US4853001A — Porous inorganic siliceous-containing gas enrichi…

Claim 1

Independent Claim 256 words

A process of enriching at least one gas from a mixture of gases utilizing a porous, silica-rich membrane material comprising: using at least one hollow, porous, silica-rich, inorganic hydrophilic fiber that is non-crystalline as a porous separation membrane, where the fiber has pore sizes within the range of 1 to around 50 Angstroms in diameter and has a predominant percentage of pore volume comprised of average pore diameters of around 25 Angstroms or less and has a fiber diameter in the range of around 1 to 250 microns and has a wall thickness in the range of around 1 to 50 microns, wherein the silica-rich fiber results from extracting at least 15 weight percent extractable components selected from the group consisting of: (a) components extractable with acids, where the acids are other than hydrofluoric acid, (b) water extractable components, or (c) a mixture thereof, from non-phase-separated, hollow glass fibers formed by attenuation from melt at speeds in the range of at least 500 ft/min to around 30,000 ft/min, where the non-phase-separated glass fibers have a composition selected from the group consisting of: (a) leachable, single-phase, fiberizable, glass compositions; and (b) leachable, phase-separable but non-phase-separated fiberizable silica-containing glass compositions, both having at least 15 to about 60 weight percent components selected from the group consisting of components soluble in acids, where the acids are other than hydrofluoric acid, water soluble components, and mixtures thereof whereby membrane performance in terms of selectivities and permeabilities in gas enrichment can be enhanced over that performance predicted from Knudsen diffusion calculations.

Claim 2

Dependent Claim 256 words

A process of enriching at least one gas from a mixture of gases utilizing a porous, silica-rich membrane material comprising: using at least one hollow, porous, silica-rich, inorganic hydrophilic fiber that is non-crystalline as a porous separation membrane, where the fiber has pore sizes within the range of 1 to around 50 Angstroms in diameter and has a predominant percentage of pore volume comprised of average pore diameters of around 25 Angstroms or less and has a fiber diameter in the range of around 1 to 250 microns and has a wall thickness in the range of around 1 to 50 microns, wherein the silica-rich fiber results from extracting at least 15 weight percent extractable components selected from the group consisting of: (a) components extractable with acids, where the acids are other than hydrofluoric acid, (b) water extractable components, or (c) a mixture thereof, from non-phase-separated, hollow glass fibers formed by attenuation from melt at speeds in the range of at least 500 ft/min to around 30,000 ft/min, where the non-phase-separated glass fibers have a composition selected from the group consisting of: (a) leachable, single-phase, fiberizable, glass compositions; and (b) leachable, phase-separable but non-phase-separated fiberizable silica-containing glass compositions, both having at least 15 to about 60 weight percent components selected from the group consisting of components soluble in acids, where the acids are other than hydrofluoric acid, water soluble components, and mixtures thereof whereby membrane performance in terms of selectivities and permeabilities in gas enrichment can be enhanced over that performance predicted from Knudsen diffusion calculations.

Claim 3

Dependent Claim 15 words

Process of claim 1, wherein acid gases are removed from acid gaseous containing gaseous mixtures.

Claim 4

Dependent Claim 13 words

Process of claim 1, wherein helium is separated from methane and/or natural gas.

Claim 5

Dependent Claim 32 words

Process of claim 1, wherein oxygen is separated from a gaseous mixture selected from the group consisting of oxygen and nitrogen, air, carbon dioxide containing air and oxygen and chlorine gaseous mixtures.

Claim 6

Dependent Claim 11 words

Process of claim 1, wherein a plurality of fibers are used.

Claim 7

Dependent Claim 18 words

Process of claim 1, wherein the porous, silica-rich fibers result from non-heat-treated, hollow glass fibers that are non-phase-separated.

Claim 8

Dependent Claim 13 words

Process of claim 1, wherein nitrogen is separated from methane and/or natural gas.

Claim 9

Dependent Claim 53 words

Article of claim 1, wherein the non-phase-separated hollow glass fibers have a composition that is selected from the group consisting of E-glass, and 621-glass where the glass fibers are attenuated at a speed of around 1,500 to about 6,000 feet per minute, and where the glass fibers are leached without being heat treated.

Claim 10

Dependent Claim 139 words

Article of claim 1, wherein the non-phase-separated hollow glass fibers have a fiberizable composition having an amount in weight percent of silica from 40 to 56 and having an amount of a tetravalent oxide of zirconium, titanium, or hafnium of up to 20 weight percent and acid extractable components selected from the group consisting of: boron oxide from 5 to 13 weight percent and one or more of: alkali metal oxides, alkaline earth metal oxides, trivalent oxides, SnO 2 and P 2 O 5 where the total amount of the acid extractable components gives a volume percent of the acid extractables in the glass fibers in the range of at least 15 to 60 volume percent, and wherein the hollow glass fibers are non-heat-treated and whereby the extraction of the hollow glass fibers results in hollow porous, silica-rich fibers.

Claim 11

Dependent Claim 20 words

Process of claim 1, wherein the hollow glass fibers are attenuated from melt without application of a chemical sizing composition.

Claim 12

Dependent Claim 82 words

Process of claim 1, wherein using the porous silica-rich membrane material includes: contacting the gaseous mixture with one surface of the hollow, porous, silica-rich fiber at temperature in the range of below ambient to elevated temperatures and at a pressure in the range of about 1 to 5,000 psi; and removing from the vicinity of the opposite surface of the hollow porous silica-rich fiber from that of the contact surface, a produce enriched in at least one gas of said gaseous mixture.

Claim 13

Dependent Claim 12 words

Process of claim 11, wherein the product removed is the permeate gas.

Claim 14

Dependent Claim 17 words

Process of claim 11, wherein the product removed is the rejected gas separated from the permeate gas.

Claim 15

Dependent Claim 39 words

Process of claim 11, wherein the product gas removed is both the permeate gas, separated from a rejected gas and removed from one side of the fiber, and the rejected gas removed from the other side of the fiber.

Claim 16

Dependent Claim 202 words

A gas separation material, comprising: at least one hollow, porous, non-crystalline, inorganic, silica-rich fiber as a porous separation membrane having pore sizes within the range of about 1 to around 50 Angstroms in diameter, and a predominant percentage of pore volume comprised of average pore diameters of around 25 Angstroms or less and fiber diameters in the range of 1 to around 25 micrometers, and a fiber wall thickness in the range of around 1 to around 50 micrometers, wherein the silica-rich fiber results from extracting extractable materials selected from the group consisting of acid and water extractable materials and mixtures thereof from non-phase separated, hollow glass fibers, formed by attenuation from melt at speeds in the range of at least 500 ft/min to around 30,000 ft/min, where the non-phase-separated glass fibers have a composition selected from the group consisting of (a) leachable, single-phase compositions, and (b) leachable, phase-separable fiberizable silica-containing glass compositions, both having at least 20 to about 60 weight percent components soluble in acids, where the acids are other than hydrofluoric acid, and/or water soluble components, whereby membrane performance in terms of selectivities and permeabilities in gas separations can be enriched over that performance predicted from Knudsen diffusion calculations.

Claim 17

Dependent Claim 202 words

A gas separation material, comprising: at least one hollow, porous, non-crystalline, inorganic, silica-rich fiber as a porous separation membrane having pore sizes within the range of about 1 to around 50 Angstroms in diameter, and a predominant percentage of pore volume comprised of average pore diameters of around 25 Angstroms or less and fiber diameters in the range of 1 to around 25 micrometers, and a fiber wall thickness in the range of around 1 to around 50 micrometers, wherein the silica-rich fiber results from extracting extractable materials selected from the group consisting of acid and water extractable materials and mixtures thereof from non-phase separated, hollow glass fibers, formed by attenuation from melt at speeds in the range of at least 500 ft/min to around 30,000 ft/min, where the non-phase-separated glass fibers have a composition selected from the group consisting of (a) leachable, single-phase compositions, and (b) leachable, phase-separable fiberizable silica-containing glass compositions, both having at least 20 to about 60 weight percent components soluble in acids, where the acids are other than hydrofluoric acid, and/or water soluble components, whereby membrane performance in terms of selectivities and permeabilities in gas separations can be enriched over that performance predicted from Knudsen diffusion calculations.

Claim 18

Dependent Claim 67 words

Article of claim 15, wherein the leachable, silicate glass compositions are selected from the group consisting of phase-separable borosilicate glass fibers having one or more oxides of a metal from Group IVB of the Periodic Table, phase-separable borosilicate glass compositions with an amount of boron oxide in the range from around 5 to around 60 weight percent of the glass fibers, and alkali metal silicate glass compositions.

Claim 19

Dependent Claim 12 words

Article of claim 16, wherein the Group IVB metal oxide is zirconium.

Claim 20

Dependent Claim 29 words

Article of claim 15, wherein the pore volume of the hollow, porous, silica-rich fiber is in the range of around 0.15 up to around 1 cm 3 per gram.

Claim 21

Dependent Claim 15 words

Article of claim 15, wherein the fiber outer diameter is less than 100 microns (um).

Claim 22

Dependent Claim 22 words

Article of claim 15, wherein the fiber outer diameter is in the range selected from about 10 to about 70 microns (um).

Claim 23

Dependent Claim 15 words

Article of claim 15, wherein the fiber outer diameter is less than 50 microns (um).

Claim 24

Dependent Claim 24 words

Article of claim 15, wherein the attenuation speed of the hollow glass fibers is in the range of 1,000 ft/min to around 20,000 ft/min.

Claim 25

Dependent Claim 24 words

Article of claim 15, wherein the wall thickness of the hollow glass fibers is in the range of around 1 to 10 microns (um).

Claim 26

Dependent Claim 25 words

Article of claim 15, wherein the wall thickness of the hollow glass fibers is in the range of about 1 to about 5 microns (um).

Claim 27

Dependent Claim 27 words

Article of claim 15, wherein the inner diameter to outer diameter ratio of the hollow glass fibers is in the range of about 0.4 to about 0.96.

Claim 28

Dependent Claim 16 words

Article of claim 15, wherein the mean pore size is less than 30 Angstroms in diameter.

Claim 29

Dependent Claim 16 words

Article of claim 15, wherein the mean pore side is less than 20 Angstroms in diameter.

Claim 30

Dependent Claim 99 words

Article of claim 15, wherein the acid extractable components are selected from the group consisting of P 2 O 5 , Al 2 O 3 , Fe 2 O 3 , PbO, Na 2 O, SNO 2 , ZnO, CaO, MgO, K 2 O, BaO, fluorine and B 2 O 3 or mixtures thereof where the total acid extractable components are present in the range of around 15 to 60 weight percent of the glass fiber and where B 2 O 3 is present as the predominant acid extractable component in the range of 5 to 60 weight percent.

Claim 31

Dependent Claim 18 words

Article of claim 15, wherein the hollow, porous fibers are produced from non-heat-treated, glass fibers that are non-phase-separated.

Claim 32

Dependent Claim 39 words

Article of claim 15, wherein the non-phase-separated hollow glass fibers have a composition that is selected from the group consisting of E-glass, and 621-glass where the glass fibers are attenuated at a speed of around 1,500 to 6,000 ft/min.

Claim 33

Dependent Claim 79 words

The gas separation material of claim 15, prepared from non-phase-separated, hollow glass fibers by acid leaching with agitation with an acid having a normality of around 3 to 4, at a temperature in the range of 50° C. to 70° C. for about 24 to about 48 hours to remove a substantial amount of the at least 20 weight percent acid soluble components to result in the pore volume in the range of about 0.15 to about 0.75 cc/gm.

Claim 34

Dependent Claim 138 words

Article of claim 15, wherein the non-phase-separated hollow glass fibers have a fiberizable composition having an amount in weight percent of silica from 40 to 56 and having an amount of tetravalent oxide of zirconium, titanium, or hafnium of up to 20 weight percent and acid extractable components selected from the group consisting of: boron oxide from 5 to 13 weight percent and one or more of: alkali metal oxides, alkaline earth metal oxides, trivalent oxides, SnO 2 and P 2 O 5 , where the total amount of said extractable components gives a volume percent of the acid extractables in the glass fibers in the range of at least 15 to 60 volume percent, and wherein the hollow glass fibers are non-heat-treated and whereby the extraction of the hollow glass fibers results in hollow porous, silica-rich fibers.

Claim 35

Dependent Claim 19 words

Article of claim 15, wherein the hollow glass fibers are devoid of the presence of a chemical sizing composition.

Claim 36

Dependent Claim 171 words

A gas separation material for enriching at least one gas from a gaseous mixture, comprising: at least one hollow, porous, non-crystalline, inorganic, silica-rich fiber with pore sizes within the range of 1 to around 30 Angstroms in diameter and with a predominant percentage of pore volume comprised of average pore diameter of less than around 20 Angstroms in diameter and a fiber outer diameter in the range of around 4 microns (um) to 40 microns (um) and with a fiber wall thickness in the range of around 1 micron to 10 microns (um), and with an inner diameter to outer diameter ratio of around 0.4 to around 0.96 and where the silica-rich fibers result from extracting acid soluble components from the non-phase-separated, hollow glass fibers having a phase separable borosilicate glass fiber composition with one or more oxides of a metal of Group IVB of the Periodic Table, whereby membrane performance in terms of selectivities and permeabilities in gas separations can be enhanced over that performance predicted from Knudsen diffusion calculations.

Claim 37

Dependent Claim 171 words

A gas separation material for enriching at least one gas from a gaseous mixture, comprising: at least one hollow, porous, non-crystalline, inorganic, silica-rich fiber with pore sizes within the range of 1 to around 30 Angstroms in diameter and with a predominant percentage of pore volume comprised of average pore diameter of less than around 20 Angstroms in diameter and a fiber outer diameter in the range of around 4 microns (um) to 40 microns (um) and with a fiber wall thickness in the range of around 1 micron to 10 microns (um), and with an inner diameter to outer diameter ratio of around 0.4 to around 0.96 and where the silica-rich fibers result from extracting acid soluble components from the non-phase-separated, hollow glass fibers having a phase separable borosilicate glass fiber composition with one or more oxides of a metal of Group IVB of the Periodic Table, whereby membrane performance in terms of selectivities and permeabilities in gas separations can be enhanced over that performance predicted from Knudsen diffusion calculations.

Claim 38

Dependent Claim 16 words

Article of claim 34, wherein the hollow glass fibers are devoid of any chemical sizing composition.

Claim 39

Dependent Claim 249 words

A process for producing a gas enriching membrane, comprising: (a) forming at least one non-phase-separated, hollow glass fiber having a composition selected from the group consisting of (a) extractable, single-phase silicates, and (2) extractable phase-separable silicates both having an amount of at least 20 weight percent extractables by acids other than hydrofluoric or phosphoric acid, extractables or water extractables of at least 15 weight percent, where the hollow glass fibers have an outer diameter in the range of 1 to 250 microns (um) and have a wall thickness in the range of around 1 to around 50 microns (um) and have an inner to outer diameter ratio in the range of 0.4 to 0.96 and where the fibers are attenuated (formed) at a speed in the range of 500 to 30,000 feet/min. with rapid cooling of the fibers, (b) leaching a non-heat-treated, hollow glass fiber to remove extractables selected from the group consisting of acid extractables soluble in acids that are acids other than hydrofluoric acid, and water soluble, and mixtures thereof to produce a porous, silica-rich, hollow fiber having pores with diameters from 1 to 50 Angstroms and with predominant percentage of the pore volume comprised of pores with an average diameter of around 20 Angstroms or less and with a pore volume in the range of around 0.15 to around 0.75 cm 3 /gm, whereby membrane performance in terms of selectivities and permeabilities in gas separations can be enhanced over that performance predicted from Knudsen diffusion calculations.

Claim 40

Dependent Claim 249 words

A process for producing a gas enriching membrane, comprising: (a) forming at least one non-phase-separated, hollow glass fiber having a composition selected from the group consisting of (a) extractable, single-phase silicates, and (2) extractable phase-separable silicates both having an amount of at least 20 weight percent extractables by acids other than hydrofluoric or phosphoric acid, extractables or water extractables of at least 15 weight percent, where the hollow glass fibers have an outer diameter in the range of 1 to 250 microns (um) and have a wall thickness in the range of around 1 to around 50 microns (um) and have an inner to outer diameter ratio in the range of 0.4 to 0.96 and where the fibers are attenuated (formed) at a speed in the range of 500 to 30,000 feet/min. with rapid cooling of the fibers, (b) leaching a non-heat-treated, hollow glass fiber to remove extractables selected from the group consisting of acid extractables soluble in acids that are acids other than hydrofluoric acid, and water soluble, and mixtures thereof to produce a porous, silica-rich, hollow fiber having pores with diameters from 1 to 50 Angstroms and with predominant percentage of the pore volume comprised of pores with an average diameter of around 20 Angstroms or less and with a pore volume in the range of around 0.15 to around 0.75 cm 3 /gm, whereby membrane performance in terms of selectivities and permeabilities in gas separations can be enhanced over that performance predicted from Knudsen diffusion calculations.

Claim 41

Dependent Claim 156 words

Process of claim 36, wherein the non-phase-separated hollow glass fibers have a fiberizable composition having an amount in weight percent of silica from 40 to 56 and having an amount of a tetravalent oxide of zirconium, titanium, or hafnium of up to 20 weight percent and acid extractable components selected from the group consisting of: boron oxide from 5 to 13 weight percent and one or more of: alkali metal oxides, alkaline earth metal oxides, trivalent oxides, SnO 2 , and P 2 O 5 where the total amount of the acid extractable components gives a volume percent of the acid extractables in the glass fibers in the range of at least 15 to 60 volume percent, where the hollow glass fibers are leached without heat treating and whereby the extraction of the hollow glass fibers results in hollow porous, silica-rich fibers having a pore volume of around 0.15 to around 0.75 cubic centimeters per gram.

Claim 42

Dependent Claim 19 words

Process of claim 36, wherein the hollow glass fibers are attenuated without the application of a chemical sizing composition.

Claim 43

Dependent Claim 53 words

Process of claim 36, wherein the non-phase-separated hollow glass fibers have a composition that is selected from the group consisting of E-glass and 621-glass and where the glass fibers are attenuated at a speed of around 1,500 to 6,000 feet per minute, and where the glass fibers are leached without being heat treated.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1992-07-31	1993-01-30	1993-08-01	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1996-07-31	1997-01-30	1997-08-01	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2000-07-31	2001-01-30	2001-08-01	$7700.00	Window Closed / Lapsed

Porous inorganic siliceous-containing gas enriching material and process of manufacture and use

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag