Diamond compacts and process for making same

Assignee: Australian National University
•
Filing: 1985-08-23
•
Granted: 1989-10-17
•
Expires: 2005-08-23
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A process for producing a diamond compact having a compressive strength of at least 10 kbars, the process being performed in the graphite stability field at a maximum pressure of 40 kbars at a temperature of between 1100° C. and 1600° C. for a time which permits plastic deformation of the diamond crystals giving face-to-face contacts there-between and a substantial or complete degree of chemical equilibration between the bonding agent and the diamond crystals. Bonding agents are selected from elements and alloys which produce a bond with diamond having a melting point above 1600° C. and which inhibit the formation of free graphite in the compact.

Inventors

  • 👤 Alfred E. Ringwood

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-05 15:46
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/6303; C04B35/6316; B; B01; B01J; B01J3/00; B01J3/06; B01J3/062; C04B35/515; C04B35/52; C04B35/56; C04B35/5607; C04B35/5626; C04B35/628; C04B35/62802; C04B35/64; C04B35/645; C04B35/65; C22; C22C; C22C26/00; B01J2203/00; B01J2203/06; B01J2203/0605; B01J2203/062; B01J2203/065; B01J2203/0655; B01J2203/0675; B01J2203/0685; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/38; C04B2235/3817; C04B2235/3826; C04B2235/3839; C04B2235/3843; C04B2235/40; C04B2235/404; C04B2235/42; C04B2235/421; C04B2235/422; C04B2235/427; C04B2235/428; C04B2235/50; C04B2235/54; C04B2235/5418; C04B2235/5436; C04B2235/5463; C04B2235/5472; C04B2235/65; C04B2235/656; C04B2235/70; C04B2235/72; C04B2235/721; C04B2235/728; C04B2235/74; C04B2235/77; C04B2235/80; C04B2235/95; C04B2235/96

Claims Analysis

Total Claims: 20
Claim 1
Independent Claim 260 words
A process for producing a diamond compact for cutting, turning drilling, and otherwise working ultra-hard ceramics, carbides and rocks which comprises: (i) intimately mixing a mass of particulate diamond crystals with a solid particulate powder bonding agent in the proportions 60-95 volume percent of diamond to 40-5 volume percent of bonding agent, the bonding agent comprising an element which reacts with carbon to form a stable carbide having a melting point exceeding about 1600° C. or a metallic alloy containing such element; (ii) subjecting the mixture to a temperature in the range of 1100°-1600° C. at a mean confining pressure in the range of 10 kbars to 40 kbars, said combination of mean confining pressure and temperature lying within the graphite stability field; and (iii) maintaining the temperature and pressure conditions of the mixture for a period greater than about 3 minutes to cause said element in the bonding agent to react extensively with carbon in the diamond crystals to form an interstitial carbide phase having a melting point about 1600° C. providing a strong bond between the diamond crystals while inhibiting the formation of free graphite by retrogressive transformation from diamond, said period being sufficient to result in substantial plastic deformation of the diamond crystals whereby contact between the diamond crystals occur over extended mating surfaces and also to result in substantial chemical equilibrium between the bonding agent and the diamond crystals whereby there is produced a thermally stable diamond compact having a minimum melting point above 1600° C. and a compressive strength above 10 kbars at ambient temperature.
Claim 2
Dependent Claim 260 words
A process for producing a diamond compact for cutting, turning drilling, and otherwise working ultra-hard ceramics, carbides and rocks which comprises: (i) intimately mixing a mass of particulate diamond crystals with a solid particulate powder bonding agent in the proportions 60-95 volume percent of diamond to 40-5 volume percent of bonding agent, the bonding agent comprising an element which reacts with carbon to form a stable carbide having a melting point exceeding about 1600° C. or a metallic alloy containing such element; (ii) subjecting the mixture to a temperature in the range of 1100°-1600° C. at a mean confining pressure in the range of 10 kbars to 40 kbars, said combination of mean confining pressure and temperature lying within the graphite stability field; and (iii) maintaining the temperature and pressure conditions of the mixture for a period greater than about 3 minutes to cause said element in the bonding agent to react extensively with carbon in the diamond crystals to form an interstitial carbide phase having a melting point about 1600° C. providing a strong bond between the diamond crystals while inhibiting the formation of free graphite by retrogressive transformation from diamond, said period being sufficient to result in substantial plastic deformation of the diamond crystals whereby contact between the diamond crystals occur over extended mating surfaces and also to result in substantial chemical equilibrium between the bonding agent and the diamond crystals whereby there is produced a thermally stable diamond compact having a minimum melting point above 1600° C. and a compressive strength above 10 kbars at ambient temperature.
Claim 3
Dependent Claim 37 words
A process according to claim 1, wherein said element is silicon which melts under said temperature and pressure conditions and reacts with carbon in the diamond crystals to produce said interstitial carbide phase comprised of silicon carbide.
Claim 4
Dependent Claim 56 words
A process according to claim 2, wherein an elevated temperature up to 1600° C. is applied to the intimate mixture prior to application of pressure in the range of 10 kbars to 40 kbars to maximize the degree of plastic deformation of said diamond crystals and to minimize production of graphite by retrogressive transformation of diamond.
Claim 5
Dependent Claim 27 words
A process according to claim 1, wherein said element is selected from the group comprising titanium, tungsten, molybdenum, niobium, tantalum, zirconium, hafnium, chromium, vanadium, scandium and boron.
Claim 6
Dependent Claim 39 words
A process according to claim 4, wherein said element reacts with carbon in the diamond crystals in the solid state to form said interstitial carbide phase by solid state reaction during the application of said temperature and pressure conditions.
Claim 7
Dependent Claim 33 words
A process according to claim 4, wherein an elevated temperature up to 1600° C. is applied to the ultimate mixture prior to application of pressure within the range 10 kbars to 40 kbars.
Claim 8
Dependent Claim 32 words
A process according to claim 1, wherein the applied pressure is in the range of 15 to 30 kbars and the applied temperature is in the range 1200° C. to 1600° C.
Claim 9
Dependent Claim 31 words
A process according to claim 1, wherein the intimate mixing is performed by applying the bonding agent to the surfaces of the diamond crystals in the form of coatings or films.
Claim 10
Dependent Claim 19 words
A process according to claim 1, wherein said temperature and pressure conditions are maintained for more than 5 minutes.
Claim 11
Dependent Claim 256 words
A process for producing a diamond compact for cutting, turning drilling, and otherwise working ultra-hard ceramics, carbides and rocks which comprises: (i) intimately mixing a mass of particulate diamond crystals with a solid particulate powder bonding agent in the proportions 60-95 volume percent of diamond to 40-5 volume percent of bonding agent, the bonding agent comprising a metal which does not form a stable carbide but which when heated in contact with a diamond surface becomes strongly bonded to that surface by a mechanism which includes acceptance of carbon into solid solution in its crystal lattice, and which does not melt at temperatures below 1600° C. when in contact with carbon; (ii) subjecting the mixture to a temperature in the range of 1100°-1600° C. at a mean confining pressure of between 10 kbars to 40 kbars, said combination of mean confining pressure and temperature lying within the graphite stability field; and (iii) maintaining the temperature and pressure conditions on the mixture for a period greater than about 3 minutes to cause said metal to accept carbon from the diamond crystals into solid solution thereby to become strongly bonded to the diamond crystals while inhibiting the formation of free graphite by retrogressive transformation from diamond, said period being sufficient to result in substantial plastic deformation of the diamond crystals whereby contacts between the diamond crystals occur over extended mating surfaces and there is produced a, thermally stable diamond compact having a minimum melting point above 1600° C. and a compressive strength above 10 kbars at ambient temperature.
Claim 12
Dependent Claim 256 words
A process for producing a diamond compact for cutting, turning drilling, and otherwise working ultra-hard ceramics, carbides and rocks which comprises: (i) intimately mixing a mass of particulate diamond crystals with a solid particulate powder bonding agent in the proportions 60-95 volume percent of diamond to 40-5 volume percent of bonding agent, the bonding agent comprising a metal which does not form a stable carbide but which when heated in contact with a diamond surface becomes strongly bonded to that surface by a mechanism which includes acceptance of carbon into solid solution in its crystal lattice, and which does not melt at temperatures below 1600° C. when in contact with carbon; (ii) subjecting the mixture to a temperature in the range of 1100°-1600° C. at a mean confining pressure of between 10 kbars to 40 kbars, said combination of mean confining pressure and temperature lying within the graphite stability field; and (iii) maintaining the temperature and pressure conditions on the mixture for a period greater than about 3 minutes to cause said metal to accept carbon from the diamond crystals into solid solution thereby to become strongly bonded to the diamond crystals while inhibiting the formation of free graphite by retrogressive transformation from diamond, said period being sufficient to result in substantial plastic deformation of the diamond crystals whereby contacts between the diamond crystals occur over extended mating surfaces and there is produced a, thermally stable diamond compact having a minimum melting point above 1600° C. and a compressive strength above 10 kbars at ambient temperature.
Claim 13
Dependent Claim 11 words
A process according to claim 10 wherein said metal is rhenium.
Claim 14
Dependent Claim 22 words
A process according to claim 10, wherein said metal is selected from the group consisting of rhodium, ruthenium, iridium, osmium and platinum.
Claim 15
Dependent Claim 59 words
A process according to claim 10, wherein an elevated temperature up to 1600° C. is applied to the intimate mixture prior to the application of pressure in the range of 10 kbars to 40 kbars whereby to maximize the degree of plastic deformation of the diamond crystals and to minimize formation of free carbon by retrogressive transformation of diamond.
Claim 16
Dependent Claim 33 words
A process according to claim 10, wherein the applied pressure is in the range of 15 to 30 kbars and the applied temperature is in the range of 1200° C. to 1600° C.
Claim 17
Dependent Claim 31 words
A process according to claim 10, wherein the intimate mixing is performed by applying the bonding agent to the surfaces of the diamond crystals in the form of coatings or films.
Claim 18
Dependent Claim 19 words
A process according to claim 10, wherein said temperature and pressure conditions are maintained for more than 5 minutes.
Claim 19
Dependent Claim 18 words
A process as in claim 1 wherein the bonding agent has a particle size less than 50 microns.
Claim 20
Dependent Claim 18 words
A process as in claim 10 wherein the bonding agent has a particle size less than 50 microns.

References Cited (Backward Citations)

US3574580A Cited
US4142869A Cited
US4124401A Cited
US4167399A Cited
US4168957A Cited
US4151686A Cited
US4241135A Cited
US4231195A Cited
US4259090A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1992-10-16 1993-04-17 1993-10-17 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1996-10-16 1997-04-17 1997-10-17 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 2000-10-16 2001-04-17 2001-10-17 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag