Optical fiber provided with a synthetic resin coating
Assignee: Draka Comteq BV
•
Filing: 1988-09-29
•
Granted: 1990-02-27
•
Expires: 2008-09-29
Abstract
Abstract An optical fiber provided with a synthetic resin coating, comprising a glass fibre, a first enveloping layer of a synthetic rubber having a modulus of elasticity from 0.1 to 10 MPa and a subsequent enveloping layer of a synthetic resin having a larger modulus of elasticity than the first layer, obtains a large mechanical resistance and a high insensitivity to temperature variations within the range from -60° C. to +80° C., in that the thickness of the first layer is from 5 to 20 μm and in that the modulus of elasticity of the second layer is more than 1000 MPa.
Inventors
- 👤 Dirk J. Broer
- 👤 Cornelis M. G. Jochem
- 👤 Theodorus M. Meeuwsen
- 👤 Daniel C. L. Vangheluwe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 21:16
CPC Classifications
C; C03; C03C; C03C25/00; C03C25/10; C03C25/104; C03C25/1065; G; G02; G02B; G02B6/00; G02B6/02; G02B6/02395; G02B6/44; G02B6/4401; G02B6/4429; G02B6/4438
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
81 words
An optical fiber having a synthetic resin coating and comprising a glass fiber, a first enveloping layer of a synthetic rubber having a modulus of elasticity of from 0.1 to 10 MPa, and a second enveloping layer of a synthetic resin having a modulus of elasticity larger than that of the first layer, wherein the thickness of the first layer is of from 5 to 20 μm and the modulus of elasticity of the second layer is more than 1000 MPa.
Claim 2
Dependent Claim
81 words
An optical fiber having a synthetic resin coating and comprising a glass fiber, a first enveloping layer of a synthetic rubber having a modulus of elasticity of from 0.1 to 10 MPa, and a second enveloping layer of a synthetic resin having a modulus of elasticity larger than that of the first layer, wherein the thickness of the first layer is of from 5 to 20 μm and the modulus of elasticity of the second layer is more than 1000 MPa.
Claim 3
Dependent Claim
42 words
An optical fiber as claimed in claim 1, wherein both layers are formed from curable synthetic resin compositions which are applied immediately after the optical fiber has been drawn and which are made to cure by exposure to electrons or UV light.
Claim 4
Dependent Claim
34 words
An optical fiber as claimed in claim 2, wherein the second hard layer is formed from a curable synthetic resin composition which comprises ethoxylated bisphenol-A diacrylate, isocyanurate triacrylate and at least one polyurethane acrylate.
Claim 5
Dependent Claim
28 words
An optical fiber as claimed in claim 2, wherein the first soft layer is formed from a curable synthetic resin composition comprising at least one polyether urethane acrylate.
Claim 6
Dependent Claim
71 words
An optical fiber as claimed in claim 1 wherein the first layer is formed from a curable synthetic resin composition comprising about 68% by weight of a polyether urethane acrylate, about 20% by weight of 2-phenoxy-ethyl acrylate, about 6% by weight of tripropylene glycol diacrylate, about 2% by weight of 2,2-dimethoxy-2-phenylacetophenone, about 2% by weight of p-chloro-benzpohenone-2-ethoxyethylacrylate and about 2% by weight of a mixture of mono and di-2-acryloyl ethoxy phosphate.
Claim 7
Dependent Claim
55 words
An optical fiber as claimed in claim 1 or 5 wherein the second layer is formed from a curable synthetic resin composition comprising about 19.1% by weight of a polyester urethane acrylate, about 23.9% by weight of an isocyanurate tiacrylate, about 4.5% by weight of 2,2-dimethoxy-2-phenylacetophenone, and about 52.5% by weight of ethoxylated bisphenol-A diacrylate.
Claim 8
Dependent Claim
63 words
An optical fiber as claimed in claim 1 or 5 wherein the second layer is formed from a curable synthetic resin composition comprising about 10% by weight of a polyester urethane acrylate, about 18% by weight of an isocyanurate triacrylate, about 10% by weight of an epoxyacrylate, about 4% by weight of 1-hydroxycyclohexylphenyl ketone and about 58% by weight of ethoxylated bisphenol-A diacrylate.
References Cited (Backward Citations)
US4213672A
Cited
US4239335A
Cited
US4763981A
Cited
US4718748A
Cited
US4738509A
Cited
US4741596A
Cited
US4741597A
Cited
US4733941A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-26 | 1993-08-28 | 1994-02-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-26 | 1997-08-28 | 1998-02-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-26 | 2001-08-28 | 2002-02-27 | $7700.00 | Window Closed / Lapsed |