US4897153A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of processing siloxane-polyimides for electronic packaging applications
Assignee: Lockheed Martin Corp
•
Filing: 1989-04-24
•
Granted: 1990-01-30
•
Expires: 2009-04-24
Abstract
Abstract A method of forming a multilayer metallization pattern using siloxane polyimide dielectric layers comprises forming the first siloxane polyimide layer, laser etching holes in the first layer, plasma etching the first layer to be sure the holes are clean, then cleaning the surface of the first layer in an etchant for silicon oxide, after which the metallization layer is formed and patterned and a second siloxane polyimide layer is formed thereover with good adhesion.
Inventors
- 👤 Herbert S. Cole
- 👤 James E. Kohl
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:10
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/66; H10P14/668; H10P14/6681; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/081; H10W20/093; H10W20/096; H10W20/40; H10W20/45; H10W20/47; H10W70/00; H10W70/60; H10W70/611; H10W70/614; H10W99/00; H05; H05K; H05K3/00; H05K3/0011; H05K3/0017; H05K3/38; H05K3/381; H05K3/46; H05K3/4644
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
93 words
A process comprising the steps of: forming a first copolymer layer; treating said first copolymer layer under conditions which leave the exposed surface of said first copolymer layer enriched with some elements of the copolymer formula; cleaning said exposed surface of said first copolymer layer with an etchant or solvent which substantially removes said enrichment to leave an exposed surface of said first copolymer layer which is substantially similar to that of an untreated surface of said copolymer; and forming a second copolymer layer on said exposed surface of said first copolymer layer.
Claim 2
Dependent Claim
93 words
A process comprising the steps of: forming a first copolymer layer; treating said first copolymer layer under conditions which leave the exposed surface of said first copolymer layer enriched with some elements of the copolymer formula; cleaning said exposed surface of said first copolymer layer with an etchant or solvent which substantially removes said enrichment to leave an exposed surface of said first copolymer layer which is substantially similar to that of an untreated surface of said copolymer; and forming a second copolymer layer on said exposed surface of said first copolymer layer.
Claim 3
Dependent Claim
29 words
The process recited in claim 1 wherein: after the treating step, the enriched surface of said first copolymer layer includes at least one element introduced by that treating step.
Claim 4
Dependent Claim
35 words
The process recited in claim 1 wherein the enriched exposed surface of said first copolymer layer is substantially inorganic in nature; and said cleaning step employs an etchant or solvent which removes that inorganic material.
Claim 5
Dependent Claim
24 words
The process recited in claim 1 wherein the treating step comprises the step of: plasma etching said first copolymer layer in an oxygen-containing plasma.
Claim 6
Dependent Claim
19 words
The process recited in claim 4 wherein in the plasma etching step, said plasma further comprises CF 4 .
Claim 7
Dependent Claim
18 words
The process recited in claim 5 wherein: following the plasma etching step, the enriched exposed surface includes fluorine.
Claim 8
Dependent Claim
41 words
The process recited in claim 6 wherein: said first copolymer layer is a siloxane polyimide copolymer; and the exposed enriched surface is enriched with silicon, oxygen and fluorine relative to the composition of an unetched layer of that siloxane polyimide copolymer.
Claim 9
Dependent Claim
31 words
The process recited in claim 7 wherein the cleaning step comprises the step of exposing the surface of said first copolymer layer to an etchant or solvent which removes silicon oxide.
Claim 10
Dependent Claim
18 words
The process recited in claim 7 wherein: the cleaning etchant or solvent includes HF as an active component.
Claim 11
Independent Claim
99 words
A method of forming a siloxane polyimide laminate comprising the steps of: forming a first siloxane polyimide copolymer layer; treating an exposed surface of said first siloxane polyimide copolymer layer in a manner which leaves the exposed surface of said first siloxane polyimide copolymer layer enriched with silicon and oxygen relative to an untreated surface of that siloxane polyimide copolymer; cleaning said exposed surface of said first siloxane polyimide copolymer with an etchant or solvent which removes silicon oxide; and forming a second siloxane polyimide copolymer layer on the cleaned exposed surface of said first siloxane polyimide copolymer layer.
Claim 12
Independent Claim
99 words
A method of forming a siloxane polyimide laminate comprising the steps of: forming a first siloxane polyimide copolymer layer; treating an exposed surface of said first siloxane polyimide copolymer layer in a manner which leaves the exposed surface of said first siloxane polyimide copolymer layer enriched with silicon and oxygen relative to an untreated surface of that siloxane polyimide copolymer; cleaning said exposed surface of said first siloxane polyimide copolymer with an etchant or solvent which removes silicon oxide; and forming a second siloxane polyimide copolymer layer on the cleaned exposed surface of said first siloxane polyimide copolymer layer.
Claim 13
Dependent Claim
36 words
The method recited in claim 10 further comprising the step of: forming a patterned metal layer on the exposed surface of said first siloxane polyimide copolymer layer prior to forming said second siloxane polyimide copolymer layer.
Claim 14
Dependent Claim
18 words
The method recited in claim 10 wherein: said treating step comprises etching said surface in an oxygen-containing plasma.
Claim 15
Dependent Claim
14 words
The method recited in claim 12 wherein said plasma further comprises CF 4 .
Claim 16
Dependent Claim
35 words
The method recited in claim 13 wherein said step of cleaning comprises the step of: exposing said enriched surface of said first siloxane polyimide copolymer layer to an etchant or solvent which removes silicon oxide.
Claim 17
Dependent Claim
21 words
The method recited in claim 14 wherein: said etchant or solvent which removes silicon oxide comprises HF as an active component.
Claim 18
Dependent Claim
20 words
The method recited in claim 10 wherein: said treating step comprises etching said surface in a CF 4 -containing plasma.
Claim 19
Independent Claim
109 words
A method of forming a siloxane polyimide copolymer laminate comprising the steps of: forming a first siloxane polyimide copolymer layer; treating the exposed surface of said first siloxane polyimide copolymer layer in a manner which leaves a substantially inorganic coating of a silicon and oxygen containing substance on the exposed surface; removing said substantially inorganic coating to leave the exposed surface of said first siloxane polyimide copolymer layer with a surface composition which is substantially similar to that of an untreated layer of that siloxane polyimide copolymer; and forming a second layer of a siloxane polyimide copolymer on the cleaned, exposed surface of said first siloxane polyimide copolymer layer.
Claim 20
Independent Claim
109 words
A method of forming a siloxane polyimide copolymer laminate comprising the steps of: forming a first siloxane polyimide copolymer layer; treating the exposed surface of said first siloxane polyimide copolymer layer in a manner which leaves a substantially inorganic coating of a silicon and oxygen containing substance on the exposed surface; removing said substantially inorganic coating to leave the exposed surface of said first siloxane polyimide copolymer layer with a surface composition which is substantially similar to that of an untreated layer of that siloxane polyimide copolymer; and forming a second layer of a siloxane polyimide copolymer on the cleaned, exposed surface of said first siloxane polyimide copolymer layer.
Claim 21
Dependent Claim
27 words
The method recited in claim 17 wherein: said step of removing said inorganic coating comprises cleaning the exposed surface with an etchant which removes said inorganic coating.
Claim 22
Dependent Claim
15 words
The method recited in claim 18 wherein: said etchant is one which removes silicon oxide.
Claim 23
Dependent Claim
15 words
The method recited in claim 19 wherein: said etchant includes HF as an active component.
Claim 24
Independent Claim
65 words
A method comprising the steps of: treating a body of siloxane polyimide copolymer to remove a portion of said body, the treatment being one which leaves a portion of the surface of said body enriched with some elements of the copolymer formula relative to an untreated body of siloxane polyimide; and cleaning said portion of said surface with a fluid which substantially removes the enrichment.
Claim 25
Independent Claim
65 words
A method comprising the steps of: treating a body of siloxane polyimide copolymer to remove a portion of said body, the treatment being one which leaves a portion of the surface of said body enriched with some elements of the copolymer formula relative to an untreated body of siloxane polyimide; and cleaning said portion of said surface with a fluid which substantially removes the enrichment.
Claim 26
Dependent Claim
26 words
The method recited in claim 21 wherein said treating step comprises a step selected from the group of steps consisting of plasma etching and laser ablating.
Claim 27
Dependent Claim
20 words
The method recited in claim 22 wherein said cleaning step comprises the step of etching or dissolving the enriched layer.
Claim 28
Dependent Claim
20 words
The method recited in claim 21 wherein said cleaning step comprises the step of etching or dissolving the enriched layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-01-29 | 1993-07-31 | 1994-01-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-01-29 | 1997-07-31 | 1998-01-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-01-29 | 2001-07-31 | 2002-01-30 | $7700.00 | Window Closed / Lapsed |