Method of manufacturing a semiconductor device of the hetero-junction bipolar transistor type
Assignee: Ommic SAS
•
Filing: 1988-12-28
•
Granted: 1989-12-26
•
Expires: 2008-12-28
Abstract
Abstract A method of manufacturing a hetero-junction bipolar transistor especially of gallium arsenide comprising the formation of epitaxial layers superimposed to obtain a collector layer (1) of the n + type, an emitter layer (3) of the n-type, the formation of localized implantations of the p + type to obtain the base region (31, 30) or of the n + type to form collector contact islands (20). This method also including the formation of base contacts B (70) having the dimensions B 0 and located at a relative distance of E 1 , then covering the metallization (70) of pads (81) of silica (Si 3 N 4 ) having edges perpendicular to the plane of the layers on which bear spacers of silicon nitride (Si 3 N 4 ) (52) having dimensions h 1 defining with a high precision the dimension E 0 =B 1 -2h of the emitter contact E and the distances between the different collector (90), base (70) and emitter (90) contacts C, B and E, respectively.
Inventors
- 👤 Daniel Selle
- 👤 Philippe Boissenot
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 21:13
CPC Classifications
H; H10; H10D; H10D10/00; H10D10/01; H10D10/021; H10D10/80; H10D10/821; H10D62/00; H10D62/80; H10D62/85
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
455 words
A method of manufacturing a semiconductor device of the hetero-junction bipolar transistor type having a planar structure, said method comprising at least the step of manufacturing a structure comprising successively at least one collector layer of a binary material of a first conductivity type, a base layer of a binary material of the second conductivity type opposite to the first type, an emitter layer of a ternary material of the first conductivity type and a binary highly doped contact layer of the first conductivity type, characterized in that it moreover comprises the steps of: (a) depositing a layer of silicon nitride (Si 3 N 4 ), (b) positioning a mask MK 2 defining openings normal to the base regions and etching the layer of silicon nitride (Si 3 N 4 ) through these openings until the surface of the contact layer is exposed by a method which permits of obtaining etching edges perpendicular to the plane of the layers, thus forming in the nitride layer openings remote from each other, (c) localized implanting of ions of the second conductivity type through the openings of the nitride layer with an energy sufficient to attain the base layer so as to form islands of the second conductivity type connecting the base layer to the surface of the contact layer, (d) depositing a metallic layer which is formed in the openings as well as on the remaining parts of the nitride (Si 3 N 4 ) layer, (e) forming a layer of silica (SiO 2 ) of very large thickness and then planarizing through a known method the device thus obtained down to the upper level of the nitride (Si 3 N 4 ) layer by reactive ion etching (RIE) and ion machining, (f) selectively etching the remaining parts of the nitride (Si 3 N 4 ) layer to maintain pads of silica (SiO 2 ) covering the base metallizations, (g) depositing a fresh layer of silicon nitride (Si 3 N 4 ) and forming by a known method spacers formed in this new layer of nitride, which spacers bear on the edges of the silica (SiO 2 ) pads intended to reduce the distance between these pads of silica thus forming an opening defining the width of the emitter contact, these spacers also defining the distance between the collector, base and emitter electrodes, (h) depositing a metallic layer suitable to form the emitter and collector contacts, the pads of silica (SiO 2 ) and the spacers serving as masks, and then eliminating these dielectric parts, and (i) localized ion implanting between the collector base and emitter contacts serving as masks of species suitable to form insulating islands between these electrodes with an energy permitting of conductivity type.
Claim 2
Independent Claim
455 words
A method of manufacturing a semiconductor device of the hetero-junction bipolar transistor type having a planar structure, said method comprising at least the step of manufacturing a structure comprising successively at least one collector layer of a binary material of a first conductivity type, a base layer of a binary material of the second conductivity type opposite to the first type, an emitter layer of a ternary material of the first conductivity type and a binary highly doped contact layer of the first conductivity type, characterized in that it moreover comprises the steps of: (a) depositing a layer of silicon nitride (Si 3 N 4 ), (b) positioning a mask MK 2 defining openings normal to the base regions and etching the layer of silicon nitride (Si 3 N 4 ) through these openings until the surface of the contact layer is exposed by a method which permits of obtaining etching edges perpendicular to the plane of the layers, thus forming in the nitride layer openings remote from each other, (c) localized implanting of ions of the second conductivity type through the openings of the nitride layer with an energy sufficient to attain the base layer so as to form islands of the second conductivity type connecting the base layer to the surface of the contact layer, (d) depositing a metallic layer which is formed in the openings as well as on the remaining parts of the nitride (Si 3 N 4 ) layer, (e) forming a layer of silica (SiO 2 ) of very large thickness and then planarizing through a known method the device thus obtained down to the upper level of the nitride (Si 3 N 4 ) layer by reactive ion etching (RIE) and ion machining, (f) selectively etching the remaining parts of the nitride (Si 3 N 4 ) layer to maintain pads of silica (SiO 2 ) covering the base metallizations, (g) depositing a fresh layer of silicon nitride (Si 3 N 4 ) and forming by a known method spacers formed in this new layer of nitride, which spacers bear on the edges of the silica (SiO 2 ) pads intended to reduce the distance between these pads of silica thus forming an opening defining the width of the emitter contact, these spacers also defining the distance between the collector, base and emitter electrodes, (h) depositing a metallic layer suitable to form the emitter and collector contacts, the pads of silica (SiO 2 ) and the spacers serving as masks, and then eliminating these dielectric parts, and (i) localized ion implanting between the collector base and emitter contacts serving as masks of species suitable to form insulating islands between these electrodes with an energy permitting of conductivity type.
Claim 3
Dependent Claim
110 words
A method as claimed in claim 1, characterized in that the structure of the collector, base and emitter layers is formed on a semi-insulating substrate and in that in this structure: the collector is constituted by the superposition of two binary layers of the first conductivity type, the first of which is highly doped, the base layer is formed by a localized implantation of ions of the second conductivity type in the superficial region of the second collector layer, islands connecting the first collector layer to the contact layer are formed by a localized implantation into a region chosen to form the collector to ions of the first conductivity type.
Claim 4
Dependent Claim
39 words
A method as claimed in claim 1 or 2, characterized in that the transistors is insulated by an ion implantation suitable to form insulation regions defining the active zone of the transistor, the latter being masked during this operation.
Claim 5
Dependent Claim
47 words
A method as claimed in claim 1 or 2, characterized in that a not intentionally doped binary layer is formed between the base layer and the ternary emitter layer to avoid the diffusion of the charge carriers from the binary base layer to the ternary emitter layer.
Claim 6
Dependent Claim
42 words
A method as claimed in claim 4, characterized in that a ternary layer having a composition gradient is formed between the binary not intentionally doped layer and the ternary emitter layer to obtain a gradual hetero-junction between the emitter and the base.
Claim 7
Dependent Claim
41 words
A method as claimed in claim 1 or 2, characterized in that it comprises between the step (b) and the step (c) a step (b') (b') implantation in the openings of ions suitable to form insulating zones under the base region.
Claim 8
Dependent Claim
69 words
A method as claimed in claim 2, characterized in that: the substrate consists of semi-insulating gallium arsenide (GaAs) orientated in a crystallographic direction [100]: the binary layers consist of gallium arsenide (GaAs); the ternary layers consist of gallium aluminum arsenide (GaAlAs) having, a composition gradient of the element A1 when this gradient is provided; the first conductivity type is the n-type; the second opposite conductivity type is the p-type.
Claim 9
Dependent Claim
30 words
A method as claimed in claim 7, characterized in that, in order to obtain the n + or n-conductivity type, the layers are doped by means of Si + ions.
Claim 10
Dependent Claim
35 words
A method as claimed in claim 7 or 8, characterized in that, in order to obtain islands of the n + conductivity type, the ion implantation provided is effected by means of Si + ions.
Claim 11
Dependent Claim
49 words
A method as claimed in claim 1 or 2, characterized in that, in order to obtain zones of the p +`l conductivity type, the ion implantation provided is effected by means of ions among Be, Mg, Zn and among an associaton of F with Be or P with Mg.
Claim 12
Dependent Claim
60 words
A method as claimed in claim 1 or 2, characterized in that the metallic layer deposited during the step d) to form the base contacts is chosen among the compounds Au-Mn, Au-Be, Au-Zn, and in that the metallic layer deposited during the step h) to form the emitter and collector contacts is a multi-layer of Au-Ge and on it Ni.
Claim 13
Independent Claim
27 words
A method as claimed in any one of claims 3, characterized in that, in order to form the insulating zones, oxygen (0 + ) ions are implanted.
Claim 14
Dependent Claim
37 words
A method as claimed in claim 1 or 2, characterized in that, in order to form the insulating zones between the electrodes, during the step (i) elements are implanted chosen among B ions, O ions and protons.
Claim 15
Dependent Claim
51 words
A method as claimed in claim 1 or 2, characterized in that the base layer is an additional layer of a binary material of the group III-V of the second conductivity type with an etching treatment around a mask defining the base zone down to upper level of the collector layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-12-25 | 1993-06-26 | 1993-12-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-12-25 | 1997-06-26 | 1997-12-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-12-25 | 2001-06-26 | 2001-12-26 | $7700.00 | Window Closed / Lapsed |