Method of making bipolar integrated circuits

Claim 1

A method of fabricating a bipolar polysilicon emitter transistor in a single crystal substrate, the method including defining a doped well in the substrate by implanting phosphorus dopant ions at a dose of about 7.7×10 12 /cm 2 into the well region at an energy of about 100 KeV and heating the substrate to drive in the dopant, implanting boron ions at a dose of about 2.8×10 12 /cm 2 and at an energy of about 160 KeV and further heating the substrate to drive in the boron dopant and to effect compensation between the two dopants whereby the peak net dopant concentration is disposed at a depth of 2 to 5 microns below the substrate surface, implanting boron ions into the well thus forming to define a p-type base layer depositing a body of undoped polysilicon on a selected area of the base layer so as to define a polysilicon emitter, providing an oxide coating on the polysilicon emitter body, implanting boron ions into the base layer to define p+-type base contact regions, and oxide layer on the emitter body providing a mask whereby the base contact regions are aligned with the emitter body and whereby implantation into the emitter body is inhibited, implanting an n-type dopant into the well to provide a collector contact, heating the substrate to drive in the implanted base contact regions and collector contact, and applying metal contacts to the collector contact, the base contact regions and the polysilicon emitter body.

Claim 2

A method of fabricating a bipolar polysilicon emitter transistor in a single crystal substrate, the method including defining a doped well in the substrate by implanting phosphorus dopant ions at a dose of about 7.7×10 12 /cm 2 into the well region at an energy of about 100 KeV and heating the substrate to drive in the dopant, implanting boron ions at a dose of about 2.8×10 12 /cm 2 and at an energy of about 160 KeV and further heating the substrate to drive in the boron dopant and to effect compensation between the two dopants whereby the peak net dopant concentration is disposed at a depth of 2 to 5 microns below the substrate surface, implanting boron ions into the well thus forming to define a p-type base layer depositing a body of undoped polysilicon on a selected area of the base layer so as to define a polysilicon emitter, providing an oxide coating on the polysilicon emitter body, implanting boron ions into the base layer to define p+-type base contact regions, and oxide layer on the emitter body providing a mask whereby the base contact regions are aligned with the emitter body and whereby implantation into the emitter body is inhibited, implanting an n-type dopant into the well to provide a collector contact, heating the substrate to drive in the implanted base contact regions and collector contact, and applying metal contacts to the collector contact, the base contact regions and the polysilicon emitter body.

Claim 3

A method of fabricating a bipolar polysilicon emitter transistor in a doped well in a single crystal silicon substrate, the method including the steps of: implanting phosphorus ions into a well region at an energy of about 100 KeV and a dose of about 7.7×10 12 /cm 2 ; heating the substrate to a temperature of about 1175° C. to drive in the dopant; implanting boron ions into said well region at an energy of about 160 KeV and a dose of about 2.8×10 12 /cm 2 ; further heating the substrate to a temperature of about 1175° C. to drive in the boron dopant and to effect compensation between the phosphorus and boron dopants providing a peak dopant concentration of 4.5×10 15 cm -3 to 4.5.×10 16 cm -3 at a depth of 2 to 5 microns below the substrate surface; providing a field oxide pattern having first and second openings over said doped well; providing a thin oxide layer in said first and second openings; impanting boron ions into said doped well via said first opening to define a p-type base layer; providing a further opening a said field oxide over a central region of said base layer, said central region ultimately becoming a base region of the transistors; providing a polysilicon emitter body on the base region in register with said further opening and in contrast with the base region via that opening; heating structure to provide an oxide film on the polysilicon emitter body; implanting boron ions via said first openings, the oxide on the emitter body providing an implantation mask whereby to define, in said first opening, p + -type base contact regions aligned with the polysilicon emitter body, and whereby to inhibit implantation of ions into the emitter body; implanting arsenic ions via said second opening to form an n + -type collector contact; heating the structure to drive in the implanted base contact regions and collector contact; and applying metal contacts to the collector contact, the base contact regions and to the polysilicon emitter body.

Claim 4

A method of fabricating a bipolar polysilicon emitter transistor in a doped well in a single crystal silicon substrate, the method including the steps of: implanting phosphorus ions into a well region at an energy of about 100 KeV and a dose of about 7.7×10 12 /cm 2 ; heating the substrate to a temperature of about 1175° C. to drive in the dopant; implanting boron ions into said well region at an energy of about 160 KeV and a dose of about 2.8×10 12 /cm 2 ; further heating the substrate to a temperature of about 1175° C. to drive in the boron dopant and to effect compensation between the phosphorus and boron dopants providing a peak dopant concentration of 4.5×10 15 cm -3 to 4.5.×10 16 cm -3 at a depth of 2 to 5 microns below the substrate surface; providing a field oxide pattern having first and second openings over said doped well; providing a thin oxide layer in said first and second openings; impanting boron ions into said doped well via said first opening to define a p-type base layer; providing a further opening a said field oxide over a central region of said base layer, said central region ultimately becoming a base region of the transistors; providing a polysilicon emitter body on the base region in register with said further opening and in contrast with the base region via that opening; heating structure to provide an oxide film on the polysilicon emitter body; implanting boron ions via said first openings, the oxide on the emitter body providing an implantation mask whereby to define, in said first opening, p + -type base contact regions aligned with the polysilicon emitter body, and whereby to inhibit implantation of ions into the emitter body; implanting arsenic ions via said second opening to form an n + -type collector contact; heating the structure to drive in the implanted base contact regions and collector contact; and applying metal contacts to the collector contact, the base contact regions and to the polysilicon emitter body.