Titanium diboride-based composite articles with alumina dispersoids, having improved fracture toughness

Claim 2

A densified, hard, abrasion resistant ceramic-based composite article of improved fracture toughness comprising about 5-60 volume percent of one or more first dispersoids selected from the group consisting of alumina whiskers, chopped alumina fibers, and alumina particles uniformly distributed in a matrix of titanium diboride.

Claim 3

An article according to claim 1 wherein the dispersoid is present in an amount of about 5-50 volume percent.

Claim 4

An article according to claim 2 wherein the dispersoid aspect ratio of length to diameter is about 6-200.

Claim 5

A cutting tool comprising an article according to claim 3 wherein the dispersoid aspect ratio is about 15-100.

Claim 6

A wear part comprising an article according to claim 3 wherein the dispersoid aspect ratio is about 100-200.

Claim 7

An article according to claim 1 having a density of at least about 98% of theoretical density.

Claim 8

An article according to claim 1 having a fracture toughness of at least about 2.5 MN/m 3/2 .

Claim 9

An article according to claim 1 further comprising about 5-55 volume percent of one or more other dispersoids selected from the group consisting of whiskers, fibers, and particles of hard refractory carbides, nitrides, and carbonitrides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, and tungsten, and hafnium diboride, tungsten diboride, silicon nitride, alumina, zirconia, and hafnia, and mixtures and solid solutions thereof, the combined percent of all dispersoids not exceeding about 60 volume percent.

Claim 10

A coated article comprising an article according to claim 1 having deposited thereon a hard, wear resistant coating of one or more layers independently selected from the group consisting of the refractory carbides, nitrides, and carbonitrides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, and tungsten, and mixtures and solid solutions thereof, and alumina, zirconia, yttria and hafnia, and mixtures and solid solutions thereof.

Claim 11

A coated article according to claim 9 wherein each layer is about 0.1-20 microns thick, and the total coating thickness does not exceed 20 microns.

Claim 12

An article according to claim 1 wherein the first dispersoids include whiskers, fibers, or particles coated with a refractory material different from the first dispersoid material, the coating thickness being between a monolayer and about 1/3 the diameter of the whiskers, fibers, or particles.

Claim 13

An article according to claim 11 wherein the coating comprises at least one of the refractory carbides, nitrides, or carbonitrides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, or tungsten.

Claim 14

An article according to claim 11 wherein the coating comprises at least one of zirconia, hafnia, or yttria.

Claim 15

A densified, hard, abrasion resistant ceramic-based composite article of improved fracture toughness comprising about 5-60 volume percent of one or more first dispersoids selected from the group consisting of alumina whiskers, chopped alumina fibers, and alumina particles uniformly distributed in a matrix of titanium diboride; and prepared by a process comprising the steps of wet blending in a non-reactive liquid medium a mixture comprising about 95-40 volume percent titanium diboride powder and about 5-60 volume percent of one or more first dispersoids selected from the group consisting of alumina whiskers, chopped alumina fibers, and alumina particles to uniformly disperse the first dispersoids in the powder and liquid medium; drying the mixture to remove the liquid medium; and consolidating the dry mixture to a density of at least about 98% of theoretical density to form the article.

Claim 16

A densified, hard, abrasion resistant ceramic-based composite article of improved fracture toughness comprising about 5-60 volume percent of one or more first dispersoids selected from the group consisting of alumina whiskers, chopped alumina fibers, and alumina particles uniformly distributed in a matrix of titanium diboride; and prepared by a process comprising the steps of wet blending in a non-reactive liquid medium a mixture comprising about 95-40 volume percent titanium diboride powder and about 5-60 volume percent of one or more first dispersoids selected from the group consisting of alumina whiskers, chopped alumina fibers, and alumina particles to uniformly disperse the first dispersoids in the powder and liquid medium; drying the mixture to remove the liquid medium; and consolidating the dry mixture to a density of at least about 98% of theoretical density to form the article.

Claim 17

A process for preparing a densified, hard, abrasion resistant ceramic-based composite article of improved fracture toughness comprising the steps of: wet blending in a non-reactive liquid medium a mixture comprising about 95-40 volume percent titanium diboride powder and about 5-60 volume percent of one or more first dispersoids selected from the group consisting of alumina whiskers, chopped alumina fibers, and alumina particles to uniformly disperse the first dispersoids in the powder and liquid medium; drying the mixture to remove the liquid medium; and consolidating the dry mixture to a density of at least about 98% of theoretical density to form the article.

Claim 18

A process for preparing a densified, hard, abrasion resistant ceramic-based composite article of improved fracture toughness comprising the steps of: wet blending in a non-reactive liquid medium a mixture comprising about 95-40 volume percent titanium diboride powder and about 5-60 volume percent of one or more first dispersoids selected from the group consisting of alumina whiskers, chopped alumina fibers, and alumina particles to uniformly disperse the first dispersoids in the powder and liquid medium; drying the mixture to remove the liquid medium; and consolidating the dry mixture to a density of at least about 98% of theoretical density to form the article.

Claim 19

A process according to claim 15 in which the wet blending step comprises wet blending in a non-reactive medium the mixture further comprising about 5-55 volume percent of other dispersoids selected from the group consisting of whiskers, fibers, and particles of hard refractory carbides, nitrides, and carbonitrides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, and tungsten, and hafnium diboride, tungsten diboride, silicon nitride, zirconia, and hafnia, alumina, the combined percent of all dispersoids not exceeding about 60 volume percent.

Claim 20

A process according to claim 15 further comprising the step of depositing on the densified article a hard, wear resistant coating of one or more layers independently selected from the group consisting of the refractory carbides, nitrides, and carbonitrides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, and tungsten, and mixtures and solid solutions thereof, and alumina, zirconia, hafnia, and yttria and mixtures and solid solutions thereof.

Claim 21

A process according to claim 15 wherein the consolidating step comprises pressing the dry mixture at about 5000 psi and about 1750°-1900° C. for about 0.5-3.0 hr.

Claim 22

A process according to claim 15 wherein the first dispersoids include whiskers, fibers, or particles coated with a refractory material different from the first dispersoid material, the coating thickness being between a monolayer and about 1/3 the diameter of the whiskers, fibers, or particles.

Claim 23

A process according to claim 19 wherein the coating comprises at least one of the refractory carbides, nitrides, or carbonitrides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, or tungsten.

Claim 24

A process according to claim 19 wherein the coating comprises at least one of zirconia, hafnia, or yttria.

Claim 25

A process according to claim 15 further comprising the step before the wet blending step of coating one or more of the first dispersoids with a refractory material different from the first dispersoid material, the coating thickness being between a monolayer and about 1/3 the diameter of the first dispersoid.