High temperature post exposure baking treatment for positive photoresist compositions
Assignee: Celanese Corp
•
Filing: 1986-10-17
•
Granted: 1989-12-05
•
Expires: 2006-10-17
Abstract
Abstract The invention provides a method for producing a photographic element which comprises coating a substrate with a positive working photosensitive composition which composition comprises an aqueous alkali soluble resin, a quinone diazide photosensitizer and a solvent composition, heat treating said coated substrate at a temperature of from about 20° C. to about 100° C. until substantially all of said solvent composition is removed; imagewise exposing said photosensitive composition to actinic radiation; baking said coated substrate at a temperature of from about 120° C. to about 160° C. for from about 15 seconds to about 90 seconds; and removing the exposed non-image areas of said composition with a suitable developer.
Inventors
- 👤 Mark A. Spak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:23
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/16; G03F7/168
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
151 words
A method for producing a photographic element which consists essentially of coating a substrate with a positive working photosensitive composition which composition comprises an aqueous alkali soluble resin, a quinone diazide photosensitizer and a solvent composition, then heat treating said coated substrate at a temperature of from about 20° C. to about 100° C. until substantially all of said solvent composition is removed; then imagewise exposing said photosensitive composition to actinic radiation; then baking said coated substrate at a temperature of from at least about 130° C. to about 155° C. for from about 15 seconds to about 90 seconds; and the removing the exposed non-image areas of said composition with a developer until substantially all of the coating has dissolved from the exposed areas, which developer consists essentially of an aqueous alkaline solution to attain an image having thermal stability at least equal to the temperature of said baking step.
Claim 2
Independent Claim
151 words
A method for producing a photographic element which consists essentially of coating a substrate with a positive working photosensitive composition which composition comprises an aqueous alkali soluble resin, a quinone diazide photosensitizer and a solvent composition, then heat treating said coated substrate at a temperature of from about 20° C. to about 100° C. until substantially all of said solvent composition is removed; then imagewise exposing said photosensitive composition to actinic radiation; then baking said coated substrate at a temperature of from at least about 130° C. to about 155° C. for from about 15 seconds to about 90 seconds; and the removing the exposed non-image areas of said composition with a developer until substantially all of the coating has dissolved from the exposed areas, which developer consists essentially of an aqueous alkaline solution to attain an image having thermal stability at least equal to the temperature of said baking step.
Claim 3
Dependent Claim
24 words
The method of claim 1 wherein said heat treating step is conducted at a temperature of from about 50° C. to about 90° C.
Claim 4
Dependent Claim
24 words
The method of claim 1 wherein said heat treating step is conducted at a temperature of from about 70° C. to about 90° C.
Claim 5
Dependent Claim
17 words
The method of claim 1 wherein said heat treatment is conducted for up to about 3 minutes.
Claim 6
Dependent Claim
17 words
The method of claim 1 wherein said heat treatment is conducted for up to about 1 minute.
Claim 7
Dependent Claim
23 words
The method of claim 1 wherein said baking treatment is conducted at a temperature of from about 140° C. to about 155° C.
Claim 8
Dependent Claim
20 words
The method of claim 1 wherein said baking treatment is conducted for from about 30 seconds to about 90 seconds.
Claim 9
Dependent Claim
55 words
The method of claim 1 wherein said heat treatment is conducted at from about 85° C. to about 95° C. for up to about one minute; and said post exposure baking treatment is conducted at a temperature of from about 140° C. to about 155° C. for from about 30 seconds to about 90 seconds.
Claim 10
Dependent Claim
34 words
The method of claim 1 wherein said photosensitive composition further comprises one or more additives selected from the group consisting of colorants, leveling agents, anti-striation agents, plasticizers, adhesion promoters, speed enhancers, solvents and surfactants.
Claim 11
Dependent Claim
34 words
The method of claim 1 wherein said diazide component comprises one or more compounds selected from the group consisting of diazo sulfonyl-chloride reaction products with hydroxy or polyhydroxy aryl compounds, aryl amines or polyamines.
Claim 12
Dependent Claim
37 words
The method of claim 1 wherein said substrate comprises one or more components selected from the group consisting of silicon, aluminum, polymeric resins, silicon dioxide, doped silicon dioxide, silicon nitride, tantalum, copper, polysilicon, ceramics and aluminum/copper mixtures.
Claim 13
Dependent Claim
18 words
The method of claim 1 wherein said photosensitizer is the condensation product of (1,2)naphthoquinonediazide-5-sulfonyl chloride with 2,3,4 trihydroxybenzophenone.
Claim 14
Dependent Claim
12 words
The method of claim 1 wherein said resin is a novolak resin.
Claim 15
Dependent Claim
34 words
The method of claim 1 wherein said solvent composition comprises one or more compounds selected from the group consisting of xylene, butyl acetate, ethylene glycol monoethyl ether acetate and propylene glycol mono-alkyl ether acetate.
Claim 16
Dependent Claim
11 words
The photographic element produced according to the method of claim 1.
References Cited (Backward Citations)
US3046121A
Cited
US4015986A
Cited
US4104070A
Cited
US4241165A
Cited
EP0021719A2
Cited
US4573782A
Cited
US4439516A
Cited
US4576901A
Cited
EP0164248A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-12-04 | 1993-06-05 | 1993-12-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-12-04 | 1997-06-05 | 1997-12-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-12-04 | 2001-06-05 | 2001-12-05 | $7700.00 | Window Closed / Lapsed |