US4873069A — Method for the preparation of silicon carbide whi…

Claim 1

Independent Claim 168 words

A method for producing a high yield of silicon carbide whiskers having diameters of about 0.5 to about 10 micrometers and lengths of about 10 to about 1000 micrometers, which comprises: preparing a mixture of silicon dioxide particles and carbon fibers, said silicon dioxide particles having an average diameter of about 5 to 15 millimicrons and an average surface area of about 200 to 400 square meters per gram, said silicon dioxide particles being about 1.5 to about 2.75 times, by weight, said carbon fibers and said silicon dioxide having a void volume of about 40 percent to about 98 percent; heating said mixture to a temperature of about 1600° to 1900° C. in a furnace for a time at least about 0.2 hours, followed by cooling to room temperature; and maintaining gaseous reaction products of reactions between said silicon dioxide and said carbon fibers at the surface of said mixture at a steady state condition during said heating by flowing a substantially inert gas through said furnace.

Claim 2

Independent Claim 168 words

A method for producing a high yield of silicon carbide whiskers having diameters of about 0.5 to about 10 micrometers and lengths of about 10 to about 1000 micrometers, which comprises: preparing a mixture of silicon dioxide particles and carbon fibers, said silicon dioxide particles having an average diameter of about 5 to 15 millimicrons and an average surface area of about 200 to 400 square meters per gram, said silicon dioxide particles being about 1.5 to about 2.75 times, by weight, said carbon fibers and said silicon dioxide having a void volume of about 40 percent to about 98 percent; heating said mixture to a temperature of about 1600° to 1900° C. in a furnace for a time at least about 0.2 hours, followed by cooling to room temperature; and maintaining gaseous reaction products of reactions between said silicon dioxide and said carbon fibers at the surface of said mixture at a steady state condition during said heating by flowing a substantially inert gas through said furnace.

Claim 3

Dependent Claim 45 words

The method of claim 1 further comprising mixing a catalyst with said silicon carbide particles and said carbon fibers prior to said heating, said catalyst being about 3 to 10 percent by weight based upon the combined weight of said silicon dioxide and carbon fibers.

Claim 4

Dependent Claim 45 words

The method of claim 2 wherein said mixture comprises ten parts by weight said silicon dioxide powder, five parts by weight said carbon fibers, and one part said catalyst; and wherein said heating is carried out at about 1600°-1900° C. for 0.2 to 2 hours.

Claim 5

Dependent Claim 28 words

The method of claim 2 wherein said catalyst is selected from the group consisting of aluminum metal and decomposable compounds of boron, aluminum, and lanthanum and mixtures thereof.

Claim 6

Dependent Claim 13 words

The method of claim 1 wherein said carbon fibers are carbonized cotton fibers.

Claim 7

Dependent Claim 15 words

The method of claim 1 wherein said inert gas is selected from argon and helium.

Claim 8

Dependent Claim 11 words

The method of claim 6 wherein said inert gas is argon.

Claim 9

Independent Claim 176 words

A method of producing a high yield of beta silicon carbide whiskers having diameters of about 0.5 to about 5 micrometers and lengths of about 10 to about 100 micrometers, which comprises: preparing a mixture of a. 9-11 parts by weight of silicon dioxide particles having an average size of about 5 to 15 millimicrons and a surface area of about 200 to 400 square meters per gram, said silicon dioxide having a void volume of about 40 percent or greater, b. 4-6 parts by weight of carbonized cotton fibers having a void volume of about 40 percent or greater, and c. 0.5 to 1.5 parts by weight of a catalyst selected from aluminum metal, and oxides of boron, aluminum and lanthanum; heating said mixture in a furnace at a temperature of about 1350° to about 1950° C. for 0.5 to 4 hours; and maintaining gaseous products of reactions between said silicon dioxide and carbonized cotton fibers at the surface of said mixture at a steady state with a flow of argon gas through said furnace.

Claim 10

Independent Claim 176 words

A method of producing a high yield of beta silicon carbide whiskers having diameters of about 0.5 to about 5 micrometers and lengths of about 10 to about 100 micrometers, which comprises: preparing a mixture of a. 9-11 parts by weight of silicon dioxide particles having an average size of about 5 to 15 millimicrons and a surface area of about 200 to 400 square meters per gram, said silicon dioxide having a void volume of about 40 percent or greater, b. 4-6 parts by weight of carbonized cotton fibers having a void volume of about 40 percent or greater, and c. 0.5 to 1.5 parts by weight of a catalyst selected from aluminum metal, and oxides of boron, aluminum and lanthanum; heating said mixture in a furnace at a temperature of about 1350° to about 1950° C. for 0.5 to 4 hours; and maintaining gaseous products of reactions between said silicon dioxide and carbonized cotton fibers at the surface of said mixture at a steady state with a flow of argon gas through said furnace.

Claim 11

Dependent Claim 34 words

The method of claim 8 wherein said silicon dioxide particles are produced by the hydrolysis of silicon tetrachloride vapor in a flame of hydrogen and oxygen, and residual hydrogen chloride is removed by calcination.

Claim 12

Dependent Claim 27 words

The method of claim 8 wherein said carbonized cellulose fibers are produced by carbonizing cotton in an inert atmosphere at about 400° C. to about 3000° C.

Claim 13

Dependent Claim 12 words

The method of claim 8 wherein said catalyst is anhydrous boric oxide.

Claim 14

Dependent Claim 19 words

The method of claim 8 wherein said catalyst is a mixture of anhydrous boric oxide and powdered aluminum metal.

Claim 15

Dependent Claim 47 words

The method of claim 8 wherein said mix comprises: ten parts by weight of said silicon dioxide particles; five parts by weight of said carbonized cotton particles; one part by weight of said anhydrous boric oxide; and about 0.2 to 0.35 parts said powdered aluminum metal catalyst.

Claim 16

Independent Claim 222 words

A method of producing a high yield of smooth surface beta silicon carbide whiskers having diameters of about 0.5 to about 10 micrometers and lengths of about 10 to about 1000 micrometers, which comprises: preparing a mixture of a. 9-11 parts by weight of silicon dioxide particles having an average diameter of about 5 to 15 millimicrons and a surface area of about 200 to 400 square meters per gram, said silicon dioxide produced by the hydrolysis of silicon tetrachloride in a flame of hydrogen and oxygen, with residual hydrogen chloride removed by calcination said silicon dioxide having a void volume of about 80-98 percent, b. 4-6 parts by weight of carbonized cotton fibers, said carbonized cotton fibers produced by carbonizing cotton fibers in a hydrogen atmosphere at about 900° C., said carbonized cotton fibers having a void volume of about 80-98 percent, c. 0.1 to 1.5 parts by weight of anhydrous boric oxide as a catalyst, and d. 0.2 to 0.35 parts by weight of aluminum metal powder as a further catalyst, heating said mixture in a furnace at a temperature of about 1350° to 1950° C. for about 0.5 to 4 hours; and maintaining gaseous products of reactions between said silicon dioxide and said carbonized cotton fibers on the surface of said mixture with a flowing stream of argon gas.

Claim 17

Independent Claim 222 words

A method of producing a high yield of smooth surface beta silicon carbide whiskers having diameters of about 0.5 to about 10 micrometers and lengths of about 10 to about 1000 micrometers, which comprises: preparing a mixture of a. 9-11 parts by weight of silicon dioxide particles having an average diameter of about 5 to 15 millimicrons and a surface area of about 200 to 400 square meters per gram, said silicon dioxide produced by the hydrolysis of silicon tetrachloride in a flame of hydrogen and oxygen, with residual hydrogen chloride removed by calcination said silicon dioxide having a void volume of about 80-98 percent, b. 4-6 parts by weight of carbonized cotton fibers, said carbonized cotton fibers produced by carbonizing cotton fibers in a hydrogen atmosphere at about 900° C., said carbonized cotton fibers having a void volume of about 80-98 percent, c. 0.1 to 1.5 parts by weight of anhydrous boric oxide as a catalyst, and d. 0.2 to 0.35 parts by weight of aluminum metal powder as a further catalyst, heating said mixture in a furnace at a temperature of about 1350° to 1950° C. for about 0.5 to 4 hours; and maintaining gaseous products of reactions between said silicon dioxide and said carbonized cotton fibers on the surface of said mixture with a flowing stream of argon gas.

Claim 18

Dependent Claim 46 words

The method of claim 14 wherein said mix comprises: ten parts by weight of said silicon dioxide particles; five parts by weight of said carbonized cotton fibers; one part by weight of said boric oxide catalyst; and 0.25 part by weight of said powdered aluminum metal.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1992-10-09	1993-04-10	1993-10-10	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1996-10-09	1997-04-10	1997-10-10	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2000-10-09	2001-04-10	2001-10-10	$7700.00	Window Closed / Lapsed

Method for the preparation of silicon carbide whiskers

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag