Co-fired metal-ceramic package
Assignee: CPS Technologies Corp
•
Filing: 1987-08-13
•
Granted: 1989-08-29
•
Expires: 2007-08-13
Abstract
Abstract Glass-ceramic packages for integrated circuits containing multi-layer, interconnected thick film wiring patterns are obtained by co-sintering a glass-ceramic composite and copper, silver, palladium, gold, based conductors at temperatures not exceeding about 1000 DEG C. The dielectric systems include composites of borosilicate glasses and crystalline fillers which are fabricated by either mixing glass frit and the filler or by a sol-gel coating process. The package is fabricated using a tape specifically designed for clean binder burnout in a reducing atmosphere at low temperatures and also for superior mechanical and thermal properties. Metallization, applied by the thick film screening technique, utilized herein has glass-ceramic bonding agents designed to promote adhesion yet maintain the desired electrical properties and post-processing characteristics.
Inventors
- 👤 Eric A. Barringer
- 👤 Sheldon I. Lieberman
- 👤 Mark S. Schmidt
- 👤 James D. Hodge
- 👤 Richard Waack
- 👤 Donald J. Kelley
- 👤 Brian W. Saxton
- 👤 William C. Gruber
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 03:43
CPC Classifications
C; C03; C03C; C03C14/00; C03C14/004; H; H10; H10W; H10W70/00; H10W70/60; H10W70/67; H10W70/69; H10W70/692; H10W99/00; A; A61; A61B; A61B90/00; A61B90/20; C03C2214/00; C03C2214/04; C03C2214/08; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K1/09; H05K1/092; H05K3/00; H05K3/46; H05K3/4644; H05K3/4673; H05K3/4676; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24926; Y10T428/25; Y10T428/252
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
237 words
A process of making a co-fired ceramic composite package, comprising: (a) preparing a slurry comprising (i) a ceramic fraction composed of particles selected from the group consisting of alumina, spinel, cordierite, mullite, forsterite, quartz, and mixtures thereof, and (ii) a glassy fraction composed of 20-57 wt. % alkaline earth oxides, of which calcium oxide comprises 50-100 wt. % and magnesium oxide comprises 0-50 wt. %, 0-10 wt. % aluminum oxide, 23-40 wt. % silicon dioxide, and 25-40 wt. % boron oxide, and (iii) at least one binder; (b) casting the slurry to form a tape having a solids portion composed of at least 40 wt. % to 60 wt. % ceramic and the remainder essentially the glassy fraction; (c) forming a plurality of via holes at desired positions on the tape; (d) applying conductive formulations to selected areas of the tape, including via holes, the formulations including at least one metal selected from the group consisting of copper, silver, palladium, gold, alloys including any of the foregoing, and mixtures thereof to form a conductive green piece; (e) heating the conductive green piece to a temperature of less than approximately 800° C. and for a sufficient length of time to ensure substantially complete binder burnout; and (f) raising the temperature to a peak temperature of less than approximately 1000° C. for a time sufficient to ensure the piece reaches a density of at least 90% of theoretical density.
Claim 2
Dependent Claim
237 words
A process of making a co-fired ceramic composite package, comprising: (a) preparing a slurry comprising (i) a ceramic fraction composed of particles selected from the group consisting of alumina, spinel, cordierite, mullite, forsterite, quartz, and mixtures thereof, and (ii) a glassy fraction composed of 20-57 wt. % alkaline earth oxides, of which calcium oxide comprises 50-100 wt. % and magnesium oxide comprises 0-50 wt. %, 0-10 wt. % aluminum oxide, 23-40 wt. % silicon dioxide, and 25-40 wt. % boron oxide, and (iii) at least one binder; (b) casting the slurry to form a tape having a solids portion composed of at least 40 wt. % to 60 wt. % ceramic and the remainder essentially the glassy fraction; (c) forming a plurality of via holes at desired positions on the tape; (d) applying conductive formulations to selected areas of the tape, including via holes, the formulations including at least one metal selected from the group consisting of copper, silver, palladium, gold, alloys including any of the foregoing, and mixtures thereof to form a conductive green piece; (e) heating the conductive green piece to a temperature of less than approximately 800° C. and for a sufficient length of time to ensure substantially complete binder burnout; and (f) raising the temperature to a peak temperature of less than approximately 1000° C. for a time sufficient to ensure the piece reaches a density of at least 90% of theoretical density.
Claim 3
Dependent Claim
15 words
A process according to claim 1, wherein step (e) is conducted in a non-oxidizing atmosphere.
Claim 4
Dependent Claim
9 words
A package made by the process of claim 2.
Claim 5
Dependent Claim
15 words
A process according to claim 1 wherein step (f) is conducted in a non-oxidizing atmosphere.
Claim 6
Dependent Claim
9 words
A package made by the process of claim 4.
Claim 7
Dependent Claim
23 words
A process according to claim 1, further comprising prior to step (e) the step of laminating together a plurality of conductive green pieces.
Claim 8
Dependent Claim
9 words
A package made by the process of claim 6.
Claim 9
Dependent Claim
9 words
A package made by the process of claim 1.
Claim 10
Dependent Claim
13 words
The process as defined by claim 1, wherein the ceramic particles are cordierite.
Claim 11
Dependent Claim
18 words
The process as defined by claim 1, wherein the ceramic particles are a mixture of quartz and alumina.
Claim 12
Dependent Claim
18 words
The process as defined by claim 1, wherein the ceramic particles are a mixture of alumina and cordierite.
Claim 13
Dependent Claim
18 words
The process as defined by claim 1, wherein the ceramic particles are a mixture of quartz and cordierite.
Claim 14
Dependent Claim
13 words
The process as defined by claim 1, wherein the conductive metal is copper.
Claim 15
Dependent Claim
16 words
The process as defined in claim 1, wherein the firing is performed in a nitrogen atmosphere.
Claim 16
Dependent Claim
14 words
The process as defined in claim 14, wherein the firing atmosphere also contains hydrogen.
Claim 17
Dependent Claim
14 words
The process as defined by claim 1, wherein the firing is performed in air.
Claim 18
Dependent Claim
13 words
The process as defined by claim 1, wherein the conductive metal is gold.
Claim 19
Dependent Claim
22 words
The process defined by claim 1, wherein the ceramic particles are present in the slurry in an amount of 40-75 wt. %.
Claim 20
Dependent Claim
22 words
The process defined by claim 1, wherein the glassy fraction is present in the slurry in an amount of 25-60 wt. %.
Claim 21
Dependent Claim
35 words
The process defined by claim 1, wherein the binder is a methacrylate polymer, and wherein the slurry further comprises (iv) a solvent and (v) a plasticizer selected from the group consisting of phthalates and adipates.
References Cited (Backward Citations)
US4642148A
Cited
US4621066A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-08-28 | 1993-02-27 | 1993-08-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-08-28 | 1997-02-27 | 1997-08-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-08-28 | 2001-02-27 | 2001-08-29 | $7700.00 | Window Closed / Lapsed |