Chemical preparation of zirconium-aluminum-magnesium oxide composites
Assignee: Dow Chemical Co
•
Filing: 1986-01-24
•
Granted: 1989-11-14
•
Expires: 2006-01-24
Abstract
Abstract A composite ceramic material having improved properties is disclosed as well as several methods for preparing the same. The composite powder is substantially comprised of zirconia and spinel phases, produced by precipitation and calcination of the precipitate of the oxide forming precursor salts. A preferred method for introducing the zirconium is as a soluble and/or decomposable salt during precipitation of the spinel forming hydroxyl or halo hydroxyl spinel forming salts. The zirconium salt decomposes to zirconia during calcining and/or sintering of the powder resulting from the precipitation. A preferred composite is that obtained from magnesium and aluminum salts, resulting in a MgAl 2 O 4 spinel and intimately admixed ZrO 2 which contains a stabilizing agent.
Inventors
- 👤 Walter W. Henslee
- 👤 Thomas S. Witkowski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 17:04
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/44; C04B35/443; C01; C01G; C01G25/00; C01G25/006; C01P; C01P2002/00; C01P2002/30; C01P2002/32; C01P2004/00; C01P2004/60; C01P2004/62; C01P2004/80
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
153 words
A sinterable precursor powder convertible to zirconia-spinel ceramic composites comprised of spinel forming metal compounds intimately admixed with a zirconium compound, said powder consisting of an intimate admixture derived from intimately admixing in a liquid medium (1) at least one decomposable salt of a metal or metals which form spinel crystal structures on calcination, (2) a zirconium compound selected from the group consisting of (a) a salt capable of being converted upon heating to zirconium oxide, or (b) a fine zirconium oxide powder which admixture is co-precipitated, and the solids recovered, said metal or metals being present in mole ratios to form the spinel structure with or without an additional amount of one of the spinel forming metals to form a segregated metal oxide phase when converted and said metal/metals and said zirconium compound being present in an amount greater than 0 but less than 100% of the total weight of the composition.
Claim 2
Dependent Claim
153 words
A sinterable precursor powder convertible to zirconia-spinel ceramic composites comprised of spinel forming metal compounds intimately admixed with a zirconium compound, said powder consisting of an intimate admixture derived from intimately admixing in a liquid medium (1) at least one decomposable salt of a metal or metals which form spinel crystal structures on calcination, (2) a zirconium compound selected from the group consisting of (a) a salt capable of being converted upon heating to zirconium oxide, or (b) a fine zirconium oxide powder which admixture is co-precipitated, and the solids recovered, said metal or metals being present in mole ratios to form the spinel structure with or without an additional amount of one of the spinel forming metals to form a segregated metal oxide phase when converted and said metal/metals and said zirconium compound being present in an amount greater than 0 but less than 100% of the total weight of the composition.
Claim 3
Dependent Claim
17 words
The powder of claim 1 wherein the spinel forming metal compounds are compounds of magnesium and aluminum.
Claim 4
Dependent Claim
22 words
The powder of claim 1 wherein the zirconium compound is present in amount of from greater than zero to less than 50%.
Claim 5
Dependent Claim
17 words
The powder of claim 1 wherein the zirconium compound is present in an amount of from 5-20%.
Claim 6
Dependent Claim
17 words
The powder of claim 1, wherein the spinel forming metal compounds are compounds of magnesium and aluminum.
Claim 7
Dependent Claim
35 words
A composite produced by heating the powder of claim 1 to a temperature sufficient to substantially convert the precursor components to a composite of the spinel and zirconium oxide with or without other oxide stabilizers.
Claim 8
Dependent Claim
18 words
The composite of claim 6 comprising a spinel matrix and a zirconium oxide segregated phase intimately dispersed therein.
Claim 9
Dependent Claim
18 words
The composite as defined in claim 6 wherein said zirconium oxide particle size is less than one micron.
Claim 10
Independent Claim
164 words
A method for preparing a sinterable ceramic material which comprises (a) intimately admixing in a liquid medium (1) at least one decomposable salt of a metal or metals which form spinel crystal structures on calcination (2) a zirconium salt capable of being converted to zirconium oxide on heating or a fine zirconium oxide powder; (b) precipitating said salt or salts by evaporation at a pH wherein the soluble salt or salts precipitate; (c) recovering said precipitate substantially free of the liquid medium in which the precipitation occurred; and (d) calcining said precipitate at least to a temperature where the spinel structure forms and zirconium oxide is present wherein said spine forming metals are present in mole ratios sufficient to form the spinel structure as the major composite powder component of the composition and wherein the zirconium compound is present in a sufficient quantity to constitute from greater than 0 to less than 100 weight percent of the total composition as the Zirconium oxide component.
Claim 11
Independent Claim
164 words
A method for preparing a sinterable ceramic material which comprises (a) intimately admixing in a liquid medium (1) at least one decomposable salt of a metal or metals which form spinel crystal structures on calcination (2) a zirconium salt capable of being converted to zirconium oxide on heating or a fine zirconium oxide powder; (b) precipitating said salt or salts by evaporation at a pH wherein the soluble salt or salts precipitate; (c) recovering said precipitate substantially free of the liquid medium in which the precipitation occurred; and (d) calcining said precipitate at least to a temperature where the spinel structure forms and zirconium oxide is present wherein said spine forming metals are present in mole ratios sufficient to form the spinel structure as the major composite powder component of the composition and wherein the zirconium compound is present in a sufficient quantity to constitute from greater than 0 to less than 100 weight percent of the total composition as the Zirconium oxide component.
Claim 12
Dependent Claim
17 words
The method of claim 9 wherein said spinel forming metal salts are magnesium salts and aluminum salts.
Claim 13
Dependent Claim
17 words
The method of claim 9 wherein said pH of precipitation is from about 4 to about 12.
Claim 14
Dependent Claim
23 words
The method of claim 9 wherein a stabilized zirconium oxide is added to or formed in situ with said spinel forming metal salts.
Claim 15
Dependent Claim
21 words
The method of claim 11 wherein a stabilizer, selected from the group of magnesium, calcium, yttrium, or aluminum compounds is included.
References Cited (Backward Citations)
US2409844A
Cited
DE1939119A1
Cited
SU687048A1
Cited
DE2810134A1
Cited
US4221650A
Cited
US4314827A
Cited
JPS589875A
Cited
DE3230216A1
Cited
JPS5832066A
Cited
US4626518A
Cited
SU1073225A1
Cited
US4506024A
Cited
EP0140638A1
Cited
US4587225A
Cited
DE3512368A1
Cited
US4525464A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-13 | 1993-05-15 | 1993-11-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-13 | 1997-05-15 | 1997-11-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-13 | 2001-05-15 | 2001-11-14 | $7700.00 | Window Closed / Lapsed |