Optical fibre comprising a synthetic resin cladding and method of and device for manufacturing such an optical fibre
Assignee: Plasma Optical Fibre BV
•
Filing: 1986-09-02
•
Granted: 1988-03-29
•
Expires: 2006-09-02
Abstract
Abstract The invention provides an optical fibre having a synthetic resin cladding, comprising a glass fibre, a first cladding layer of a synthetic rubber and a subsequent cladding layer of a synthetic resin the molecules of which are oriented substantially in the longitudinal direction of the glass fibre, in which a low application temperature, a low pressure and a high cladding rate can be used in that the oriented synthetic resin is formed from a curable synthetic resin composition which comprises one or more oligomeric compounds the molecules of which comprise reactive groups and the molecular weight of which is smaller than 5000. The invention further relates to a method of manufacturing such an optical fibre and a device for cladding a glass fibre with a curable synthetic resin composition in which an elongation flow in the curable synthetic resin composition is produced to effect the orientation in the curable synthetic resin composition.
Inventors
- 👤 Dirk J. Broer
- 👤 Grietje N. Mol
- 👤 Cornelis M. G. Jochem
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 08:34
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/44; G02B6/4401; G02B6/4402; C; C03; C03C; C03C25/00; C03C25/10; C03C25/104; C03C25/1065; C03C25/12; C03C25/18
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
83 words
An optical fibre having a synthetic resin cladding, comprising a glass fibre, a first cladding layer of a synthetic rubber and a subsequent cladding layer of a synthetic resin the molecules of which are oriented mainly in the longitudinal direction of the glass fibre, characterized in that the oriented synthetic resin is formed from a curable synthetic resin composition which comprises one or more oligomeric compounds the molecules of which comprise reactive groups and the molecular weight of which is smaller than 5000.
Claim 2
Dependent Claim
83 words
An optical fibre having a synthetic resin cladding, comprising a glass fibre, a first cladding layer of a synthetic rubber and a subsequent cladding layer of a synthetic resin the molecules of which are oriented mainly in the longitudinal direction of the glass fibre, characterized in that the oriented synthetic resin is formed from a curable synthetic resin composition which comprises one or more oligomeric compounds the molecules of which comprise reactive groups and the molecular weight of which is smaller than 5000.
Claim 3
Dependent Claim
26 words
An optical fibre as claimed in claim 1, characterized in that the oligomeric compound is selected from the group formed by polyesterurethane acrylates and polyetherurethane acrylates.
Claim 4
Independent Claim
103 words
A method of manufacturing an optical fibre, characterized in that a curable synthetic resin composition which comprises one or more oligomeric compounds the molecules of which comprise reactive groups and the molecular weight of which is smaller than 5000, is applied to a glass fibre having at least one enveloping layer of synthetic rubber, in which the molecules of the curable synthetic resin composition are oriented during application to the glass fibre, after which the curable synthetic resin composition is made to cure while forming a synthetic resin the molecules of which are oriented substantially in the longitudinal direction of the optical fibre.
Claim 5
Independent Claim
103 words
A method of manufacturing an optical fibre, characterized in that a curable synthetic resin composition which comprises one or more oligomeric compounds the molecules of which comprise reactive groups and the molecular weight of which is smaller than 5000, is applied to a glass fibre having at least one enveloping layer of synthetic rubber, in which the molecules of the curable synthetic resin composition are oriented during application to the glass fibre, after which the curable synthetic resin composition is made to cure while forming a synthetic resin the molecules of which are oriented substantially in the longitudinal direction of the optical fibre.
Claim 6
Dependent Claim
33 words
A method as claimed in claim 3, characterized in that the molecules of the curable synthetic resin composition are oriented during the application to the glass fibre by means of an elongation flow.
Claim 7
Dependent Claim
29 words
A method as claimed in claim 4, characterized in that a sub-atmospheric pressure is applied in the space between the glass fibre and the applied curable synthetic resin composition.
Claim 8
Dependent Claim
24 words
A method as claimed in claim 3, characterized in that the curable synthetic resin composition is made to cure by means of actinic radiation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-29 | 1991-09-28 | 1992-03-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-29 | 1995-09-28 | 1996-03-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-29 | 1999-09-28 | 2000-03-29 | $7700.00 | Window Closed / Lapsed |