US4908166A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for preparing polyolefin composites containing a phase change material
Assignee: University of Dayton
•
Filing: 1988-05-27
•
Granted: 1990-03-13
•
Expires: 2008-05-27
Abstract
Abstract A composite useful in thermal energy storage, said composite being formed of a polyolefin matrix having a phase change material such as a crystalline alkyl hydrocarbon incorporated therein. The composite is useful in forming pellets, sheets or fibers having thermal energy storage characteristics; methods for forming the composite are also disclosed.
Inventors
- 👤 Ival O. Salyer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:29
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/01; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/06; C08L23/10; C09; C09K; C09K5/00; C09K5/02; C09K5/06; C09K5/063; F; F28; F28D; F28D20/00; F28D20/02; F28D20/023; C08K3/00; C08K3/34; C08K3/36; C08L2312/00; C08L2312/06; C08L91/00; C08L91/06; Y; Y02; Y02E; Y02E60/00; Y02E60/14; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
81 words
Method of making a polyolefin composite article of the type having a phase change material selected from the group consisting of crystalline alkyl hydrocarbons, crystalline fatty acids and crystalline fatty acid esters; said phase change material having a heat of fusion greater than about 30 cal/g., dispersed therein comprising forming a melt of said polyolefin and mixing said phase change material throughout said melt, imparting the desired shape to said melt to form an article, and allowing said article to cool.
Claim 2
Dependent Claim
81 words
Method of making a polyolefin composite article of the type having a phase change material selected from the group consisting of crystalline alkyl hydrocarbons, crystalline fatty acids and crystalline fatty acid esters; said phase change material having a heat of fusion greater than about 30 cal/g., dispersed therein comprising forming a melt of said polyolefin and mixing said phase change material throughout said melt, imparting the desired shape to said melt to form an article, and allowing said article to cool.
Claim 3
Dependent Claim
21 words
Method as recited in claim 1 further comprising mixing a flame retarding agent with said polyolefin and said phase change material.
Claim 4
Dependent Claim
18 words
Method as recited in claim 1 wherein said phase change material comprises a crystalline straight chain alkyl hydrocarbon.
Claim 5
Dependent Claim
28 words
Method as recited in claim 1 wherein said polyolefin is a member selected from the group consisting of polyethylene, polypropylene, polybutene, crystalline polystyrene and poly(4-methyl-pentene-1) or copolymers thereof.
Claim 6
Dependent Claim
24 words
Method as recited in claim 1 wherein said imparting comprises forming a sheet from said melt and cutting the sheet into the desired articles.
Claim 7
Dependent Claim
21 words
Method as recited in claim 1 wherein said imparting comprises extruding said melt through a die orifice to form said article.
Claim 8
Dependent Claim
103 words
Method of preparing a polyolefin composite article of the type having a phase change material selected from the group consisting of crystalline alkyl hydrocarbons, crystalline fatty acids and crystalline fatty acid esters; said phase change material having a heat of fusion greater than about 30 cal/g., and a flame retarding agent dispersed therein comprising forming a melt of said polyolefin and mixing said flame retarding agent throughout said melt, imparting the desired shape to said melt to form an article, crosslinking said article, and contacting said article with said phase change material so as to disperse said phase change material throughout said article.
Claim 9
Dependent Claim
103 words
Method of preparing a polyolefin composite article of the type having a phase change material selected from the group consisting of crystalline alkyl hydrocarbons, crystalline fatty acids and crystalline fatty acid esters; said phase change material having a heat of fusion greater than about 30 cal/g., and a flame retarding agent dispersed therein comprising forming a melt of said polyolefin and mixing said flame retarding agent throughout said melt, imparting the desired shape to said melt to form an article, crosslinking said article, and contacting said article with said phase change material so as to disperse said phase change material throughout said article.
Claim 10
Dependent Claim
28 words
Method as recited in claim 7 wherein said phase change material is in the form of a molten liquid, and said article is permeated by said molten liquid.
Claim 11
Dependent Claim
18 words
Method as recited in claim 7 wherein said phase change material comprises a crystalline straight chain alkyl hydrocarbon.
Claim 12
Dependent Claim
41 words
Method as recited in claim 7 wherein said flame retarding agent comprises a halogen donor compound that is soluble in said phase change material and wherein an antimony oxide material is also mixed with said flame retarding agent in said melt.
Claim 13
Dependent Claim
14 words
Method as recited in claim 10 wherein said soluble flame retarding agent comprises dibromoethyldibromocyclohexane.
Claim 14
Dependent Claim
28 words
Method as recited in claim 7 wherein said imparting comprises forming a sheet or strands from said melt and cutting the sheet into the desired articles or pellets.
Claim 15
Dependent Claim
16 words
Method as recited in claim 7 wherein said flame retarding agent comprises a halogenated phosphate ester.
Claim 16
Dependent Claim
80 words
Method of preparing a polyolefin composite article of the type having a phase change material and a flame retarding agent dispersed throughout said article comprising forming a melt of said polyolefin and mixing an antimony oxide in said melt, imparting the desired shape to said melt to form an article, crosslinking said article, permeating said article with said phase change material, and permeating said article with a halogen donor flame retardant compound that is soluble in said phase change material.
Claim 17
Dependent Claim
80 words
Method of preparing a polyolefin composite article of the type having a phase change material and a flame retarding agent dispersed throughout said article comprising forming a melt of said polyolefin and mixing an antimony oxide in said melt, imparting the desired shape to said melt to form an article, crosslinking said article, permeating said article with said phase change material, and permeating said article with a halogen donor flame retardant compound that is soluble in said phase change material.
References Cited (Backward Citations)
US3603106A
Cited
US3823089A
Cited
US3928357A
Cited
US4259198A
Cited
US4003426A
Cited
FR2368529A1
Cited
US4182398A
Cited
US4253983A
Cited
JPS5442380A
Cited
US4273667A
Cited
EP0022717A1
Cited
US4463799A
Cited
DE3045842A1
Cited
US4747240A
Cited
US4470917A
Cited
US4545916A
Cited
JPS59142276A
Cited
US4505953A
Cited
JPS59170180A
Cited
US4513053A
Cited
US4504402A
Cited
JPS59232164A
Cited
JPS6086191A
Cited
JPS6086188A
Cited
US4561989A
Cited
US4708812A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-12 | 1993-09-11 | 1994-03-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-12 | 1997-09-11 | 1998-03-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-12 | 2001-09-11 | 2002-03-13 | $7700.00 | Window Closed / Lapsed |