Process for preparing nodular pigmentary titanium dioxide

Claim 2

A process for preparing nodular titanium dioxide pigment comprising digesting in hydrochloric acid a mixture of a titanium dioxide-bearing material and an alkali metal compound, said digestion including heating the mixture at a rate and temperature sufficient to form a nodular-shaped material and refluxing said mixture; and calcining the digested material.

Claim 3

The process of claim 1 wherein the titanium dioxide-bearing material is selected from the group consisting of sorelslag, beneficiated ilmenite and chloride slag.

Claim 4

The process of claim 1 wherein the titanium dioxide-bearing material is a sorelslag.

Claim 5

The process of claim 1 wherein the alkali metal compound is selected from a group consisting of an alkali metal hydroxide, an alkali metal carbonate or an alkali metal oxide.

Claim 6

The process of claim 1 wherein the alkali metal hydroxide is sodium hydroxide.

Claim 7

The process of claim 1 wherein the mixture is heated up to its boiling point temperature.

Claim 8

The process of claim 1 wherein the mixture is heated up to its boiling point temperature at a rate of from about 2° C./minute to about 5° C./minute.

Claim 9

A process for preparing nodular titanium dioxide pigment comprising the steps of: (a) mixing a titanium dioxide-bearing material with an alkali metal compound said titanium-bearing material characterized in that it is at a size sufficient for substantially all of the material to react with the alkali metal compound; (b) roasting the mixture; (c) mixing a hydrochloric acid to the roasted mixture; (d) heating the roasted material/acid mixture to its boiling point at a rate sufficient to form a nodular-shaped material; and (e) refluxing the material of step (d); and (f) calcining the material of step (e).

Claim 10

A process for preparing nodular titanium dioxide pigment comprising the steps of: (a) mixing a titanium dioxide-bearing material with an alkali metal compound said titanium-bearing material characterized in that it is at a size sufficient for substantially all of the material to react with the alkali metal compound; (b) roasting the mixture; (c) mixing a hydrochloric acid to the roasted mixture; (d) heating the roasted material/acid mixture to its boiling point at a rate sufficient to form a nodular-shaped material; and (e) refluxing the material of step (d); and (f) calcining the material of step (e).

Claim 11

The process of claim 8 wherein the alkali metal compound is selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate or an alkali metal oxide.

Claim 12

A process for preparing nodular titanium dioxide pigment comprising the steps of: (a) comminuting a titanium dioxide-bearing material to a size sufficient for substantially all the material to react with an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate, and an alkali metal oxide; (b) mixing the titanium dioxide-bearing material with an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate, and an alkali metal oxide; (c) roasting the mixture; (d) mixing the roasted mixture with hydrochloric acid; (e) heating the mixture of (d) to its boiling point at a rate sufficient to form a nodular-shaped solid product in the acid; (f) refluxing the material of step (e); and (g) calcining at least the solid product to form a nodular-shaped titanium dioxide pigment.

Claim 13

A process for preparing nodular titanium dioxide pigment comprising the steps of: (a) comminuting a titanium dioxide-bearing material to a size sufficient for substantially all the material to react with an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate, and an alkali metal oxide; (b) mixing the titanium dioxide-bearing material with an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate, and an alkali metal oxide; (c) roasting the mixture; (d) mixing the roasted mixture with hydrochloric acid; (e) heating the mixture of (d) to its boiling point at a rate sufficient to form a nodular-shaped solid product in the acid; (f) refluxing the material of step (e); and (g) calcining at least the solid product to form a nodular-shaped titanium dioxide pigment.

Claim 14

The process of claim 10 including further the step of micronizing the calcined product.

Claim 15

The process of claim 11 including further the step of micronizing the calcined product to below about one micron.

Claim 16

The process of claim 10 wherein the acid digestion step (e) and (f) are carried out at least two times.

Claim 17

A process for preparing a nodular pigmentary titanium dioxide comprising the steps of: (a) sandmilling a mixture of a titanium dioxide-bearing material and an alkali metal hydroxide; (b) roasting the mixture; (c) sandmilling the roasted mixture; (d) separating solubilized material from the roasted mixture; (e) mixing the roasted mixture with hydrochloric acid; (f) heating the roasted material/acid mixture to its boiling point at a rate sufficient to form a nodular-shaped solid product in the acid; (g) refluxing the material of step (f); (h) separating the solid product from the acid; (i) washing the solid product; and (j) calcining the solid product to form a nodular-shaped titanium dioxide pigment.

Claim 18

A process for preparing a nodular pigmentary titanium dioxide comprising the steps of: (a) sandmilling a mixture of a titanium dioxide-bearing material and an alkali metal hydroxide; (b) roasting the mixture; (c) sandmilling the roasted mixture; (d) separating solubilized material from the roasted mixture; (e) mixing the roasted mixture with hydrochloric acid; (f) heating the roasted material/acid mixture to its boiling point at a rate sufficient to form a nodular-shaped solid product in the acid; (g) refluxing the material of step (f); (h) separating the solid product from the acid; (i) washing the solid product; and (j) calcining the solid product to form a nodular-shaped titanium dioxide pigment.

Claim 19

The process of claim 14 wherein the titanium dioxide-bearing material is selected from the group consisting of sorelslag, beneficiated ilmenite or chloride slag.

Claim 20

The process of claim 14 wherein the titanium dioxide-bearing material is sorelslag.

Claim 21

The process of claim 14 wherein the alkali metal hydroxide is sodium hydroxide.

Claim 22

The process of claim 14 wherein the acid is mixed with the roasted material at room temperature.

Claim 23

The process of claim 14 including further the step of micronizing the calcined product.

Claim 24

The process of claim 14 including further the step of micronizing the calcined product to below about 1 micron.

Claim 25

The process of claim 14 wherein the digestion step is carried out at least two times.

Claim 26

The process of claim 14 wherein the titanium dioxide-bearing material is sandmilled to an average particle size of about 10 microns or less.

Claim 27

The process of claim 14 wherein step (a), the titanium dioxide-bearing material is mixed with the alkali metal hydroxide in a ratio of about 100:30 to about 100:60.

Claim 28

The process of claim 14 wherein the mixture is roasted at about 700° C. to about 900° C.

Claim 29

The process of claim 14 wherein the roasted mixture is sandmilled in water to solubilize impurities.

Claim 30

The process of claim 14 wherein the impurities are filtered from the roasted mixture.

Claim 31

The process of claim 14 wherein the acid is filtered from the solid product in step (h).

Claim 32

The process of claim 14 wherein the solid product is washed with water in step (i).

Claim 33

A process for preparing a nodular titanium dioxide pigment comprising the steps of: (a) comminuting a titanium dioxide-bearing material selected from the group consisting of sorelslag, beneficiated ilmenite and chloride slag to an average particle size of about 10 microns or less; (b) mixing the titanium dioxide-bearing material with an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate, and an alkali metal oxide; (c) roasting the mixture at about 700° C. to about 900° C.; (d) digesting the roasted material in hydrochloric acid; said digestion including heating the roasted material/acid solution to its boiling point at a rate of at about 90° C. to about 110° C. such that a nodular-shaped solid is formed; and (e) calcining at least the solid product at a temperature ranging from about 800° C. to about 1000° C. to form a titanium dioxide pigment.

Claim 34

A process for preparing a nodular titanium dioxide pigment comprising the steps of: (a) comminuting a titanium dioxide-bearing material selected from the group consisting of sorelslag, beneficiated ilmenite and chloride slag to an average particle size of about 10 microns or less; (b) mixing the titanium dioxide-bearing material with an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate, and an alkali metal oxide; (c) roasting the mixture at about 700° C. to about 900° C.; (d) digesting the roasted material in hydrochloric acid; said digestion including heating the roasted material/acid solution to its boiling point at a rate of at about 90° C. to about 110° C. such that a nodular-shaped solid is formed; and (e) calcining at least the solid product at a temperature ranging from about 800° C. to about 1000° C. to form a titanium dioxide pigment.

Claim 35

A process for preparing a nodular titanium dioxide pigment comprising the steps of: (a) sandmilling a mixture of titanium dioxide-bearing material selected from the group consisting of sorelslag, beneficiated ilmenite and chloride slag, and an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate or an alkali metal oxide in water to an average particle size of about 10 microns or less; (b) roasting the mixture at about 700° C. to about 900° C.; (c) sandmilling the roasted mixture in water; (d) digesting the roasted mixture in hydrochloric acid, said digestion including heating the roasted material/acid solution to its boiling point at a rate sufficient to form nodular solids of titanium dioxide material; and (e) calcining the titanium dioxide material at a temperature ranging from about 800° C. to about 1000° C. to form a titanium dioxide pigment.

Claim 36

A process for preparing a nodular titanium dioxide pigment comprising the steps of: (a) sandmilling a mixture of titanium dioxide-bearing material selected from the group consisting of sorelslag, beneficiated ilmenite and chloride slag, and an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate or an alkali metal oxide in water to an average particle size of about 10 microns or less; (b) roasting the mixture at about 700° C. to about 900° C.; (c) sandmilling the roasted mixture in water; (d) digesting the roasted mixture in hydrochloric acid, said digestion including heating the roasted material/acid solution to its boiling point at a rate sufficient to form nodular solids of titanium dioxide material; and (e) calcining the titanium dioxide material at a temperature ranging from about 800° C. to about 1000° C. to form a titanium dioxide pigment.

Claim 37

The process of claim 29 wherein the digesting is carried out in about 10 to about 120 minutes.

Claim 38

The process of claim 29 wherein the titanium dioxide pigment produced after calcination has a brightness (R∞) of about 80 percent or above.

Claim 39

The process of claim 29 wherein the titanium dioxide pigment produced after calcination has a scattering coefficient (S) of about 2000 cm 2 /g or above.

Claim 40

The process of claim 29 wherein the titanium dioxide pigment produced after calcination has an iron content of less than about 520 ppm.

Claim 41

The process of claim 29 wherein the titanium dioxide-bearing material is comminuted to an average particle size of about 10 microns or less.

Claim 42

The process of claim 29 wherein the titanium dioxide-bearing material is comminuted to an average particle size of about 15 microns or less.

Claim 43

The process of claim 29 wherein the titanium dioxide-bearing material is sandmilled to a maximum particle size of about 10 microns or less.