Nonwoven continuously-bonded trilaminate
Assignee: Kimberly Clark Worldwide Inc
•
Filing: 1988-11-18
•
Granted: 1989-09-05
•
Expires: 2008-11-18
Abstract
Abstract A nonwoven composite material comprising a meltblown fabric layer of a thermoplastic polymer sandwiched between two prebonded, spunbonded reinforcing fabric layers of a thermoplastic polymer, all continuously-bonded together to form a composite material. The preferred thermoplastic polymer for both the meltblown and spunbonded layers is polypropylene. The nonwoven composite material contains a minimal number of loose fibers, is highly resistant to the penetration of liquids and would also be expected to exhibit good abrasion resistance, while maintaining tear resistance and softness comparable to non-prebonded materials characterized by discrete bonding patterns. The nonwoven composite material is especially useful as a sterilization wrap for surgical and other health care items.
Inventors
- 👤 Mark H. S. Berman
- 👤 Dilip D. Doshi
- 👤 Thomas F. Gilmore
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 14:25
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; A; A61; A61L; A61L2/00; A61L2/26; B32B5/02; B32B5/022; D; D04; D04H; D04H1/00; D04H1/40; D04H1/54; D04H1/559; D04H1/56; D04H3/00; D04H3/08; D04H3/14; A61B; A61B46/00; B32B2262/00; B32B2262/02; B32B2262/0253; B32B2305/00; B32B2305/08; B32B2307/00; B32B2307/50; B32B2307/582; B32B2437/00; B32B2439/00; B32B2439/80; Y; Y10; Y10S; Y10S428/00; Y10S428/903; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24992
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
159 words
A nonwoven composite material having a basis weight ranging from 1-3 oz/yd 2 , suitable for use as a sterilization wrap, comprising: a layer of a meltblown fabric of thermoplastic polymeric microfibers having an average fiber diameter of up to 10 microns and a basis weight ranging from 0.3 to 0.6 oz/yd 2 ; two prebonded reinforcing fabric layers of thermoplastic polymer filaments selected from spunbonded, wetlaid and carded webs and having basis weights that may be identical or different and range from 0.3 to 2.0 oz/yd 2 ; wherein said meltblown fabric layer and said reinforcing fabric layers are positioned in juxtaposed surface-to surface relationship, said meltblown fabric layer positioned between said reinforcing fabric layers, and wherein all of said layers are continuously-bonded together in a nip of double helical grooved rolls by the application of heat and pressure to form a composite material having areas of heavy bonding, areas of intermediate bonding and areas of light bonding.
Claim 2
Dependent Claim
159 words
A nonwoven composite material having a basis weight ranging from 1-3 oz/yd 2 , suitable for use as a sterilization wrap, comprising: a layer of a meltblown fabric of thermoplastic polymeric microfibers having an average fiber diameter of up to 10 microns and a basis weight ranging from 0.3 to 0.6 oz/yd 2 ; two prebonded reinforcing fabric layers of thermoplastic polymer filaments selected from spunbonded, wetlaid and carded webs and having basis weights that may be identical or different and range from 0.3 to 2.0 oz/yd 2 ; wherein said meltblown fabric layer and said reinforcing fabric layers are positioned in juxtaposed surface-to surface relationship, said meltblown fabric layer positioned between said reinforcing fabric layers, and wherein all of said layers are continuously-bonded together in a nip of double helical grooved rolls by the application of heat and pressure to form a composite material having areas of heavy bonding, areas of intermediate bonding and areas of light bonding.
Claim 3
Dependent Claim
41 words
The nonwoven composite material of claim 1, wherein said thermoplastic polymeric microfibers used to form the meltblown fabric are selected from polypropylene, nylon 6, nylon 6,6, polybutylene terephthalate, polyethylene, polyethylene terephthalate, linear low density polyethylene, and copolymers, composites and blends thereof.
Claim 4
Dependent Claim
14 words
The nonwoven composite material of claim 2, wherein said thermoplastic polymeric microfibers are polypropylene.
Claim 5
Dependent Claim
42 words
The nonwoven composite material of claim 1, wherein said thermoplastic polymer filaments used to form the reinforcing fabric layers are selected from polypropylene, nylon 6, nylon 6,6, polybutylene terephthalate, polyethylene, polyethylene terephthalate, linear low density polyethylene, and copolymers, composites and blends thereof.
Claim 6
Dependent Claim
14 words
The nonwoven composite material of claim 4, wherein said thermoplastic polymer filaments are polypropylene.
Claim 7
Dependent Claim
18 words
The nonwoven composite material of claim 1, wherein said reinforcing fabric layers of thermoplastic polymer filaments are spunbonded.
Claim 8
Dependent Claim
28 words
The nonwoven composite material of claim 6, wherein said thermoplastic polymer filaments used to make the reinforcing fabric layers have an average filament diameter greater than 12 microns.
Claim 9
Dependent Claim
21 words
The nonwoven composite material of claim 7, wherein said filaments have an average filament diameter ranging between 12 and 55 microns.
Claim 10
Dependent Claim
28 words
The nonwoven composite material of claim 6, wherein the ratio of the meltblown fabric layer to the spunbonded reinforcing fabric layers ranges from 0.075:1 to 1:1 by weight.
Claim 11
Dependent Claim
21 words
The nonwoven composite material of claim 9, wherein said ratio of meltblown layer to spunbonded layers ranges from 0.2:1 to 0.7:1.
References Cited (Backward Citations)
US3542634A
Cited
US4039711A
Cited
US3788936A
Cited
US4041203A
Cited
US4196245A
Cited
US4374888A
Cited
US4436780A
Cited
US4493868A
Cited
US4508113A
Cited
US4555811A
Cited
US4766029A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-04 | 1993-03-06 | 1993-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-04 | 1997-03-06 | 1997-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-04 | 2001-03-06 | 2001-09-05 | $7700.00 | Window Closed / Lapsed |