US4853346A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Ohmic contacts for semiconductor devices and method for forming ohmic contacts
Assignee: International Business Machines Corp
•
Filing: 1987-12-31
•
Granted: 1989-08-01
•
Expires: 2007-12-31
Abstract
Abstract A method for forming an ohmic contact on a GaAs semiconductor material comprising depositing a non-uniform layer of Au onto the surface layer of the semiconductor material, depositing a multi-layer ohmic contact of AuGeNi onto the non-uniform layer and alloying the ohmic contact to the semiconductor material. The non-uniform Au layer may be deposited by backscattering Au during sputter cleaning of the semiconductor surface wherein the electrode is coated with Au. After alloying, the ohmic contact comprises a two layer structure having a high density of large area NiAs(Ge) grains contacting the semiconductor material as the first layer and an AuGa phase as the top layer. The ohmic contact has reduced contact resistance and exhibits a reduction in the spread of contact resistance after high temperature annealing.
Inventors
- 👤 John M. Baker
- 👤 Alessandro C. Callegari
- 👤 Dianne L. Lacey
- 👤 Yih-Cheng Shih
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 22:34
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0116; H10D64/60; H10D64/62; H10D62/00; H10D62/80; H10D62/85
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
64 words
A method of forming an ohmic contact on a semiconductor material containing GaAs comprising the steps of: (a) depositing a non-uniform layer of Au onto one surface of the semiconductor material by sputter cleaning the semiconductor by using an Au-coated rf-electrode; (b) depositing a multi-layer ohmic contact of AuGeNi onto the non-uniform Au layer; and (c) alloying the ohmic contact to the semiconductor material.
Claim 2
Independent Claim
64 words
A method of forming an ohmic contact on a semiconductor material containing GaAs comprising the steps of: (a) depositing a non-uniform layer of Au onto one surface of the semiconductor material by sputter cleaning the semiconductor by using an Au-coated rf-electrode; (b) depositing a multi-layer ohmic contact of AuGeNi onto the non-uniform Au layer; and (c) alloying the ohmic contact to the semiconductor material.
Claim 3
Dependent Claim
19 words
The method of claim 1 wherein the sputter cleaning is performed at a pressure of at least 10 mTorr.
Claim 4
Dependent Claim
20 words
The method of claim 2 wherein the sputter cleaning is performed at a pressure of 20 mTorr utilizing Ar gas.
Claim 5
Dependent Claim
73 words
The method of claim 1 wherein the multi-layer ohmic contact is deposited by: (a) depositing a layer of approximately 50 angstroms of Ni into the non-uniform layer of Au; (b) depositing a layer of approximately 1,000 angstroms of AuGe onto the Ni; (c) depositing a layer of approximately 300 angstroms of Ni onto the AuGe layer; and (d) depositing a layer of between 500 to 1000 angstroms of Au onto the Ni layer.
Claim 6
Dependent Claim
41 words
The method of claim 4 wherein the ohmic contact after alloying comprises a two layer structure having a high density of large area NiAs(Ge) grains contacting the semiconductor material as a first layer and a AuGa phase as a top layer.
Claim 7
Dependent Claim
20 words
The method of claim 5 wherein the large area NiAs(Ge) grains contacting the semiconductor material are approximately 300 nm wide.
Claim 8
Dependent Claim
17 words
The method of claim 1 wherein the sputter cleaning is performed by a d.c. glow discharge process.
Claim 9
Dependent Claim
23 words
The method of claim 1 wherein the alloying step is performed at a temperature in the range between 400° C. to 550° C.
Claim 10
Dependent Claim
39 words
The method of claim 8 further including a step of annealing the semiconductor material subsequent to the alloying step at a temperature in the range between 350° C.-450° C. for a time period between 2 hours to 10 hours.
Claim 11
Dependent Claim
11 words
The method of claim 1 wherein the semiconductor material is GaAlAs.
Claim 12
Independent Claim
74 words
A method of forming an ohmic contact on a semiconductor material containing GaAs comprising the steps of: (a) simultaneously cleaning one surface of the semiconductor material and depositing a non-uniform layer of Au onto the surface of the semiconductor material being cleaned; (b) depositing a multi-layer ohmic contact of Ni/AuGe/Ni/Au onto the surface of the semiconductor material having the non-uniform layer of Au thereon; and (c) alloying the ohmic contact to the semiconductor material.
Claim 13
Independent Claim
74 words
A method of forming an ohmic contact on a semiconductor material containing GaAs comprising the steps of: (a) simultaneously cleaning one surface of the semiconductor material and depositing a non-uniform layer of Au onto the surface of the semiconductor material being cleaned; (b) depositing a multi-layer ohmic contact of Ni/AuGe/Ni/Au onto the surface of the semiconductor material having the non-uniform layer of Au thereon; and (c) alloying the ohmic contact to the semiconductor material.
Claim 14
Dependent Claim
27 words
The method of claim 11 wherein the simultaneous cleaning and depositing of the Au is performed by sputter cleaning the semiconductor material surface utilizing an Au-coated rf-electrode.
Claim 15
Dependent Claim
41 words
The method of claim 12 wherein the ohmic contact after alloying comprises a two layer structure having a high density of large area NiAs(Ge) grains contacting the semiconductor material as a first layer and a AuGa phase as a top layer.
Claim 16
Dependent Claim
20 words
The method of claim 13 wherein the large area NiAs(Ge) grains contacting the semiconductor material are approximately 300 nm wide.
Claim 17
Dependent Claim
29 words
The method of claim 11 wherein the simultaneous cleaning and depositing of the Au is performed by sputter cleaning the semiconductor material and evaporating Au onto the semiconductor material.
Claim 18
Dependent Claim
18 words
The method of claim 15 wherein the sputter cleaning is performed by ion bombardment with an ion gun.
Claim 19
Dependent Claim
17 words
The method of claim 15 wherein the sputter cleaning is performed by a d.c. glow discharge process.
Claim 20
Dependent Claim
41 words
The method of claim 15 wherein the ohmic contact after alloying comprises a two layer structure having a high density of large area NiAs(Ge) grains contacting the semiconductor material as a first layer and a AuGa phase as a top layer.
Claim 21
Dependent Claim
20 words
The method of claim 18 wherein the large area NiAs(Ge) grains contacting the semiconductor material are approximately 300 nm wide.
Claim 22
Dependent Claim
33 words
The method of claim 11 wherein the simultaneous cleaning and depositing of the Au is performed by sputter cleaning the semiconductor material and sputtering Au from a separate target onto the semiconductor material.
Claim 23
Independent Claim
84 words
A method of forming an ohmic contact on a semiconductor material containing GaAs comprising the steps of: (a) sputter cleaning one surface of the semiconductor material; (b) depositing a non-uniform layer of Au on the cleaned semiconductor material surface; (c) depositing a multi-layer ohmic contact of AuGeNi onto the non-uniform Au layer; and (d) alloying the ohmic contact to the semiconductor material thereby forming a two layer contact having a first layer containing a high density of large area grains contacting said semiconductor material.
Claim 24
Independent Claim
84 words
A method of forming an ohmic contact on a semiconductor material containing GaAs comprising the steps of: (a) sputter cleaning one surface of the semiconductor material; (b) depositing a non-uniform layer of Au on the cleaned semiconductor material surface; (c) depositing a multi-layer ohmic contact of AuGeNi onto the non-uniform Au layer; and (d) alloying the ohmic contact to the semiconductor material thereby forming a two layer contact having a first layer containing a high density of large area grains contacting said semiconductor material.
Claim 25
Dependent Claim
74 words
The method of claim 21 wherein the multi-layer ohmic contact is deposited by: (a) depositing a layer of approximately 50 angstroms of Ni onto the non-uniform layer of Au; (b) depositing a layer of approximately 1,000 angstroms of AuGe onto the Ni layer; (c) depositing a layer of approximately 300 angstroms of Ni onto the AuGe layer; and (d) depositing a layer of between 500 to 1000 angstroms of Au onto the Ni layer.
Claim 26
Dependent Claim
41 words
The method of claim 22 wherein the ohmic contact after alloying comprises a two layer structure having a high density of large area NiAs(Ge) grains contacting the semiconductor material as a first layer and a AuGa phase as a top layer.
Claim 27
Dependent Claim
20 words
The method of claim 23 wherein the large area NiAs(Ge) grains contacting the semiconductor material are approximately 300 nm wide.
Claim 28
Independent Claim
85 words
A method of forming an ohmic contact on a semiconductor material containing GaAs comprising the steps of: (a) depositing a non-uniform layer of Au onto one surface of the semiconductor material; (b) depositing a multi-layer ohmic contact of AuGeNi onto the non-uniform Au layer; and (c) alloying the ohmic contact to the semiconductor material thereby forming a two layer structure having a high density of large area NiAs(Ge) grains contacting the semiconductor material as a first layer and a AuGa phase as a top layer.
Claim 29
Independent Claim
85 words
A method of forming an ohmic contact on a semiconductor material containing GaAs comprising the steps of: (a) depositing a non-uniform layer of Au onto one surface of the semiconductor material; (b) depositing a multi-layer ohmic contact of AuGeNi onto the non-uniform Au layer; and (c) alloying the ohmic contact to the semiconductor material thereby forming a two layer structure having a high density of large area NiAs(Ge) grains contacting the semiconductor material as a first layer and a AuGa phase as a top layer.
Claim 30
Dependent Claim
26 words
The method of claim 25 wherein the non-uniform layer of Au is deposited onto the semiconductor by sputter cleaning the semiconductor by using an Au-coated rf-electrode.
Claim 31
Dependent Claim
26 words
The method of claim 26 further including the step of depositing a layer of Ni onto the non-uniform layer of Au prior to the AuGeNi deposition.
References Cited (Backward Citations)
US3386867A
Cited
US3850688A
Cited
US3914785A
Cited
US3959522A
Cited
US4179534A
Cited
US4186410A
Cited
US4188710A
Cited
US4454528A
Cited
JPS5580366A
Cited
US4301188A
Cited
US4471005A
Cited
US4510514A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-31 | 1993-01-30 | 1993-08-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-31 | 1997-01-30 | 1997-08-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-31 | 2001-01-30 | 2001-08-01 | $7700.00 | Window Closed / Lapsed |