Limiting tin sludge formation in tin or tin/lead electroplating solutions
Assignee: Shipley Co Inc
•
Filing: 1988-04-29
•
Granted: 1989-10-03
•
Expires: 2008-04-29
Abstract
Abstract Baths and methods for electroplating tin or tin-lead alloys wherein the formation of tetravalent tin and stannic oxide sludge is reduced or prevented. These baths contain a soluble divalent tin compound, a soluble alkyl or alkylol sulfonic acid at least one wetting agent, and a hydroxyl phenyl compound reducing agent. Other compounds may be added to the bath for improving its performance during electroplating.
Inventors
- 👤 Fred I. Nobel
- 👤 Barnet D. Ostrow
- 👤 David N. Schram
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 05:32
CPC Classifications
C; C25; C25D; C25D3/00; C25D3/02; C25D3/34; C25D3/36; C25D3/30; C25D3/32; C25D3/56; C25D3/60; H; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/3465; H05K3/3473
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
72 words
An electrolyte for limiting the formation of tetravalent tin oxide sludge when electroplating tin or tin-lead alloys therefrom, which electrolyte comprises a soluble divalent tin compound; a soluble alkyl sulfonic acid in an amount sufficient to provide a solution having a pH less than about 3; at least one wetting agent; and resorcinol in an amount sufficient to reduce or prevent the formation of tetravalent tin and stannic oxide sludge when electroplating.
Claim 2
Dependent Claim
72 words
An electrolyte for limiting the formation of tetravalent tin oxide sludge when electroplating tin or tin-lead alloys therefrom, which electrolyte comprises a soluble divalent tin compound; a soluble alkyl sulfonic acid in an amount sufficient to provide a solution having a pH less than about 3; at least one wetting agent; and resorcinol in an amount sufficient to reduce or prevent the formation of tetravalent tin and stannic oxide sludge when electroplating.
Claim 3
Dependent Claim
47 words
The electrolyte of claim 1 wherein the wetting agent is a solution soluble alkylene oxide condensation compound having at least about 8 moles of ethylene oxide, a solution soluble quaternary ammonium-fatty acid compound, a solution soluble amine oxide compound, a solution soluble tertiary amine, or mixtures thereof.
Claim 4
Dependent Claim
9 words
The electrolyte of claim 1 further comprising a brightener.
Claim 5
Dependent Claim
12 words
The electrolyte of claim 3 wherein the brightener is an aromatic aldehyde.
Claim 6
Dependent Claim
11 words
The electrolyte of claim 1 further comprising a soluble bismuth compound.
Claim 7
Dependent Claim
8 words
The electrolyte of claim 1 further comprising acetaldehyde.
Claim 8
Dependent Claim
12 words
The electrolyte of claim 1 further comprising a soluble divalent lead compound.
Claim 9
Dependent Claim
65 words
A method for reducing tetravalent tin and stannic oxide sludge formation in high speed tin or tin-lead electroplating solution, which method comprises electroplating a tin or tin-lead alloy from the electrolyte of claim 1 upon at least a portion of a substrate with agitation, whereby the antioxidant prevents or substantially reduces the oxidation of tin and the formation of stannic oxide sludge in the solution.
Claim 10
Dependent Claim
17 words
The method of claim 8 wherein the electroplating step is carried out a temperature above 95° F.
Claim 11
Independent Claim
107 words
A method for limiting the formation of tetravalent tin sludge in an electrolyte when electroplating tin or tin-lead alloys, which electrolyte comprises a soluble divalent tin compound, methane sulfonic acid in an amount sufficient to provide a solution having a pH less then about 3 and at least one wetting agent; which method comprises: adding a hydroxyphenyl compound comprising hydroquinone, resorcinol, phloroglucinol, pyrogallol, an amino phenol, hydroquinone sulfuric acid ester, or mixtures thereof, in an amount sufficient to reduce or prevent the formation of tetravalent tin and stannic oxide sludge; and electroplating a tin or tin-lead alloy upon a substrate at a temperature above about 95° F.
Claim 12
Independent Claim
107 words
A method for limiting the formation of tetravalent tin sludge in an electrolyte when electroplating tin or tin-lead alloys, which electrolyte comprises a soluble divalent tin compound, methane sulfonic acid in an amount sufficient to provide a solution having a pH less then about 3 and at least one wetting agent; which method comprises: adding a hydroxyphenyl compound comprising hydroquinone, resorcinol, phloroglucinol, pyrogallol, an amino phenol, hydroquinone sulfuric acid ester, or mixtures thereof, in an amount sufficient to reduce or prevent the formation of tetravalent tin and stannic oxide sludge; and electroplating a tin or tin-lead alloy upon a substrate at a temperature above about 95° F.
Claim 13
Dependent Claim
27 words
The method of claim 10 wherein the amount of hydroxyphenyl compound ranges from about 1 to 20 g/l and the eletroplating step is carried out with agitation.
Claim 14
Dependent Claim
29 words
The method of claim 10 which further comprises adding an amount of a solution soluble divalent lead compound to the electrolyte to obtain a tin-lead alloy deposit when electroplating.
Claim 15
Dependent Claim
17 words
The method of claim 10 which further comprises agitating the solution or substrate during the electroplating step.
Claim 16
Dependent Claim
48 words
The method of claim 10 wherein the wetting agent comprises a solution soluble alkylene oxide condensate compound having at least 8 moles of ethylene oxide, a solution soluble quaternary ammonium fatty acid compound, a solution soluble amine oxide compound, a solution soluble tertiary amine compound, or mixtures thereof.
Claim 17
Dependent Claim
24 words
The method of claim 10 which further comprises increasing the brightness of the resulting electrodeposit by adding a sufficient amount of an aromatic aldehyde.
Claim 18
Dependent Claim
29 words
The method of claim 10 which further comprises increasing the low current density electroplating characteristics of the electrolyte by adding a sufficient amount of a solution soluble bismuth compound.
Claim 19
Dependent Claim
25 words
The method of claim 10 which further comprises increasing the high current density electroplating characteristics of the electrolyte by adding a sufficient amount of acetaldehyde.
Claim 20
Dependent Claim
37 words
The method of claim 10 wherein the setting agent comprises an alkylene oxide condensate compound having at least about 8 moles of ethylene oxide to impart a cloud point of above about 90° F. to the electrolyte.
Claim 21
Dependent Claim
27 words
The method of claim 18 which further comprises increasing the throwing power of the electrolyte by adding a sufficient amount of solution soluble quaternary ammonium-fatty acid compound.
Claim 22
Dependent Claim
27 words
The method of claim 18 which further comprises increasing the throwing power of the electrolyte by adding a sufficient amount of a solution soluble amine oxide compound.
Claim 23
Dependent Claim
27 words
The method of claim 18 which further comprises increasing the throwing power of the electrolyte by adding a sufficient amount of a solution soluble tertiary amine compound.
References Cited (Backward Citations)
DE122265C
Cited
GB555929A
Cited
US2525942A
Cited
US2460252A
Cited
US3082157A
Cited
GB1151460A
Cited
US3663384A
Cited
US3769182A
Cited
US3785939A
Cited
US3905878A
Cited
US3730853A
Cited
US3749649A
Cited
US4000047A
Cited
US4118289A
Cited
US3875029A
Cited
US4132610A
Cited
US4072582A
Cited
US4135991A
Cited
US4388158A
Cited
US4384930A
Cited
US4599149A
Cited
US4459185A
Cited
US4582756A
Cited
US4565610A
Cited
US4565609A
Cited
US4617097A
Cited
US4662999A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-02 | 1993-04-03 | 1993-10-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-02 | 1997-04-03 | 1997-10-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-02 | 2001-04-03 | 2001-10-03 | $7700.00 | Window Closed / Lapsed |