Gold-tin-gold ohmic contact to N-type group III-V semiconductors
Assignee: AT&T Inc
•
Filing: 1978-05-24
•
Granted: 1979-12-18
•
Expires: 1998-05-24
Abstract
Abstract A semiconductor device with a low resistance ohmic contact, strongly adherent to the n-type surface of a body (11) of Group III-V compound semiconductor is obtained by a process including the sequential deposition of gold (13), tin (14) and gold (15) at a surface temperature of less than 200 degrees C followed by a heat treatment in a nonoxidizing atmosphere. This process has shown particular advantage when applied to aluminum containing compound semiconductors (e.g., gallium aluminum arsenide). For such use an initial deposition of aluminum (16) has proven particularly successful in producing consistently low resistance ohmic contacts. The invention has been used in the production of light emitting diodes.
Inventors
- 👤 Chuan C. Chang
- 👤 Felix Ermanis
- 👤 Robert J. McCoy
- 👤 Shohei Nakahara
- 👤 Tan T. Sheng
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 08:04
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0116; H10D62/00; H10D62/80; H10D62/85; H10D64/60; H10D64/62; Y; Y10; Y10S; Y10S148/00; Y10S148/02
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
136 words
Method for making a semiconductor device comprising making contact to a semiconductor portion at least one micrometer thick, which said portion includes at least 95 mole percent of Group III-V compound semiconductor, which method comprises (a) depositing a contacting layer of metal on the surface of the semiconductor portion and (b) heat treating the semiconductor portion in a nonoxidizing atmosphere CHARACTERIZED IN THAT the depositing includes the sequential deposition of gold, tin and gold, the first gold deposition and the tin deposition taking place while the body is at a temperature of less than 200 degrees C. and the first gold deposition deposits a layer at least 0.1 micrometers thick and the heat treating step includes a residence time of at least one-half minute in the temperature range from 350 degrees C. to 500 degrees C.
Claim 2
Dependent Claim
136 words
Method for making a semiconductor device comprising making contact to a semiconductor portion at least one micrometer thick, which said portion includes at least 95 mole percent of Group III-V compound semiconductor, which method comprises (a) depositing a contacting layer of metal on the surface of the semiconductor portion and (b) heat treating the semiconductor portion in a nonoxidizing atmosphere CHARACTERIZED IN THAT the depositing includes the sequential deposition of gold, tin and gold, the first gold deposition and the tin deposition taking place while the body is at a temperature of less than 200 degrees C. and the first gold deposition deposits a layer at least 0.1 micrometers thick and the heat treating step includes a residence time of at least one-half minute in the temperature range from 350 degrees C. to 500 degrees C.
Claim 3
Dependent Claim
25 words
A method of claim 1 in which the molar ratio of tin to gold in the contacting layer is from 0.2 to 5 mole percent.
Claim 4
Dependent Claim
14 words
A method of claim 1 in which the portion is an epitaxially deposited layer.
Claim 5
Dependent Claim
22 words
A method of claim 1 in which the semiconductor includes aluminum as at least 10 mole percent of its Group III constituents.
Claim 6
Dependent Claim
23 words
A method of claim 4 in which the depositing step includes the initial deposition of aluminum, sufficient to produce a 20 Angstrom layer.
Claim 7
Dependent Claim
25 words
A method of claim 1 in which the total thickness of gold in the first and second gold depositions is at least 2 micrometers thick.
Claim 8
Dependent Claim
29 words
A method of claim 1 in which the heat treating includes a residence time from 0.5 to 2 minutes in the temperature range from 350 to 500 degrees C.
Claim 9
Dependent Claim
28 words
A method of claim 7 in which the deposition includes sequentially depositing approximately 0.2 micrometers of gold, approximately 0.05 micrometers of tin and approximately 2.8 micrometers of gold.
Claim 10
Dependent Claim
18 words
A method of claim 1 including a further step of applying an external contact to the gold layer.
References Cited (Backward Citations)
US3636618A
Cited
US3850688A
Cited
US3942243A
Cited
US3890699A
Cited
US4011583A
Cited
US3959522A
Cited
US4081824A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-17 | 1983-06-18 | 1983-12-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-17 | 1987-06-18 | 1987-12-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-17 | 1991-06-18 | 1991-12-18 | $7700.00 | Window Closed / Lapsed |