Method for tinting hydrophilic plastic articles
Assignee: Novartis AG
•
Filing: 1988-11-01
•
Granted: 1990-02-06
•
Expires: 2008-11-01
Abstract
Abstract Tinted hydrophilic plastic articles, such as soft contact lenses, are prepared by carrying out the tinting operation while the hydrophilic material is still in its non-hydrated state. Tinting at this point avoids the need for use of swelling agents and also permits integration of the tinting procedure into an overall automated manufacturing operation. A preferred embodiment of the invention is an integrated process for producing a tinted soft contact lens comprising the steps of providing a casting mold having an arbor formed as a cup shaped container, filling said container with a monomeric lens forming liquid, polymerizing said liquid to produce a lens blank having one optical surface formed by the bottom of said cup shaped container, generating (e.g., machining) a second optical surface on said blank while said casting mold is mounted on a precision mandrel, tinting said resulting lens by impregnating the pores of said blank with a dispersion of a solubilized vat dye precursor and subsequently precipitatintg an insoluble vat dye within said pores, the blank being rinsed both before and after precipitation of said vat dye while still mounted in said casting mold, drying said blank to return it to a substantially xerogel state, edging and further processing said blank to convert it into a tinted hydrated soft contact lens, and subsequently hydrating said lens. While the foregoing is the preferred embodiment, the method may be utilized at the xerogel stage in all other presently known methods of forming lenses, e.g., lathing, cast molding and spin casting.
Inventors
- 👤 Praful Doshi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 08:54
CPC Classifications
B; B29; B29D; B29D11/00; B29D11/00865; B29D11/00894; B29D11/00903; G; G02; G02B; G02B1/00; G02B1/04; G02B1/041; G02B1/043
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
146 words
A method for producing a tinted, hyrated contact lens wherein a tinting step is carried out as an in-line step during the process of converting a monomeric, lens forming material to a packaged, fully hydrated contact lens, comprising the steps of: 1. converting the monomeric material to an intermediate contact lens article in the xerogel state; 2. generating at least one optical surface on said article; 3. tinting said article by impregnating the pores of said article with a dispersion of a solubilized vat dye as a precursor at a temperature in the range 35° to 85° degrees Centigrade, rinsing said article, precipitating the vat dye in a water insoluble form in the pores of said article and rinsing said article a second time; 4. drying said article to substantially its former xerogel state; 5. converting said xerogel article to a packaged, fully hydrated contact lens.
Claim 2
Independent Claim
146 words
A method for producing a tinted, hyrated contact lens wherein a tinting step is carried out as an in-line step during the process of converting a monomeric, lens forming material to a packaged, fully hydrated contact lens, comprising the steps of: 1. converting the monomeric material to an intermediate contact lens article in the xerogel state; 2. generating at least one optical surface on said article; 3. tinting said article by impregnating the pores of said article with a dispersion of a solubilized vat dye as a precursor at a temperature in the range 35° to 85° degrees Centigrade, rinsing said article, precipitating the vat dye in a water insoluble form in the pores of said article and rinsing said article a second time; 4. drying said article to substantially its former xerogel state; 5. converting said xerogel article to a packaged, fully hydrated contact lens.
Claim 3
Dependent Claim
24 words
The method of claim 1 wherein said dye is a vat dye selected from the group consisting of anthraquinone, anthrone, indigoid and thioindigoid dyes.
Claim 4
Dependent Claim
14 words
The method of claim 1 wherein the said vat dye is precipitated by oxidation.
Claim 5
Dependent Claim
16 words
The method of claim 1 wherein the said dye is precipitated with an acidic oxidizing medium.
Claim 6
Dependent Claim
19 words
The method of claim 1 wherein said vat dye precursor is applied to the convex face of said lens.
Claim 7
Dependent Claim
30 words
The method of claim 1 wherein the center and the edge of the lens are masked, thus leaving a clear edge around an annular tinted area approximately a human iris.
Claim 8
Independent Claim
151 words
A method for producing a tinted hydrated soft contact lens comprising the steps of providing a casting mold having an arbor formed as a cup shaped container, filling said container with a monomeric lens forming liquid, polymerizing said liquid to produce a blank having one optical surface formed by the bottom of said cup shaped container, generating a second optical surface on said blank while said casting mold is mounted on a precision mandrel, tinting said resulting lens by impregnating the pores of said blank with a dispersion of a solubilized vat dye precursor and subsequently precipitating an insoluble vat dye within said pores, the blank being rinsed both before and after precipitation of said vat dye while still mounted in said casting mold, drying said blank to return it to a substantially xerogel state, edging and further processing said blank to convert it into a tinted hydrated soft contact lens.
Claim 9
Independent Claim
151 words
A method for producing a tinted hydrated soft contact lens comprising the steps of providing a casting mold having an arbor formed as a cup shaped container, filling said container with a monomeric lens forming liquid, polymerizing said liquid to produce a blank having one optical surface formed by the bottom of said cup shaped container, generating a second optical surface on said blank while said casting mold is mounted on a precision mandrel, tinting said resulting lens by impregnating the pores of said blank with a dispersion of a solubilized vat dye precursor and subsequently precipitating an insoluble vat dye within said pores, the blank being rinsed both before and after precipitation of said vat dye while still mounted in said casting mold, drying said blank to return it to a substantially xerogel state, edging and further processing said blank to convert it into a tinted hydrated soft contact lens.
Claim 10
Dependent Claim
22 words
The method of claim 7 wherein said vat dye is selected from the group consisting of anthraquinone, anthrone, indigoid and thioindigoid dyes.
Claim 11
Dependent Claim
13 words
The method of claim 7 wherein said vat dye is precipitated by oxidation.
Claim 12
Dependent Claim
17 words
The method of claim 7 wherein the said vat dye is precipitated with an acidic oxidizing medium.
Claim 13
Independent Claim
53 words
A method for producing a tinted soft contact lens comprising the steps of preparing a hydrophilic plastic lens material in the xerogel state, impregnating pores of said material with a dispersion of a solubilized dye precursor, precipitating an insoluble dye within said pores, and subsequently hydrating said lens material to the hydrogel state.
Claim 14
Independent Claim
53 words
A method for producing a tinted soft contact lens comprising the steps of preparing a hydrophilic plastic lens material in the xerogel state, impregnating pores of said material with a dispersion of a solubilized dye precursor, precipitating an insoluble dye within said pores, and subsequently hydrating said lens material to the hydrogel state.
References Cited (Backward Citations)
US27401A
Cited
US2976576A
Cited
US3476499A
Cited
USRE27401E
Cited
US3895169A
Cited
GB1402123A
Cited
US4056496A
Cited
US4208362A
Cited
GB1583492A
Cited
US4188353A
Cited
US4252421A
Cited
US4379893A
Cited
US4494954A
Cited
EP0122771A1
Cited
US4569858A
Cited
US4719657A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-05 | 1993-08-07 | 1994-02-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-05 | 1997-08-07 | 1998-02-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-05 | 2001-08-07 | 2002-02-06 | $7700.00 | Window Closed / Lapsed |