22 words
The method of claim 29, wherein the FIB ion dosage is on the order of 10 14 -10 16 ions/cm 2 .
Claim 37
Dependent Claim
128 words
An in-situ method of repairing a circuit connection on an IC chip, comprising: scanning the chip along the path of the circuit connection with a focused ion beam (FIB) at an ion dosage on the order of about 10 12 -10 16 ions/cm 2 to form nucleation sites on the chip along said path, heating the chip, and exposing the heated chip to a gas which includes a conductive material, said chip being heated during said gas exposure to a temperature high enough for said conductive material to grow upon said nucleation sites from said gas and form a substantially continuous conductive deposit along said path, but below the gas' spontaneous thermal decomposition temperature for the period of time said chip is heated and exposed to said gas.
Claim 38
Dependent Claim
128 words
An in-situ method of repairing a circuit connection on an IC chip, comprising: scanning the chip along the path of the circuit connection with a focused ion beam (FIB) at an ion dosage on the order of about 10 12 -10 16 ions/cm 2 to form nucleation sites on the chip along said path, heating the chip, and exposing the heated chip to a gas which includes a conductive material, said chip being heated during said gas exposure to a temperature high enough for said conductive material to grow upon said nucleation sites from said gas and form a substantially continuous conductive deposit along said path, but below the gas' spontaneous thermal decomposition temperature for the period of time said chip is heated and exposed to said gas.
Claim 39
Dependent Claim
17 words
The method of claim 33, wherein said conductive material comprises iron, and said gas comprises iron pentacarbonyl.
Claim 40
Dependent Claim
18 words
The method of claim 34, wherein said chip is heated to approximately 130° C. during said gas exposure.
Claim 41
Dependent Claim
22 words
The method of claim 33, wherein the FIB ion dosage is on the order of 10 14 -10 16 ions/cm 2 .
Claim 42
Dependent Claim
138 words
An in-situ method of forming a mask for use in the fabrication of IC chips, comprising: scanning a mask substrate along paths corresponding to desired lines on the chip with a focused ion beam (FIB) at an ion dosage on the order of about 10 12 -10 16 ions/cm 2 to form nucleation site on the mask substrate along said paths, heating the mask substrate, and exposing the heated mask substrate to a gas which includes an opaque material, said mask substrate being heated during said gas exposure to a temperature high enough for said opaque material to grow upon said nucleation sites from said gas and form substantially continuous opaque deposits along said paths, but below the gas' spontaneous thermal decomposition temperature for the period of time said mask substrate is heated and exposed to said gas.
Claim 43
Dependent Claim
138 words
An in-situ method of forming a mask for use in the fabrication of IC chips, comprising: scanning a mask substrate along paths corresponding to desired lines on the chip with a focused ion beam (FIB) at an ion dosage on the order of about 10 12 -10 16 ions/cm 2 to form nucleation site on the mask substrate along said paths, heating the mask substrate, and exposing the heated mask substrate to a gas which includes an opaque material, said mask substrate being heated during said gas exposure to a temperature high enough for said opaque material to grow upon said nucleation sites from said gas and form substantially continuous opaque deposits along said paths, but below the gas' spontaneous thermal decomposition temperature for the period of time said mask substrate is heated and exposed to said gas.
Claim 44
Dependent Claim
17 words
The method of claim 37, wherein said opaque material comprises iron, and said gas comprises iron pentacarbonyl.
Claim 45
Dependent Claim
20 words
The method of claim 38, wherein said mask substrate is heated to approximately 130° C. during exposure to said gas.
Claim 46
Dependent Claim
22 words
The method of claim 37, wherein the FIB ion dosage is on the order of 10 14 -10 16 ions/cm 2 .
Claim 47
Dependent Claim
129 words
An in-situ method of repairing a line on a mask used for the fabrication of IC chip, comprising: scanning the mask along said line with a focused ion beam (FIB) at an ion dosage on the order to about 10 12 -10 16 ions/cm 2 to form nucleation sites on the mask along said line, heating the mask, and exposing the heated mask to a gas which includes an opaque material, said mask being heated during said gas exposure to a temperature high enough for said opaque material to grow upon said nucleation sites from said gas and form a substantially continuous opaque deposit along said line, but below the gas' spontaneous thermal decomposition temperature for the period of time said mask is heated and exposed to said gas.
Claim 48
Dependent Claim
129 words
An in-situ method of repairing a line on a mask used for the fabrication of IC chip, comprising: scanning the mask along said line with a focused ion beam (FIB) at an ion dosage on the order to about 10 12 -10 16 ions/cm 2 to form nucleation sites on the mask along said line, heating the mask, and exposing the heated mask to a gas which includes an opaque material, said mask being heated during said gas exposure to a temperature high enough for said opaque material to grow upon said nucleation sites from said gas and form a substantially continuous opaque deposit along said line, but below the gas' spontaneous thermal decomposition temperature for the period of time said mask is heated and exposed to said gas.
Claim 49
Dependent Claim
17 words
The method of claim 41, wherein said opaque material comprises iron, and said gas comprises iron pentacarbonyl.
Claim 50
Dependent Claim
18 words
The method of claim 42, wherein said mask is heated to approximately 130° C. during said gas exposure.
Claim 51
Dependent Claim
22 words
The method of claim 41, wherein the FIB ion dosage is on the order of 10 14 -10 16 ions/cm 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-12 | 1993-09-11 | 1994-03-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-12 | 1997-09-11 | 1998-03-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-12 | 2001-09-11 | 2002-03-13 | $7700.00 | Window Closed / Lapsed |