Production of SiC whiskers
Assignee: GREAT LAKES CARBON Corp
•
Filing: 1980-01-28
•
Granted: 1981-08-11
•
Expires: 2000-01-28
Abstract
Abstract Silicon carbide whiskers useful for reinforcement of metals are manufactured from SiO2 and carbon. Rice hulls are ashed in air at approximately 620 DEG C. to obtain amorphous SiO2, which is then blended with fine particle size carbon. The mixture is rapidly heated under CO atmosphere to 1500 DEG C., and when the temperature reaches that point the CO atmosphere is flushed with argon, the SiC whiskers forming in the argon atmosphere. The product is purified by ashing in air to remove excess carbon and/or washed with HF to remove unreacted SiO2.
Inventors
- 👤 Ottis J. Horne, Jr.
- 👤 David E. Ramsey, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 15:30
CPC Classifications
C; C30; C30B; C30B29/00; C30B29/10; C30B29/36; C01; C01B; C01B32/00; C01B32/90; C01B32/914; C01B32/956; C01B32/963; C01B32/97; C30B25/00; C30B25/005; C01P; C01P2004/00; C01P2004/10
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
134 words
A process for the manufacture of β-silicon carbide whiskers of about 0.5 to 1.5μ in diameter and 10 to 50μ length comprising the steps of: (1) Ashing rice hulls in air at 400° to 700° C. to obtain amorphous SiO 2 ; (2) Mixing finely powdered carbonaceous powder selected from the group consisting of the carbonized residue from heating rice hulls in nitrogen at temperatures between 400° and 700° C. and calcined petroleum coke with the SiO 2 obtained in Step 1; (3) Heating the above mixture in CO at 1 atmosphere pressure; (4) When the above mixture reaches a carbide-forming temperature within the range of 1400° to 1600° C., flushing the container rapidly with an inert gas; and (5) Maintaining a flow of inert gas for a time sufficient to form SiC whiskers.
Claim 2
Dependent Claim
134 words
A process for the manufacture of β-silicon carbide whiskers of about 0.5 to 1.5μ in diameter and 10 to 50μ length comprising the steps of: (1) Ashing rice hulls in air at 400° to 700° C. to obtain amorphous SiO 2 ; (2) Mixing finely powdered carbonaceous powder selected from the group consisting of the carbonized residue from heating rice hulls in nitrogen at temperatures between 400° and 700° C. and calcined petroleum coke with the SiO 2 obtained in Step 1; (3) Heating the above mixture in CO at 1 atmosphere pressure; (4) When the above mixture reaches a carbide-forming temperature within the range of 1400° to 1600° C., flushing the container rapidly with an inert gas; and (5) Maintaining a flow of inert gas for a time sufficient to form SiC whiskers.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein the inert gas of step 5 is Ar, or other noble gas.
Claim 4
Dependent Claim
27 words
The process of claim 1 wherein from 10 to 55 parts SiO 2 and 90 to 45 parts carbonaceous powder by weight are mixed in Step 2.
Claim 5
Dependent Claim
31 words
The process of claim 1 wherein from 1 to 30 parts by wt. of Fe 2 O 3 are added to 100 parts of SiO 2 before mixing during step 2.
Claim 6
Dependent Claim
18 words
The process of claim 1 wherein the temperature rise in step 4 is from 100° to 200° C./min.
Claim 7
Dependent Claim
18 words
The process of claim 1 wherein the mixture is placed in a preheated chamber at the carbide-forming temperature.
Claim 8
Dependent Claim
22 words
The process of claim 1 wherein the rice hulls are ashed in step 1 at approximately 620° C. for approximately one hour.
Claim 9
Dependent Claim
21 words
The process of claim 1 wherein the rice hulls are carbonized in nitrogen at approximately 550° C. for approximately one hour.
Claim 10
Dependent Claim
19 words
The process of claim 1 wherein the mixture is held at the carbide-forming temperature from one to four hours.
Claim 11
Dependent Claim
21 words
The process of claim 1 wherein the mixture is held at the carbide-forming temperature, of 1500° C. for approximately two hours.
Claim 12
Dependent Claim
154 words
A process for the production of β-SiC whiskers of 0.5 to 1.5μ diameter and 10 to 50μ in length comprising the steps of: (1) Ashing a portion of rice hulls in air at about 620° C.; (2) Mixing the ash thus obtained with a particulate source of carbon selected from the group consisting of rice hulls carbonized in nitrogen for one hour at about 550° C., and 100 mesh ground calcined petroleum coke, in a ratio of approximately 55% ash to 45% carbon source by wt.; (3) Placing the mixture thus formed in a furnace; (4) Replacing the furnace atmosphere with CO; (5) Heating said mixture to about 1500° C. at a rate of temperature increase of at least 100° C. per minute; (6) Replacing the CO atmosphere with argon when the temperature of said mixture reaches 1500° C.; (7) Maintaining said mixture at 1500° C. in said argon atmosphere for about one hour.
Claim 13
Dependent Claim
154 words
A process for the production of β-SiC whiskers of 0.5 to 1.5μ diameter and 10 to 50μ in length comprising the steps of: (1) Ashing a portion of rice hulls in air at about 620° C.; (2) Mixing the ash thus obtained with a particulate source of carbon selected from the group consisting of rice hulls carbonized in nitrogen for one hour at about 550° C., and 100 mesh ground calcined petroleum coke, in a ratio of approximately 55% ash to 45% carbon source by wt.; (3) Placing the mixture thus formed in a furnace; (4) Replacing the furnace atmosphere with CO; (5) Heating said mixture to about 1500° C. at a rate of temperature increase of at least 100° C. per minute; (6) Replacing the CO atmosphere with argon when the temperature of said mixture reaches 1500° C.; (7) Maintaining said mixture at 1500° C. in said argon atmosphere for about one hour.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-10 | 1985-02-09 | 1985-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-10 | 1989-02-09 | 1989-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-10 | 1993-02-09 | 1993-08-11 | $7700.00 | Window Closed / Lapsed |