Assignee: APPLIED PHOTONIC DEVICES Inc
•
Filing: 1987-07-17
•
Granted: 1989-11-28
•
Expires: 2007-07-17
Abstract
Abstract Non-oxide or heavy metal fluoride glass optical fiber with or without a cladding and coated with an outer layer of an oxide glass having a glass transition temperature of less than 400° C. and a thermal expansion coefficient of less than about 19×10 -6 ° C. -1 . Also, a method of making and providing such coatings on non-oxide or fluoride glass, and fiber optic products prepared by such methods.
Inventors
- 👤 Lubos J. B. Vacha
- 👤 Cornelius T. Monyihan
- 👤 Peter C. Schultz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 08:37
CPC Classifications
C; C03; C03C; C03C13/00; C03C13/04; C03C13/048; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/01205; C03B37/01211; C03B37/01265; C03B37/01271; C03B37/014; C03B37/018; C03B37/02; C03B37/025; C03B37/027; C03C13/041; C03C13/042; C03B2201/00; C03B2201/60; C03B2201/70; C03B2201/80; C03B2201/82; Y; Y10; Y10S; Y10S65/00; Y10S65/15
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
114 words
A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises: preparing a preform comprising a non-oxide glass core, a non-oxide cladding therefore, and a protective coating of an oxide glass having a glass transition temperature below about 400° C. and a thermal expansion coefficient of less than about 19×10 -6 ° C. -1 ; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore, said oxide glass having a viscosity which is approximately the same as the viscosity of the non-oxide glass at the drawing temperature to obtain said coated optical fiber.
Claim 2
Independent Claim
114 words
A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises: preparing a preform comprising a non-oxide glass core, a non-oxide cladding therefore, and a protective coating of an oxide glass having a glass transition temperature below about 400° C. and a thermal expansion coefficient of less than about 19×10 -6 ° C. -1 ; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore, said oxide glass having a viscosity which is approximately the same as the viscosity of the non-oxide glass at the drawing temperature to obtain said coated optical fiber.
Claim 3
Dependent Claim
40 words
The method of claim 1 wherein the oxide glass coating is initially formed as a tube and the non-oxide glass core in the form of a solid, liquid or gas is placed into the tube prior to the drawing step.
Claim 4
Dependent Claim
26 words
The method of claim 2 wherein the core comprises a heavy metal fluoride glass and is added to the tube as a rod or by casting.
Claim 5
Dependent Claim
25 words
The method of claim 2 wherein the cladding comprises a fluoride glass which is added to the preform after the oxide glass tube is formed.
Claim 6
Dependent Claim
24 words
The method of claim 1 which further comprises initially forming a tube of said oxide glass from an alkali-boro-phosphate or alkali-Group II metal-phosphate composition.
Claim 7
Dependent Claim
29 words
The method of claim 1 which further comprises adding to said oxide glass one or more additional oxide components to impart a specific property to the oxide glass composition.
Claim 8
Independent Claim
127 words
A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises: preparing a preform which comprises a non-oxide glass core of a heavy metal fluoride glass and an overclad of an oxide glass having a glass transition temperature below about 400° C. and a thermal expansion coefficient of below about 19×10 -6 ° C. -1 ; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore and at a temperature range of between about 300° and 425° C., said oxide glass having a viscosity which is approximately the same as the viscosity of the fluoride glass at the drawing temperature to obtain said coated optical fiber.
Claim 9
Independent Claim
127 words
A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises: preparing a preform which comprises a non-oxide glass core of a heavy metal fluoride glass and an overclad of an oxide glass having a glass transition temperature below about 400° C. and a thermal expansion coefficient of below about 19×10 -6 ° C. -1 ; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore and at a temperature range of between about 300° and 425° C., said oxide glass having a viscosity which is approximately the same as the viscosity of the fluoride glass at the drawing temperature to obtain said coated optical fiber.
Claim 10
Dependent Claim
40 words
The method of claim 7 wherein the oxide glass coating is initially formed as a tube and the fluoride glass core in the form of a solid, liquid or gas is placed into the tube prior to the drawing step.
Claim 11
Dependent Claim
24 words
The method of claim 8 wherein the fluoride glass is added to the tube as a rod, by casting or by chemical vapor deposition.
Claim 12
Dependent Claim
50 words
The method of claim 7, wherein the preform further comprises a fluoride glass cladding between the core and overclad, which cladding is added to the preform after the oxide glass tube is formed, so that the oxide glass overclad is used as a protective coating for said core and cladding.
Claim 13
Dependent Claim
27 words
The method of claim 9 wherein the oxide glass has a refractive index sufficiently less than that of said core so as to act as a cladding.
Claim 14
Independent Claim
113 words
A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises: preparing a preform which comprises a non-oxide glass core and an overclad of an oxide glass of a phosphate material having a glass transition temperature below about 400° C. and a thermal expansion coefficient of below about 19×10 -6 ° C. -1 ; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore, said oxide glass having a viscosity which is approximately the same as the viscosity of the non-oxide glass at the drawing temperature to obtain said coated optical fiber.
Claim 15
Independent Claim
113 words
A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises: preparing a preform which comprises a non-oxide glass core and an overclad of an oxide glass of a phosphate material having a glass transition temperature below about 400° C. and a thermal expansion coefficient of below about 19×10 -6 ° C. -1 ; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore, said oxide glass having a viscosity which is approximately the same as the viscosity of the non-oxide glass at the drawing temperature to obtain said coated optical fiber.
Claim 16
Dependent Claim
36 words
The method of claim 12 wherein the oxide glass is formed as a tube of an alkali-boro-phosphate or alkali-alkaline earth-phosphate composition having a thermal expansion coefficient between about 15 and 19×10 -6 ° C. -1 .
Claim 17
Dependent Claim
30 words
The method of claim 12 which further comprises adding to said oxide glass one or more additional oxide forming components to impart a specific property to the oxide glass composition.
Claim 18
Dependent Claim
27 words
The method of claim 12 wherein the oxide glass has a refractive index sufficiently less than that of said core so as to act as a cladding.
Claim 19
Independent Claim
142 words
A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises: preparing a preform which comprises a non-oxide glass core and an overclad of an oxide glass having a glass transition temperature below about 400° C. and a thermal expansion coefficient of below about 19×10 -6 ° C. -1 by initially melting the oxide glass coating; rotating said molten oxide glass to form a tube of oxide glass; and placing the non-oxide glass into the tube of oxide glass to form the preform; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore, said oxide glass having a viscosity which is approximately the same as the viscosity of the non-oxide glass at the drawing temperature to obtain said coated optical fiber.
Claim 20
Independent Claim
142 words
A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises: preparing a preform which comprises a non-oxide glass core and an overclad of an oxide glass having a glass transition temperature below about 400° C. and a thermal expansion coefficient of below about 19×10 -6 ° C. -1 by initially melting the oxide glass coating; rotating said molten oxide glass to form a tube of oxide glass; and placing the non-oxide glass into the tube of oxide glass to form the preform; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore, said oxide glass having a viscosity which is approximately the same as the viscosity of the non-oxide glass at the drawing temperature to obtain said coated optical fiber.
Claim 21
Dependent Claim
29 words
The method of claim 16 wherein the rotating of said molten oxide glass is effected by casting said molten oxide glass into rotating mold means to form said tube.
Claim 22
Dependent Claim
30 words
The method of claim 17 wherein said non-oxide glass is a heavy metal fluoride glass and the fiber is drawn at a temperature range of about 300° and 425° C.
Claim 23
Dependent Claim
27 words
The method of claim 16 wherein the oxide glass has a refractive index sufficiently less than that of said core so as to act as a cladding.
Claim 24
Independent Claim
96 words
A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises: preparing a preform which comprises a non-oxide glass core of a heavy metal fluoride glass and an overclad of an oxide glass of a phosphate material; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore, said oxide glass having a viscosity which is approximately the same as the viscosity of the non-oxide glass at the drawing temperature to obtain said coated optical fiber.
Claim 25
Independent Claim
96 words
A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises: preparing a preform which comprises a non-oxide glass core of a heavy metal fluoride glass and an overclad of an oxide glass of a phosphate material; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore, said oxide glass having a viscosity which is approximately the same as the viscosity of the non-oxide glass at the drawing temperature to obtain said coated optical fiber.
Claim 26
Dependent Claim
33 words
The method of claim 20 wherein said phosphate oxide glass has a glass transition temperature below about 400° C. and a thermal expansion coefficient of below about 19×10 -6 ° C. -1 .
Claim 27
Dependent Claim
36 words
The method of claim 21 wherein the oxide glass is formed as a tube of an alkali-boro-phosphate or alkali-alkaline earth-phosphate composition having a thermal expansion coefficient between about 15 and 19×10 -6 ° C. -1 .
Claim 28
Dependent Claim
30 words
The method of claim 22 which further comprises adding to said oxide glass one or more additional oxide forming components to impart a specific property to the oxide glass composition.
Claim 29
Dependent Claim
30 words
The method of claim 23 wherein said non-oxide glass is a heavy metal fluoride glass and the fiber is drawn at a temperature range of about 300° and 425° C.
Claim 30
Dependent Claim
40 words
The method of claim 24 wherein the oxide glass coating is initially formed as a tube and the fluoride glass core in the form of a solid, liquid or gas is placed into the tube prior to the drawing step.
Claim 31
Dependent Claim
22 words
The method of claim 25 wherein the fluoride glass is added to the tube as a rod or by chemical vapor deposition.
Claim 32
Dependent Claim
49 words
The method of claim 25 wherein the preform further comprises a fluoride glass cladding between the core and overclad, which cladding is added to the preform after the oxide glass tube is formed so that the oxide glass overclad is used as a coating for said core and cladding.
Claim 33
Dependent Claim
29 words
The method of claim 25 wherein the rotating of said molten oxide glass is effected by casting said molten oxide glass into rotating mold means to form said tube.
Claim 34
Dependent Claim
27 words
The method of claim 20 wherein the oxide glass has a refractive index sufficiently less than that of said core so as to act as a cladding.
References Cited (Backward Citations)
US4141741A
Cited
US4328318A
Cited
US4358543A
Cited
US4380588A
Cited
US4343638A
Cited
US4346176A
Cited
US4265667A
Cited
US4441788A
Cited
US4445755A
Cited
US4418985A
Cited
US4439008A
Cited
US4681400A
Cited
US4538032A
Cited
US4468413A
Cited
US4660927A
Cited
US4552431A
Cited
US4519826A
Cited
US4537864A
Cited
US4627865A
Cited
US4768859A
Cited
US4597786A
Cited
US4674835A
Cited
US4750806A
Cited
US4709987A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-27 | 1993-05-29 | 1993-11-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-27 | 1997-05-29 | 1997-11-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-27 | 2001-05-29 | 2001-11-28 | $7700.00 | Window Closed / Lapsed |