Multi-component glass optical fiber for optical communication
Assignee: Toshiba Corp
•
Filing: 1982-05-26
•
Granted: 1983-12-06
•
Expires: 2002-05-26
Abstract
Abstract There is provided a multi-component system glass fiber for optical communication which comprises a multi-component system glass for core having a composition comprising SiO 2 , BaO, Al 2 O 3 , B 2 O 3 , at least one alkali metal oxide selected from Na 2 O, K 2 O and Li 2 O, MgO and CaO in amounts as specified in the specification and claims, and a multi-component system glass for clad layer having a composition comprising SiO 2 , Al 2 O 3 , B 2 O 3 , Na 2 O, K 2 O, Li 2 O, at least one alkaline earth metal selected from MgO and CaO in amounts as specified in the specification and claims. The core in the glass fiber for optical communication according to the present invention shows lower optical loss and the clad layer shows high weathering resistance, and the glass fiber according to the present invention suffers from no devitrification during fiber drawing and is excellent in dimensional stability.
Inventors
- 👤 Mituo Kasori
- 👤 Takeshi Takano
- 👤 Hironori Maki
- 👤 Naohiko Ogino
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:33
CPC Classifications
C; C03; C03C; C03C13/00; C03C13/04; C03C13/045; C03C13/046; Y; Y10; Y10S; Y10S501/00; Y10S501/90; Y10S501/903
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
241 words
A multi-component system glass fiber for optical communication which comprises: a core of a multi-component system glass having a composition consisting essentially of 35 to 45% by weight of SiO 2 , 35 to 45% by weight of BaO, 3 to 7% by weight of Al 2 O 3 , 9 to 13% by weight of B 2 O 3 , 1.2 to 4% by weight of at least one alkali metal oxide selected from the group consisting of Na 2 O, K 2 O and Li 2 O, the content of Na 2 O being 2.5% by weight or less, and 4 to 11% by weight of at least one alkaline earth metal oxide selected from the group consisting of MgO and CaO; and a clad layer, on said core, of a multi-component system glass having a composition consisting essentially of 66 to 71% by weight of SiO 2 , 4 to 7% by weight of Al 2 O 3 , 7 to 12% by weight of B 2 O 3 , 12 to 16% by weight of at least one alkali metal oxide selected from the group consisting of Na 2 O, K 2 O and Li 2 O, 2% by weight or less of at least one alkaline earth metal oxide selected from the group consisting of MgO and CaO, and 3% by weight or less of at least one of ZnO, ZrO 2 and TiO 2 .
Claim 2
Dependent Claim
241 words
A multi-component system glass fiber for optical communication which comprises: a core of a multi-component system glass having a composition consisting essentially of 35 to 45% by weight of SiO 2 , 35 to 45% by weight of BaO, 3 to 7% by weight of Al 2 O 3 , 9 to 13% by weight of B 2 O 3 , 1.2 to 4% by weight of at least one alkali metal oxide selected from the group consisting of Na 2 O, K 2 O and Li 2 O, the content of Na 2 O being 2.5% by weight or less, and 4 to 11% by weight of at least one alkaline earth metal oxide selected from the group consisting of MgO and CaO; and a clad layer, on said core, of a multi-component system glass having a composition consisting essentially of 66 to 71% by weight of SiO 2 , 4 to 7% by weight of Al 2 O 3 , 7 to 12% by weight of B 2 O 3 , 12 to 16% by weight of at least one alkali metal oxide selected from the group consisting of Na 2 O, K 2 O and Li 2 O, 2% by weight or less of at least one alkaline earth metal oxide selected from the group consisting of MgO and CaO, and 3% by weight or less of at least one of ZnO, ZrO 2 and TiO 2 .
Claim 3
Dependent Claim
244 words
A multi-component system glass fiber for optical communication according to claim 1, which comprises: a core of a multi-component system glass having a composition consisting essentially of 36 to 41% by weight of SiO 2 , 36 to 41% by weight of BaO, 3.5 to 5% by weight of Al 2 O 3 , 10 12% by weight of B 2 O 3 , 1.2% to 4% by weight of at least one alkali metal oxide selected from the group consisting of Na 2 O, K 2 O and Li 2 O, the content of Na 2 O being 1.5% by weight or less, and 4.5 to 7% by weight of at least one alkaline earth metal oxide selected from the group consisting of MgO and CaO; and a clad layer, on said core, of a multi-component system glass having a composition consisting essentially of 67 to 70% by weight of SiO 2 , 5.5 to 7% by weight of Al 2 O 3 , 7.5 to 10% by weight of B 2 O 3 , 13.5 to 16% by weight of at least one alkali metal oxide selected from the group consisting of Na 2 O, K 2 O and Li 2 O, 1% by weight or less of at least one alkaline earth metal oxide selected from the group consisting of MgO and CaO, and 2.5% by weight or less of at least one of ZnO, ZrO 2 and TiO 2 .
Claim 4
Dependent Claim
26 words
A multi-component system glass fiber for optical communication according to claim 1 wherein the amount of MgO in the core is 2 to 4% by weight.
Claim 5
Dependent Claim
26 words
A multi-component system glass fiber for optical communication according to claim 1 wherein the amount of CaO in the core is 3 to 7% by weight.
Claim 6
Dependent Claim
44 words
A multi-component system glass fiber for optical communication according to claim 1 wherein the amounts of Na 2 O, K 2 O and Li 2 O in the clad layer are 6 to 8%, 3.5 to 6% and 2 to 4% by weight, respectively.
Claim 7
Dependent Claim
29 words
A multi-component system glass fiber for optical communication according to claim 1, wherein the amount of Na 2 O in the core is at least about 1.2% by weight.
References Cited (Backward Citations)
GB1301409A
Cited
US3841882A
Cited
US4275951A
Cited
US4264131A
Cited
US4367012A
Cited
US4265667A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-05 | 1987-06-06 | 1987-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-05 | 1991-06-06 | 1991-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-05 | 1995-06-06 | 1995-12-06 | $7700.00 | Window Closed / Lapsed |