Reduced-beak planox process for the formation of integrated electronic components
Assignee: STMicroelectronics SRL
•
Filing: 1987-11-23
•
Granted: 1990-01-30
•
Expires: 2007-11-23
Abstract
Abstract A method for reducing birdbeaks formed during a planox process is disclosed. On a silicon substrate (1), oxide (2) and nitride (3) are formed. The oxide and nitride are then selectively etched using a single plasma having high selectivity with respect to silicon and a photoresist mask (4). The high selectivity toward silicon is achieved by use of a CHF 3 +CO 2 plasma under conditions of 30:1 oxide/silicon selectivity. Field oxide regions (5) with reduced birdbeaks can then be formed.
Inventors
- 👤 Livio Baldi
- 👤 Daniela Beardo
- 👤 Marco Icardi
- 👤 Adriana Rebora
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 20:21
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/10; H10W10/13; Y; Y10; Y10S; Y10S148/00; Y10S148/117; Y10S148/131
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
182 words
A method for reducing oxide wedges or bird beaks formed during a planox process for the formation of integrated electronic components, said method comprising the steps of: (a) growing a layer of oxide on a silicon substrate, said layer having a thickness of 10 nm or less; (b) depositing a layer of silicon nitride on said oxide layer; (c) depositing a photoresist layer on selected areas of said silicon nitride layer, along with appropriate masking; said selected areas being those areas which will become active areas of the electronic components; (d) etching, by use of one plasma having high selectivity with respect to silicon, the nitride and oxide layers previously deposited so as to remove those nitride and oxide layers surrounding said selected areas, thereby exposing the silicon surrounding said selected areas; (e) removing said photoresist layer from said selected areas; (f) growing a field oxide layer around said selected areas on the surface of said exposed silicon substrate; and (g) removing residual oxide and silicon nitride from said selected areas so as to expose the silicon substrate in said selected areas.
Claim 2
Independent Claim
182 words
A method for reducing oxide wedges or bird beaks formed during a planox process for the formation of integrated electronic components, said method comprising the steps of: (a) growing a layer of oxide on a silicon substrate, said layer having a thickness of 10 nm or less; (b) depositing a layer of silicon nitride on said oxide layer; (c) depositing a photoresist layer on selected areas of said silicon nitride layer, along with appropriate masking; said selected areas being those areas which will become active areas of the electronic components; (d) etching, by use of one plasma having high selectivity with respect to silicon, the nitride and oxide layers previously deposited so as to remove those nitride and oxide layers surrounding said selected areas, thereby exposing the silicon surrounding said selected areas; (e) removing said photoresist layer from said selected areas; (f) growing a field oxide layer around said selected areas on the surface of said exposed silicon substrate; and (g) removing residual oxide and silicon nitride from said selected areas so as to expose the silicon substrate in said selected areas.
Claim 3
Dependent Claim
28 words
The process of claim 1 wherein said high selectivity toward silicon is achieved by use of a CHF 3 +CO 2 plasma under conditions of 30:1 oxide/silicon selectivity.
References Cited (Backward Citations)
US4080718A
Cited
US4330931A
Cited
US4454647A
Cited
US4376672A
Cited
US4563227A
Cited
US4484979A
Cited
US4551910A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-01-29 | 1993-07-31 | 1994-01-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-01-29 | 1997-07-31 | 1998-01-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-01-29 | 2001-07-31 | 2002-01-30 | $7700.00 | Window Closed / Lapsed |