Method of depositing textured tin oxide
Assignee: BP Solar International LLC
•
Filing: 1987-08-31
•
Granted: 1989-11-14
•
Expires: 2007-08-31
Abstract
Abstract A method of forming a textured layer of tin oxide on a vitreous substrate in which the thickness and degree of texture of the layer can be controlled independently of one another. The method comprises the steps of depositing a first film of tin oxide on the substrate by chemical vapor deposition from a first reactant mixture of tin chloride, water, and an alcohol and depositing a second film of tin oxide on the first tin oxide film by chemical vapor deposition from a second reactant mixture of tin chloride and water. Where the substrate is ordinary soda lime glass, it preferably is first coated with a film of silicon dioxide. The method permits deposition of substantially uniform layers of tin oxide in a continuous deposition process.
Inventors
- 👤 James G. O'Dowd
- 👤 Anthony W. Catalano
- 👤 Charles M. Fortmann
- 👤 Ora J. Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:44
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/407; C03; C03C; C03C17/00; C03C17/34; C03C17/3411; C03C17/3417; H; H10; H10F; H10F71/00; H10F71/138; H10F77/00; H10F77/70; H10F77/707; Y; Y02; Y02E; Y02E10/00; Y02E10/50
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
94 words
A method of forming a textured layer of transparent conductive oxide on a vitreous substrate, comprising the steps of: depositing a first film of tin oxide on said substrate by chemical vapor deposition from a first reactant mixture comprising tin chloride, water, and alcohol while holding said substrate at a preselected reaction temperature; and depositing a second film of tin oxide on said first tin oxide film by chemical vapor deposition from a second reactant mixture free of alcohol and comprising tin chloride and water while holding said substrate at said preselected reaction temperature.
Claim 2
Independent Claim
94 words
A method of forming a textured layer of transparent conductive oxide on a vitreous substrate, comprising the steps of: depositing a first film of tin oxide on said substrate by chemical vapor deposition from a first reactant mixture comprising tin chloride, water, and alcohol while holding said substrate at a preselected reaction temperature; and depositing a second film of tin oxide on said first tin oxide film by chemical vapor deposition from a second reactant mixture free of alcohol and comprising tin chloride and water while holding said substrate at said preselected reaction temperature.
Claim 3
Dependent Claim
16 words
The method of claim 1, wherein said preselected reaction temperature is at least about 500° C.
Claim 4
Dependent Claim
15 words
The method of claim 1, wherein the alcohol in said first reactant mixture is methanol.
Claim 5
Dependent Claim
15 words
The method of claim 1, wherein the alcohol in said first reactant mixture is propanol.
Claim 6
Dependent Claim
15 words
The method of claim 1, wherein the alcohol in said first reactant mixture is butanol.
Claim 7
Dependent Claim
27 words
The method of claim 1, wherein the molar ratio of alcohol to the total of said first reactant mixture is less than or equal to about 1:4.
Claim 8
Dependent Claim
27 words
The method of claim 1, wherein the molar ratio of alcohol to the total of said first reactant mixture is less than or equal to about 1:20.
Claim 9
Dependent Claim
26 words
The method of claim 1, further comprising the step of depositing a film of silicon dioxide on said substrate prior to said first film depositing step.
Claim 10
Dependent Claim
15 words
The method of claim 8, wherein said silicon dioxide film is about 30-600 nanometers thick.
Claim 11
Dependent Claim
19 words
The method of claim 1, wherein each of said first and second reactant mixtures further includes a conductivity-modifying dopant.
Claim 12
Dependent Claim
12 words
The method of claim 10, wherein said conductivity modifying dopant is fluorine.
Claim 13
Dependent Claim
39 words
The method of claim 11, wherein said dopant is introduced to each of said reactant mixtures by hydrofluoric acid to said water in said respective reactant mixture in a molar ratio of water to hydrofluoric acid of about 99:1.
Claim 14
Dependent Claim
26 words
The method of claim 11, wherein said dopant is introduced to each of said reactant mixtures by adding hydrogen fluoride gas to said respective reactant mixture.
Claim 15
Independent Claim
161 words
A method of forming a textured layer of transparent conductive oxide on a vitreous substrate, comprising the steps of: depositing a first film of tin oxide on said substrate by chemical vapor deposition from a first reactant mixture comprising tin chloride, water, and alcohol while holding said substrate at a preselected reaction temperature, said first reactant mixture being conveyed to a first injection zone at said substrate by a first carrier gas containing tin chloride, a second carrier gas containing water, and a third carrier gas containing alcohol; and depositing a second film of tin oxide on said first tin oxide film by chemical vapor deposition from a second reactant mixture free of alcohol and comprising tin chloride and water while holding said substrate at said preselected reaction temperature, said second reactant mixture being conveyed to a second injection zone at said first tin oxide film by a fourth carrier gas containing tin chloride and a fifth carrier gas containing water.
Claim 16
Independent Claim
161 words
A method of forming a textured layer of transparent conductive oxide on a vitreous substrate, comprising the steps of: depositing a first film of tin oxide on said substrate by chemical vapor deposition from a first reactant mixture comprising tin chloride, water, and alcohol while holding said substrate at a preselected reaction temperature, said first reactant mixture being conveyed to a first injection zone at said substrate by a first carrier gas containing tin chloride, a second carrier gas containing water, and a third carrier gas containing alcohol; and depositing a second film of tin oxide on said first tin oxide film by chemical vapor deposition from a second reactant mixture free of alcohol and comprising tin chloride and water while holding said substrate at said preselected reaction temperature, said second reactant mixture being conveyed to a second injection zone at said first tin oxide film by a fourth carrier gas containing tin chloride and a fifth carrier gas containing water.
Claim 17
Dependent Claim
33 words
The method of claim 14, wherein each of said first and fourth carrier gases is nitrogen and is bubbled through a supply of tin chloride held at a temperature of about 34° C.
Claim 18
Dependent Claim
32 words
The method of claim 14, wherein each of said first and fifth carrier gases is nitrogen and is bubbled through a supply of water held at a temperature of about 80° C.
Claim 19
Dependent Claim
28 words
The method of claim 14, wherein said third carrier gas is nitrogen and is bubbled through a supply of alcohol held at a temperature of about 4° C.
Claim 20
Dependent Claim
15 words
The method of claim 14, wherein the alcohol in said first reactant mixture is methanol.
Claim 21
Dependent Claim
18 words
The method of claim 14, wherein each of said second and fifth carrier gases further contains hydrofluoric acid.
Claim 22
Dependent Claim
26 words
The method of claim 19, wherein the molar ratio of water to hydrofluoric acid in each of said second and fifth carrier gases is about 99:1.
Claim 23
Dependent Claim
54 words
The method of claim 14, wherein: said first injection zone includes three concentric jet areas; said first carrier gas is conveyed to one of said jet areas of said first injection zone; and said second and third carrier gases are conveyed in common to another of said jet areas of said first injection zone.
Claim 24
Dependent Claim
50 words
The method of claim 21, wherein: said second injection zone includes three concentric jet areas; said fourth carrier gas is conveyed to one of said jet areas of said second injection zone; and said fifth carrier gas is conveyed to another of said jet areas of said second injection zone.
Claim 25
Dependent Claim
56 words
The method of claim 22, further comprising the step of conveying a separator gas to a third one of said jet areas in each of said first and second injection zones, said third one of said jet areas being located radially between said one and said another of said jet areas of each respective injection zone.
Claim 26
Dependent Claim
17 words
The method of claim 23, wherein said separator gas is nitrogen and further includes hydrogen fluoride gas.
Claim 27
Independent Claim
153 words
A method of forming a textured layer of transparent conductive oxide on a vitreous substrate, comprising the steps of: depositing a first film of tin oxide on said substrate in a first deposition chamber while said substrate is conveyed through said first deposition chamber, said first tin oxide film being deposited by chemical vapor deposition from a first reactant mixture comprising tin chloride, water, and alcohol while holding said substrate at a preselected first reaction temperature; conveying said substrate from said first deposition chamber to a second deposition chamber; and depositing a second film of tin oxide on said first tin oxide film in said second deposition chamber while said substrate is conveyed through said second deposition chamber, said second tin oxide film being deposited by chemical vapor deposition from a second reactant mixture free of alcohol and comprising tin chloride and water while holding said substrate at a preselected second reaction temperature.
Claim 28
Independent Claim
153 words
A method of forming a textured layer of transparent conductive oxide on a vitreous substrate, comprising the steps of: depositing a first film of tin oxide on said substrate in a first deposition chamber while said substrate is conveyed through said first deposition chamber, said first tin oxide film being deposited by chemical vapor deposition from a first reactant mixture comprising tin chloride, water, and alcohol while holding said substrate at a preselected first reaction temperature; conveying said substrate from said first deposition chamber to a second deposition chamber; and depositing a second film of tin oxide on said first tin oxide film in said second deposition chamber while said substrate is conveyed through said second deposition chamber, said second tin oxide film being deposited by chemical vapor deposition from a second reactant mixture free of alcohol and comprising tin chloride and water while holding said substrate at a preselected second reaction temperature.
Claim 29
Dependent Claim
27 words
The method of claim 25, wherein the molar ratio of alcohol to the total of said first reactant mixture is less than or equal to about 1:4.
Claim 30
Dependent Claim
27 words
The method of claim 25, wherein the molar ratio of alcohol to the total of said first reactant mixture is less than or equal to about 1:20.
Claim 31
Dependent Claim
15 words
The method of claim 25, wherein the alcohol in said first reactant mixture is methanol.
Claim 32
Dependent Claim
45 words
The method of claim 28, wherein: the molar ratio of tin chloride in said first reactant mixture to tin chloride in said second reactant mixture is about 2:1; and the molar ratio of methanol to the total of said first reactant mixture is about 1.82:100.
Claim 33
Dependent Claim
45 words
The method of claim 28, wherein: the molar ratio of tin chloride in said first reactant mixture to tin chloride in said second reactant mixture is about 1:3; and the molar ratio of methanol to the total of said first reactant mixture is about 3.61:100.
Claim 34
Dependent Claim
45 words
The method of claim 28, wherein: the molar ratio of tin chloride in said first reactant mixture to tin chloride in said second reactant mixture is about 1:6; and the molar ratio of methanol to the total of said first reactant mixture is about 4.26:100.
References Cited (Backward Citations)
US2692836A
Cited
US2898496A
Cited
US3306768A
Cited
US4329379A
Cited
US4235945A
Cited
US4387134A
Cited
US4325987A
Cited
US4344817A
Cited
US4476158A
Cited
US4377613A
Cited
US4532537A
Cited
US4612217A
Cited
EP0186481A2
Cited
WO1986006658A1
Cited
US4696837A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-13 | 1993-05-15 | 1993-11-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-13 | 1997-05-15 | 1997-11-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-13 | 2001-05-15 | 2001-11-14 | $7700.00 | Window Closed / Lapsed |