Method for making an improved supported membrane/electrode structure combination wherein catalytically active particles are coated onto the membrane
Assignee: Dow Chemical Co
•
Filing: 1986-12-19
•
Granted: 1989-12-26
•
Expires: 2006-12-19
Abstract
Abstract The invention is a membrane/electrode combination having an electrically conductive screen which has a first and a second face. At least the first face of the screen is substantially flat. The screen has a plurality of openings passing therethrough and connecting the first and the second faces of the screen. The openings occupying up to about 75% of the surface area of each face of the electrically conductive screen. The first face of an ion exchange membrane film, which has a first and a second face, is attached to the first face of the electrically conductive screen, thereby leaving portions of the first face of the membrane film exposed through the openings in the electrically conductive screen. A plurality of catalytically active particles are disposed on the exposed portions of the first face of the membrane film in electrical and physical contact with the membrane and with the electrically conductive screen.
Inventors
- 👤 James W. McMichael
- 👤 Robert D. Door
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:39
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/90; H01M4/9091; C; C25; C25B; C25B9/00; C25B9/17; C25B9/19; C25B9/23; H01M4/92; H01M4/928; H01M8/00; H01M8/10; H01M8/1004; H01M8/1016; H01M8/1018; H01M8/102; H01M8/1023; H01M8/1039; H01M8/1041; H01M8/1053; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
103 words
A method for making an improved membrane/electrode combination comprising: (a) contacting a first face of an ion exchange membrane with a substantially flat electrically conductive electroformed screen having a plurality of openings occupying up to about 75% of the surface area of each face of the electrically conductive screen, thereby leaving a portion of the membrane exposed through the holes in the electrically conductive electroformed screen; (b) coating the portion of the membrane exposed through the openings in the electrically conductive electroformed screen with catalytically active particles; and (c) bonding the membrane to the catalytically active particles and the electrically conductive electroformed screen.
Claim 2
Independent Claim
103 words
A method for making an improved membrane/electrode combination comprising: (a) contacting a first face of an ion exchange membrane with a substantially flat electrically conductive electroformed screen having a plurality of openings occupying up to about 75% of the surface area of each face of the electrically conductive screen, thereby leaving a portion of the membrane exposed through the holes in the electrically conductive electroformed screen; (b) coating the portion of the membrane exposed through the openings in the electrically conductive electroformed screen with catalytically active particles; and (c) bonding the membrane to the catalytically active particles and the electrically conductive electroformed screen.
Claim 3
Dependent Claim
17 words
The method of claim 1 wherein the sheet is cleaned prior to being contacted with the membrane.
Claim 4
Dependent Claim
14 words
The method of claim 1 wherein the ion exchange membrane is a bilayer membrane.
Claim 5
Dependent Claim
26 words
The method of claim 3 wherein the ion exchange membrane has a layer containing sulfonic ion exchange groups, and a layer containing carboxylic ion exchange groups.
Claim 6
Dependent Claim
21 words
The method of claim 4 wherein the screen is bonded to the membrane layer which contains the carboxylic ion exchange groups.
Claim 7
Dependent Claim
14 words
The method of claim 1 wherein the membrane is in thermoplastic or sodium form.
Claim 8
Dependent Claim
12 words
The method of claim 1 wherein the membrane is in hydrogen form.
Claim 9
Dependent Claim
26 words
The method of claim 6 wherein the catalytically active particles are bonded to the membrane under pressure at a temperature of up to about 260° C.
Claim 10
Dependent Claim
26 words
The method of claim 7 wherein the catalytically active particles are bonded to the membrane under pressure at a temperature of up to about 180° C.
Claim 11
Dependent Claim
27 words
The method of claim 8 wherein the catalytically active particles are bonded to the membrane under a pressure of up to about 3.5 kilograms per square centimeter.
Claim 12
Dependent Claim
27 words
The method of claim 9 wherein the catalytically active particles are bonded to the membrane under a pressure of up to about 3.5 kilograms per square centimeter.
Claim 13
Dependent Claim
28 words
The method of claim 11 wherein the catalytically active particles are blended with a solvent/dispersant and are in the form of a solution/dispersion when coated onto the membrane.
Claim 14
Dependent Claim
14 words
The method of claim 12 wherein the solution dispersion also contains an ionomer binder.
Claim 15
Dependent Claim
262 words
The method of claim 13 wherein ionomer binder is a copolymer of a first type monomer and a second type monomer, wherein first type of monomer is represented by the general formula: CF.sub.2 ═CZZ' (I) where: Z and Z' are independently selected from the group consisting of --H, --Cl, --F, or --CF 3 ; and the second type of monomer consists of one or more monomers selected from compounds represented by the general formula: Y--(CF.sub.2).sub.a --(CFR.sub.f).sub.b --(CFR.sub.f').sub.c --O--[CF(CF.sub.2 X)--CF.sub.2 --O].sub.n --CF═CF.sub.2 (II) where: Y is selected from the group consisting of --SO 2 Z, --CN, --COZ, and C(R 3 f)(R 4 f)OH; Z is --I, --Br, --Cl, --F, --OR, or --NR 1 R 2 ; R is a branched or linear alkyl radical having from 1 to about 10 carbon atoms or an aryl radical; R 3 f and R 4 f are independently selected from the group consisting of perfluoroalkyl radicals having from 1 to about 10 carbon atoms; R 1 and R 2 are independently selected from the group consisting of --H, a branched or linear alkyl radical having from 1 to about 10 carbon atoms or an aryl radical; a is 0-6; b is 0-6; c is 0 or 1; provided a+b+c is not equal to 0; X is --Cl, --Br, --F, or mixtures thereof when N>1; n is 0 to 6; and R f and R f' are independently selected from the group consisting of --F, --Cl, perfluoroalkyl radicals having from 1 to about 10 carbon atoms and fluorochloroalkyl radicals having from 1 to about 10 carbon atoms.
Claim 16
Dependent Claim
38 words
The method of claim 14 wherein Y is --SO 2 F or --COOCH 3 ; n is 0 or 1; R f and R f' are --F; X is --Cl or --F; and a+b+c is 2 or 3.
Claim 17
Dependent Claim
108 words
The method of claim 14 wherein the copolymer also includes a third type of monomer selected from the compounds represented by the general Y'--(CF.sub.2).sub.a' --(CFR.sub.f).sub.b' --(CFR.sub.f').sub.c' --O--[CF(CF.sub.2 X')--CF.sub.2 --O].sub.n' --CF═CF.sub.2 (III) where: Y' is --F, --Cl or --Br; a' and b' are independently 0-3; c is 0 or 1; provided a'+b'+c' is not equal to 0; n' is 0-6; R f and R f' are independently selected from the group consisting of --Br, --Cl, --F, perfluoroalkyl radicals having from about 1 to about 10 carbon atoms, and chloroperfluoroalkyl radicals having from 1 to about 10 carbon atoms; and X' is --F, --Cl, --Br, or mixtures thereof when n'>1.
Claim 18
Dependent Claim
79 words
The method of claim 12 wherein the solvent/dispersant is represented by the general formula: XCF.sub.2 --CYZ--X' wherein: X is selected from the group consisting of --F, --Cl, --Br, and --I; X' is selected from the group consisting of --Cl, --Br, and --I; Y and Z are independently selected from the group consisting of --H, --F, --Cl, --Br, --I and --R'; R' is selected from the group of perfluoroalkyl radicals and chloroperfluoroalkyl radicals having from 1 to 6 carbon atoms.
Claim 19
Dependent Claim
10 words
The method of claim 12 wherein the solvent/dispersant is 1,2-dibromotetrafluoroethane.
Claim 20
Dependent Claim
10 words
The method of claim 12 wherein the solvent/dispersant is 1,2,2-trichlorotrifluoroethane.
Claim 21
Dependent Claim
21 words
The method of claim 12 wherein the solute in the solution/dispersion contains from about 4 to about 20 weight percent ionomer.
Claim 22
Dependent Claim
23 words
The method of claim 12 wherein the solute in the solution/dispersion contains from about 0.1 to about 25 weight percent catalytically active particles.
Claim 23
Dependent Claim
25 words
The method of claim 12 wherein the solute in the solution/dispersion contains from about 60 to about 90 weight percent of an electrically conductive metal.
Claim 24
Dependent Claim
22 words
The method of claim 12 wherein the solution/dispersion is blended for from about 4 to about 24 hours in a ball mill.
Claim 25
Dependent Claim
14 words
The method of claim 12 wherein the solution/dispersion contains about 25 weight percent solids.
Claim 26
Dependent Claim
13 words
The method of claim 12 wherein the solution/dispersion is sprayed onto the screen.
Claim 27
Dependent Claim
13 words
The method of claim 12 wherein the solution/dispersion is poured onto the screen.
Claim 28
Dependent Claim
19 words
The method of claim 12 wherein the solution/dispersion is applied to the screen with metering bars, knives, or rods.
Claim 29
Dependent Claim
19 words
The method of claim 12 wherein the solution/dispersion is coated to a thickness of about 20 to 50 microns.
Claim 30
Dependent Claim
17 words
The method of claim 12 wherein the solution/dispersion is coated to a thickness of about 5-10 microns.
References Cited (Backward Citations)
US3282875A
Cited
US3632498A
Cited
US4025405A
Cited
US4192725A
Cited
US4178218A
Cited
US4357218A
Cited
US3909378A
Cited
US4065366A
Cited
US4065366B1
Cited
US4126588A
Cited
US4142005A
Cited
US4123336A
Cited
US4061549A
Cited
US4116888A
Cited
US4151052A
Cited
US4212713A
Cited
US4251333A
Cited
US4465580A
Cited
US4176215A
Cited
US4276146A
Cited
US4214971A
Cited
US4270996A
Cited
US4209635A
Cited
US4239435A
Cited
US4340680A
Cited
US4319969A
Cited
EP0027009A1
Cited
US4364815A
Cited
US4315805A
Cited
US4661218A
Cited
US4457822A
Cited
US4498942A
Cited
GB2069006A
Cited
US4272353A
Cited
US4293394A
Cited
US4299674A
Cited
US4394229A
Cited
US4345986A
Cited
US4470889A
Cited
US4358412A
Cited
US4337211A
Cited
US4337137A
Cited
US4358545A
Cited
US4417969A
Cited
US4478695A
Cited
US4330654A
Cited
US4462877A
Cited
US4655887A
Cited
US4299675A
Cited
US4389297A
Cited
US4655886A
Cited
US4331521A
Cited
US4652356A
Cited
US4469579A
Cited
US4386987A
Cited
US4416932A
Cited
US4545886A
Cited
US4650551A
Cited
US4650711A
Cited
US4610762A
Cited
US4654104A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-12-25 | 1993-06-26 | 1993-12-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-12-25 | 1997-06-26 | 1997-12-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-12-25 | 2001-06-26 | 2001-12-26 | $7700.00 | Window Closed / Lapsed |