US4870033A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of manufacturing a multilayer electrode containing silicide for a semiconductor device
Assignee: Yamaha Corp
•
Filing: 1987-03-03
•
Granted: 1989-09-26
•
Expires: 2007-03-03
Abstract
Abstract An electrode using Ti or Zr having a highly reactive property but insuring a good and stable electric contact with a silicon semiconductor device surrounded by an oxygen atom-containing insulating film is realized with simplified and reduced manufacturing steps at a reduced cost by first revealing a selective surface region of the silicon semiconductor through a window, and then laminating thereon including the selective surface region a first metal layer of Ti or Zr and then a second metal layer of Mo or W to cover and protect the first metal layer from oxidation, and then etching away the laminated layers leaving that portion corresponding to the selective surface region of the device, and thereafter heating the assembly to form a silicide of the first metal with silicon of the underlying semiconductor. The upper metal layer is covered with a protective insulating layer to avoid oxidation of the upper metal layer. The step of covering with the protective insulating layer should preferably be taken before the heat-treatment for the silicide formation.
Inventors
- 👤 Tadahiko Hotta
- 👤 Osamu Hanagasaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:51
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
244 words
A method of manufacturing a two metal layer electrode for a semiconductor device having a selective surface region including a material selected from the group consisting of single crystal silicon and polycrystal silicon and intended for producing an electric contact with an overlying layer of metal and being surrounded by an insulating film containing oxygen atoms, comprising sequentially: a window-forming step to reveal said electric contact producing selective surface region of said semiconductor device at a predetermined surface site thereof by forming a window through said oxygen atom-containing insulating film; a laminated layers-forming step to deposit sequentially a first layer of metal and thereon an upper layer of metal onto said device surface that said upper layer of metal has an exposed portion for contact with said overlying layer of metal; a patterning step to etch away selected portions of the laminated layers of metal and to leave a portion thereof at a location corresponding to at least said selective surface region; an insulating layer-forming step to deposit an insulating layer to cover the upper surface of said upper layer of metal, side edges of said first and upper layers of patterned metal and the insulating film containing oxygen; and a heat-treating step to subject the resulting assembly to a heat-treatment to cause reaction between said first layer and silicon contained in said selective surface region underlying said first layer of metal to thereby form a silicide of the metal of said first layer.
Claim 2
Independent Claim
244 words
A method of manufacturing a two metal layer electrode for a semiconductor device having a selective surface region including a material selected from the group consisting of single crystal silicon and polycrystal silicon and intended for producing an electric contact with an overlying layer of metal and being surrounded by an insulating film containing oxygen atoms, comprising sequentially: a window-forming step to reveal said electric contact producing selective surface region of said semiconductor device at a predetermined surface site thereof by forming a window through said oxygen atom-containing insulating film; a laminated layers-forming step to deposit sequentially a first layer of metal and thereon an upper layer of metal onto said device surface that said upper layer of metal has an exposed portion for contact with said overlying layer of metal; a patterning step to etch away selected portions of the laminated layers of metal and to leave a portion thereof at a location corresponding to at least said selective surface region; an insulating layer-forming step to deposit an insulating layer to cover the upper surface of said upper layer of metal, side edges of said first and upper layers of patterned metal and the insulating film containing oxygen; and a heat-treating step to subject the resulting assembly to a heat-treatment to cause reaction between said first layer and silicon contained in said selective surface region underlying said first layer of metal to thereby form a silicide of the metal of said first layer.
Claim 3
Dependent Claim
50 words
A method according to claim 1, in which: the metal of said first layer is an element chemically reactive with the oxygen atoms contained in said insulating film; and the metal of said upper layer has a melting point higher than the temperature of said heat-treatment for forming a silicide.
Claim 4
Dependent Claim
61 words
A method according to claim 1, in which: the material constituting said first layer of metal is comprised of a member selected from the group consisting of Ti and Zr as its principal component; and the material of said upper layer of metal is composed of a member selected from the group consisting of Mo and W as its principal component.
Claim 5
Dependent Claim
41 words
A method according to claim 1, in which: the metal of said first layer is selected from the group consisting of Ti and Zr; and the metal of said upper layer is selected from the group consisting of Mo and W.
Claim 6
Dependent Claim
81 words
A method according to claim 1, further comprising: a step of forming a contact hole through said insulating layer covering said portion of laminated layers of metal and said insulating film to reveal a portion of said upper layer of metal; and a step of forming a wiring layer connected to said portion of said upper layer of metal revealed through said contact hole, said wiring layer having a different shape than the previously etched first and upper layers of metal.
Claim 7
Dependent Claim
43 words
A method according to claim 1, in which: said insulating layer covering the retained laminated layers of metal is comprised of a member selected from the group consisting of Al 2 O 3 , and SiO 2 and Si 3 N 4 .
Claim 8
Dependent Claim
28 words
A method according to claim 6, in which: said insulating layer covering the retained laminated layers of metal is obtained by depressed CVD technique or plasma CVD technique.
Claim 9
Dependent Claim
19 words
A method according to claim 1, in which: said insulating film containing oxygen is made of SiO 2 .
References Cited (Backward Citations)
US3465211A
Cited
JPS54149465A
Cited
US4228212A
Cited
GB2077993A
Cited
JPS58143570A
Cited
US4545116A
Cited
US4777150A
Cited
US4585515A
Cited
US4800177A
Cited
US4751198A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-25 | 1993-03-27 | 1993-09-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-25 | 1997-03-27 | 1997-09-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-25 | 2001-03-27 | 2001-09-26 | $7700.00 | Window Closed / Lapsed |