Abstract A method for manufacture of a high toughness sintered body, characterized by sintering a shaped body of a mixed powder consisting essentially of from 40 to 70% by weight of a first component of powdered ZrO 2 containing at least one stabilizer selected from the group consisting of Y 2 O 3 , CaO, and MgO and having an average particle diameter of not more than 1μ and from 30 to 60% by weight of a second component of powdered α-Al 2 O 3 having an average particle diameter of not more than 1 μm, which mixed powder may also contain not more than 3% by weight of SiO 2 , not more than 0.5% by weight of Fe 2 O 3 , or not more than 0.5% by weight of TiO 2 in a combined proportion of not more than 3% by weight at a temperature in the range of from 1400° C. to 1600° C. under normal pressure thereby producing a sintered body wherein at least 90% by weight of ZrO 2 particles present therein are accounted for by tetragonal and cubic crystals, the ratio of said tetragonal crystals to said cubic crystals is at least 1:3, and the average crystal particle diameter of the entire sintered body is at least 3μ.
A method for manufacture of a high toughness sintered body, comprising: (a) preparing a powder mixture containing 40-99.5 wt% of Component A consisting essentially of ZrO 2 powder having an average particle diameter of no longer than 1 μm and 1-6 mol% of Y 2 O 3 , 7 mol% of MgO or 6 mol% of CaO as a stabilizer and 0.5-60 wt% of Component B consisting essentially of α-Al 2 O 3 powder having an average particle diameter of not longer than 1 μm by uniformally mixing water soluble salts of ZrO 2 , stabilizer and Al 2 O 3 in the form of an aqueous solution and coprecipitating the powder mixture; and (b) sintering the powder resulting from step (a) at temperature in the range of from 1400° C. to 1600° C. at atmospheric pressure to obtain a sintered body wherein at least 90% by weight of ZrO 2 particles present therein are accounted for by tetragonal and cubic crystals, the ratios of said tetragonal crystals to said cubic crystals is at least 1:3, and the average crystal particle diameter of the entire sintered body is 3μ or less; wherein the mixed powder contains not more than 3 wt% of SiO 2 , not more than 0.5 wt% of Fe 2 O 3 , not more than 0.5 wt% of TiO 2 and not more than 3 wt% total of the SiO 2 , the Fe 2 O 3 and the TiO 2 based on the total weight of the mixed powder.
Claim 2
Independent Claim
254 words
A method for manufacture of a high toughness sintered body, comprising: (a) preparing a powder mixture containing 40-99.5 wt% of Component A consisting essentially of ZrO 2 powder having an average particle diameter of no longer than 1 μm and 1-6 mol% of Y 2 O 3 , 7 mol% of MgO or 6 mol% of CaO as a stabilizer and 0.5-60 wt% of Component B consisting essentially of α-Al 2 O 3 powder having an average particle diameter of not longer than 1 μm by uniformally mixing water soluble salts of ZrO 2 , stabilizer and Al 2 O 3 in the form of an aqueous solution and coprecipitating the powder mixture; and (b) sintering the powder resulting from step (a) at temperature in the range of from 1400° C. to 1600° C. at atmospheric pressure to obtain a sintered body wherein at least 90% by weight of ZrO 2 particles present therein are accounted for by tetragonal and cubic crystals, the ratios of said tetragonal crystals to said cubic crystals is at least 1:3, and the average crystal particle diameter of the entire sintered body is 3μ or less; wherein the mixed powder contains not more than 3 wt% of SiO 2 , not more than 0.5 wt% of Fe 2 O 3 , not more than 0.5 wt% of TiO 2 and not more than 3 wt% total of the SiO 2 , the Fe 2 O 3 and the TiO 2 based on the total weight of the mixed powder.
Claim 3
Dependent Claim
34 words
A method according to claim 1, wherein a mixed powder obtained by substituting HfO 2 for part or the whole of said ZrO 2 is used in the place of said ZrO 2 .