Semi-permeable nonwoven laminate
Assignee: Kimberly Clark Worldwide Inc
•
Filing: 1987-01-23
•
Granted: 1988-08-23
•
Expires: 2007-01-23
Abstract
Abstract A house wrap consists of a three-layer, semi-permeable, nonwoven laminate. The two exterior layers are spun-bond polypropylene having a melt flow of 35 grams per ten minutes at 230 DEG C. The interior layer is a two-component melt-blown layer of polyethylene and polypropylene. The polypropylene has a melt flow of 260 and the polyethylene has a melt flow of 350. The laminate is calendered after formation so that the polyethylene melts and flows to close up the interstitial space and to bond the layers together to create a strong semi-permeable laminate.
Inventors
- 👤 Robert J. Brock
- 👤 William Conn
- 👤 James M. Weber
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:27
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/02; B32B5/08; B32B5/22; B32B5/24; B32B5/26; B32B5/022; D; D04; D04H; D04H1/00; D04H1/40; D04H1/54; D04H1/559; D04H1/56; D04H3/00; D04H3/08; D04H3/14; D04H5/00; D04H5/06; B32B2262/00; B32B2262/02; B32B2262/0253; B32B2305/00; B32B2305/10; B32B2305/20; B32B2307/00; B32B2307/70; B32B2307/726; B32B2432/00; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2929; Y10T428/2931; Y10T442/00; Y10T442/60; Y10T442/608; Y10T442/614; Y10T442/659; Y10T442/66; Y10T442/673
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
153 words
A semi-permeable laminate comprising: (a) an interior layer comprising: (i) an array of randomly dispersed microfibers formed from a fiber forming polymer having a melt flow; and (ii) an interstitial mass, between and among the microfibers, closing up interstitial spaces, formed from a binder-filler polymer having a melt flow, wherein the melt flow of the fiber forming polymer is at least about 80 grams per ten minutes at 230° C. less than the melt flow of the binder-filler polymer; and (b) at least one exterior layer bonded to the interior layer by means of of the binder-filler polymer of the interior layer, the exterior layer comprising an array of randomly laid, continuous filaments formed from a filament forming polymer having a melt flow, wherein the melt flow of the filament forming polymer is at least about 200 grams per ten minutes at 230° C. less than the melt flow of the binder-filler polymer.
Claim 2
Dependent Claim
153 words
A semi-permeable laminate comprising: (a) an interior layer comprising: (i) an array of randomly dispersed microfibers formed from a fiber forming polymer having a melt flow; and (ii) an interstitial mass, between and among the microfibers, closing up interstitial spaces, formed from a binder-filler polymer having a melt flow, wherein the melt flow of the fiber forming polymer is at least about 80 grams per ten minutes at 230° C. less than the melt flow of the binder-filler polymer; and (b) at least one exterior layer bonded to the interior layer by means of of the binder-filler polymer of the interior layer, the exterior layer comprising an array of randomly laid, continuous filaments formed from a filament forming polymer having a melt flow, wherein the melt flow of the filament forming polymer is at least about 200 grams per ten minutes at 230° C. less than the melt flow of the binder-filler polymer.
Claim 3
Dependent Claim
36 words
The laminate of claim 1, wherein the melt flow of the fiber forming polymer is 80-100 grams per ten minutes at 230° C. less than the melt flow of the binder-filler polymer in the interior layer.
Claim 4
Dependent Claim
32 words
The laminate of claim 2, wherein the melt flow of the filament forming polymer is 200-315 grams per 10 minutes at 230° C. less than the melt flow of the binder-filler polymer.
Claim 5
Dependent Claim
25 words
The laminate of claim 2 or 3 wherein the fiber forming polymer and the filament forming polymer are polypropylene and the binder-filler polymer is polyethylene.
Claim 6
Independent Claim
167 words
A method for forming a semi-permeable nonwoven laminate comprising the steps of: (a) depositing an exterior layer of randomly-laid, continuous filaments of filament forming polymer having a melt flow; (b) subsequently depositing an interior layer of randomly-dispersed microfibers onto the exterior layer, the microfibers formed by melt-blowing the fibers from a mixture of a fiber forming polymer having a melt flow and a filler-binder polymer having a melt flow wherein the melt flow of the filament forming polymer is at least 200 grams per ten minutes at 230° C. less than and the melt flow of the fiber-forming polymer is at least about 80 grams per ten minutes at 230° C. less than the melt flow of the filler-binder polymer; and (c) hot calendering the layers together at a temperature, pressure, and speed that causes remelting and flowing of the filler-binder polymer closing up interstitial spaces between fibers and interbonding the layers but does not cause remelting of the filament forming polymer and the fiber forming polymer.
Claim 7
Independent Claim
167 words
A method for forming a semi-permeable nonwoven laminate comprising the steps of: (a) depositing an exterior layer of randomly-laid, continuous filaments of filament forming polymer having a melt flow; (b) subsequently depositing an interior layer of randomly-dispersed microfibers onto the exterior layer, the microfibers formed by melt-blowing the fibers from a mixture of a fiber forming polymer having a melt flow and a filler-binder polymer having a melt flow wherein the melt flow of the filament forming polymer is at least 200 grams per ten minutes at 230° C. less than and the melt flow of the fiber-forming polymer is at least about 80 grams per ten minutes at 230° C. less than the melt flow of the filler-binder polymer; and (c) hot calendering the layers together at a temperature, pressure, and speed that causes remelting and flowing of the filler-binder polymer closing up interstitial spaces between fibers and interbonding the layers but does not cause remelting of the filament forming polymer and the fiber forming polymer.
Claim 8
Dependent Claim
32 words
The method of claim 5 wherein the melt flow of the fiber forming polymer is 80-100 grams per ten minutes at 230° C. less than the melt flow of the binder-filler polymer.
Claim 9
Dependent Claim
32 words
The method of claim 6, wherein the melt flow of the filament forming polymer is 200-315 grams per ten minutes at 230° C. less than the melt flow of the binder-filler polymer.
Claim 10
Dependent Claim
25 words
The method of claim 6 or 7 wherein the fiber forming polymer and the filament forming polymer are polypropylene and the binder-filler polymer is polyethylene.
Claim 11
Dependent Claim
47 words
The method of claim 5, wherein the calender temperature is between 260° F. and 290° F., the calender pressure is between 167.5 pounds per lineal inch and 342.9 pounds per lineal inch, and the calender speed is between 12 feet per minute and 24 feet per minute.
Claim 12
Dependent Claim
32 words
The method of claim 9, wherein the melt flow of the fiber forming polymer is 80-100 grams per ten minutes at 230° C. less than the melt flow of the binder-filler polymer.
Claim 13
Dependent Claim
32 words
The method of claim 10, wherein the melt flow of the filament forming polymer is 200-315 grams per ten minutes at 230° C. less than the melt flow of the binder-filler polymer.
Claim 14
Dependent Claim
25 words
The method of claim 10 or 11, wherein the fiber forming polymer and the filament forming polymer are polypropylene and the binder-filler polymer is polyethylene.
References Cited (Backward Citations)
US3509009A
Cited
US3639195A
Cited
US3841953A
Cited
US3914497A
Cited
US4323626A
Cited
US4384098A
Cited
US4555811A
Cited
US4632861A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-23 | 1992-02-22 | 1992-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-23 | 1996-02-22 | 1996-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-23 | 2000-02-22 | 2000-08-23 | $7700.00 | Window Closed / Lapsed |