Abstract
Abstract Optical fibers having ultraviolet-cured coatings and reduced optical transmission losses are produced. An ultraviolet-absorbing material is incorporated in at least one coating layer. This reduces damage in the glass fiber due to the ultraviolet-curing radiation, while still allowing rapid curing of the coating. Single layer coatings and dual layer coatings are described. A single layer coating having reduced microbending losses due to partial curing of the inner portion of the coating is also described.
Inventors
- 👤 Lee L. Blyler, Jr.
- 👤 Frank V. DiMarcello
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:21
CPC Classifications
C; C08; C08F; C08F299/00; C08F299/02; C08F299/06; C08F299/065; B; B29; B29C; B29C35/00; B29C35/02; B29C35/08; B29C35/10; C03; C03C; C03C13/00; C03C13/04; C03C13/045; C03C25/00; C03C25/10; C03C25/104; C03C25/106; C03C25/1065; C03C25/12; G; G02; G02B; G02B6/00; G02B6/02; G02B6/02395; G02B6/44; G02B6/4401; G02B6/4429; G02B6/443; G02B6/4432; B29C35/0805; B29C2035/0827; B29L; B29L2011/00; B29L2011/0075; G02B6/02033
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
129 words
A method of producing a coated optical fiber comprising the steps of drawing an optical fiber from a preform at a rate of at least 1 meter per second and applying an ultraviolet-curable layer comprising prepolymer material onto said optical fiber or onto an inner layer thereon, and at least partially polymerizing the prepolymer material by exposing and ultraviolet-curable layer to ultraviolet radiation, with said drawing, applying,, and exposing being one continuous operation, characterized IN THAT the ultraviolet-curable layer further comprises at least 0.1 weight percent ultraviolet-absorbing material that does not form a substantial amount of free radicals which promote polymerization of said prepolymer material during said exposing to ultraviolet radiation, whereby the optical loss in said optical fiber due to said exposing to ultraviolet radiation in substantially reduced.
Claim 2
Independent Claim
129 words
A method of producing a coated optical fiber comprising the steps of drawing an optical fiber from a preform at a rate of at least 1 meter per second and applying an ultraviolet-curable layer comprising prepolymer material onto said optical fiber or onto an inner layer thereon, and at least partially polymerizing the prepolymer material by exposing and ultraviolet-curable layer to ultraviolet radiation, with said drawing, applying,, and exposing being one continuous operation, characterized IN THAT the ultraviolet-curable layer further comprises at least 0.1 weight percent ultraviolet-absorbing material that does not form a substantial amount of free radicals which promote polymerization of said prepolymer material during said exposing to ultraviolet radiation, whereby the optical loss in said optical fiber due to said exposing to ultraviolet radiation in substantially reduced.
Claim 3
Dependent Claim
36 words
The method of claim 1 further characterized in that said ultraviolet-curable layer further comprises photoinitiator material that forms free radicals in sufficient amount to promote polymerization of said prepolymer material when exposed to said ultraviolet radiation.
Claim 4
Dependent Claim
36 words
The method of claim 1 further characterized in that said ultraviolet-absorbing material does not substantially attenuate all radiation within the ultraviolet spectrum which causes said polymerization, thereby resulting in substantially complete curing of said ultraviolet-curable layer.
Claim 5
Dependent Claim
30 words
The method of claim 1 further characterized in that the ultraviolet-absorbing material is of such type and concentration as to prevent complete curing of the interior of said ultraviolet-curable layer.
Claim 6
Independent Claim
104 words
A method of producing a coated optical fiber comprising the steps of drawing an optical fiber from a preform at a rate of at least 1 meter per second and forming one or more inner layers on said optical fiber and then applying an ultraviolet-curable layer onto an inner layer and exposing said ultraviolet-curable layer to ultraviolet radiation, with said drawing, forming, applying, and exposing being one continuous operation, characterized in that at least one inner layer further comprises at least 0.1 weight percent ultraviolet-absorbing material, whereby the optical loss in said optical fiber due to said exposing to ultraviolet radiation is substantially reduced.
Claim 7
Independent Claim
104 words
A method of producing a coated optical fiber comprising the steps of drawing an optical fiber from a preform at a rate of at least 1 meter per second and forming one or more inner layers on said optical fiber and then applying an ultraviolet-curable layer onto an inner layer and exposing said ultraviolet-curable layer to ultraviolet radiation, with said drawing, forming, applying, and exposing being one continuous operation, characterized in that at least one inner layer further comprises at least 0.1 weight percent ultraviolet-absorbing material, whereby the optical loss in said optical fiber due to said exposing to ultraviolet radiation is substantially reduced.
Claim 8
Independent Claim
38 words
The method of claims 1 or 5 further characterized in that said optical fiber has a silica core which further comprises germanium or phosphorus or both, with said optical fiber having a numerical aperture of at least 0.23.
Claim 9
Independent Claim
34 words
The method of claims 1 or 5 further characterized in that said optical fiber has a silica core which further comprises a maximum concentration of at least 10 percent by weight of germanium dioxide.
Claim 10
Dependent Claim
26 words
The method of claim 7 further characterized in that said core further comprises a maximum concentration of at least 0.5 percent by weight of phosphorus pentoxide.
Claim 11
Independent Claim
35 words
The method of claims 1 or 5 further characterized by jacketing at least one of said coated optical fibers to form a cable, whereby said fiber or fibers operate in a dark environment after manufacture.
Claim 12
Independent Claim
38 words
The method of claims 1, 2, 3, 4, or 5 further characterized in that said ultraviolet-absorbing material is selected from the group consisting of: 2-hydroxy-4-methoxybenzophenone; 2,2'-dihydroxy-4-methoxybenzophenone; 2-hydroxy-4-methoxy-2'-carboxybenzophenone; 2-hydroxy-4-methoxy-5-sulfobenzophenone trihydrate; 2-hydroxy-4-n-octoxybenzophenone; (p-methoxybenzylidine) malonic acid, dimethylester; 2,4-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxybenzoate; and 2-(hydroxy-5-t-octylphenyl)benzotriazole.
Claim 13
Dependent Claim
12 words
A coated optical fiber produced according to the method of claim 1.
Claim 14
Dependent Claim
12 words
A coated optical fiber produced according to the method of claim 5.
Claim 15
Dependent Claim
81 words
A coated optical fiber jacketed so as to operate in a dark environment, wherein said coated optical fiber comprises a coated layer comprising polymer material and photoinitiator material that forms free radicals suitable for promoting polymerization of said polymer material when exposed to ultraviolet radiation, characterized in that said coated layer comprises at least 0.1 weight percent ultraviolet-absorbing material that does not form a substantial amount of free radical which promote polymerization of said polymer material when exposed to ultraviolet radiation.
Claim 16
Dependent Claim
81 words
A coated optical fiber jacketed so as to operate in a dark environment, wherein said coated optical fiber comprises a coated layer comprising polymer material and photoinitiator material that forms free radicals suitable for promoting polymerization of said polymer material when exposed to ultraviolet radiation, characterized in that said coated layer comprises at least 0.1 weight percent ultraviolet-absorbing material that does not form a substantial amount of free radical which promote polymerization of said polymer material when exposed to ultraviolet radiation.
Claim 17
Dependent Claim
55 words
A coated optical fiber jacketed so as to operate in a dark environment, wherein said coated optical fiber compries an inner coated layer, and further comprises a surrounding coated layer thereon comprising material that is curable by ultraviolet radiation, characterized in that said inner coated layer comprises at least 0.1 weight percent of ultraviolet-absorbing material.
Claim 18
Dependent Claim
55 words
A coated optical fiber jacketed so as to operate in a dark environment, wherein said coated optical fiber compries an inner coated layer, and further comprises a surrounding coated layer thereon comprising material that is curable by ultraviolet radiation, characterized in that said inner coated layer comprises at least 0.1 weight percent of ultraviolet-absorbing material.
Claim 19
Dependent Claim
38 words
The fiber of claims 13 or 14 further characterized in that said optical fiber has a silica core which further comprises germanium or phosphorus or both, with said optical fiber having a numerical aperture of at least 0.23.
Claim 20
Dependent Claim
34 words
The fiber of claims 13 or 14 further characterized in that said optical fiber has a silica core which further comprises a maximum concentration of at least 10 percent by weight of germanium dioxide.
Claim 21
Dependent Claim
26 words
The fiber of claim 16 further characterized in that said core further comprises a maximum concentration of at least 0.5 percent by weight of phosphorus pentoxide.
Claim 22
Dependent Claim
35 words
The fiber of claims 13 or 14 further characterized in that said ultraviolet-absorbing material is selected from the group consisting of: 2-hydroxy-4-methoxybenzophenone; 2,2'-dihydroxy-4-methoxybenzophenone; 2-hydroxy-4-methoxy-2'-carboxybenzophenone; 2-hydroxy-4-methoxy-5-sulfobenzophenone trihydrate; 2-hydroxy-4-n-octoxybenzophenone; (p-methoxybenzylidene) malonic acid, dimethylester; 2,4-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxybenzoate; and 2-(hydroxy-5-t-octylphenyl)benzotriazole.
References Cited (Backward Citations)
GB1029335A
Cited
GB1130717A
Cited
GB1186777A
Cited
GB1287954A
Cited
GB1393488A
Cited
JPS5134736A
Cited
US4105284A
Cited
US4099837A
Cited
US4111525A
Cited
US4125644A
Cited
US4129667A
Cited
US4135007A
Cited
US4263366A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-13 | 1988-05-14 | 1988-11-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-13 | 1992-05-14 | 1992-11-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-13 | 1996-05-14 | 1996-11-13 | $7700.00 | Window Closed / Lapsed |