Process for production of porous glass membrane tubes

Claim 2

A process for the production of a microporous tubular glass self-supporting membrane in the form of a hollow fiber comprising the steps of: I. drawing a hot endless thin walled glass hollow fiber from a melt of an alkali borosilicate glass, and then immediately, Ii. directly cooling the hot hollow fiber by cooling devices which are arranged directly beneath the tip sufficient to fix its external shape and internal structure the walls of the separate fibers being free, and then Iii. heating the hollow fiber to a temperature sufficient to effect phase separation into A. a coherent, silicon dioxide phase, which is substantially insoluble in mineral acid, and, B. a boron oxide phase rich in alkali borate and then Iv. extracting the hollow fiber with mineral acid by circulating the acid along the inside wall and the outside wall of the hollow fiber thereby dissolving out the boron oxide phase, thereby forming a microporous tubular glass membrane of the substantially insoluble silicon dioxide phase, wherein the hollow fiber has initial pore sizes between 11 A and 50 A and wherein the glass has the following composition by weight: A. b 2 o 3 20-35% by weight. B. alkali metal oxide 4-12% by weight. SiO 2 balance essentially.

Claim 3

A process of claim 1 wherein the tubes have an internal diameter of 30 to 80 microns.

Claim 4

A process of claim 1 further comprising the step of enlarging the pores of the microporous membrane by partially dissolving the silicon dioxide phase.

Claim 5

A process for the production of a microporous tubular glass self-supporting membrane in the form of a tube comprising the steps of: I. drawing a hot endless thin walled glass tube from a melt of an alkali borosilicate glass, and then immediately, Ii. directly cooling the hot tube sufficient to fix its external shape and internal structure, and then Iii. heating the tube to a temperature sufficient to effect phase separation into A. a coherent, silicon dioxide phase, which is substantially insoluble in mineral acid, and, B. a boron oxide phase rich in alkali borate and then Iv. extracting the tube with mineral acid by circulating the acid along the inside wall and the outside wall of the hollow fiber thereby dissolving out the boron oxide phase, thereby forming a microporous tubular glass membrane of the substantially insoluble silicon dioxide phase, and then V. asymmetrically enlarging the pores from both sides of the glass membrane by the use of different solvents wherein the tube has wall thickness between 5 and 30 microns and initial pore sizes between 11A and 50A and wherein the glass has the following composition by weight: A. b 2 o 3 20-35% by weight B. alkali metal oxide 4-12% by weight C. siO 2 balance essentially.

Claim 6

A process for the production of a microporous tubular glass self-supporting membrane in the form of a tube comprising the steps of: I. drawing a hot endless thin walled glass tube from a melt of an alkali borosilicate glass, and then immediately, Ii. directly cooling the hot tube sufficient to fix its external shape and internal structure, and then Iii. heating the tube to a temperature sufficient to effect phase separation into A. a coherent, silicon dioxide phase, which is substantially insoluble in mineral acid, and, B. a boron oxide phase rich in alkali borate and then Iv. extracting the tube with mineral acid by circulating the acid along the inside wall and the outside wall of the hollow fiber thereby dissolving out the boron oxide phase, thereby forming a microporous tubular glass membrane of the substantially insoluble silicon dioxide phase, and then V. asymmetrically enlarging the pores from both sides of the glass membrane by the use of different solvents wherein the tube has wall thickness between 5 and 30 microns and initial pore sizes between 11A and 50A and wherein the glass has the following composition by weight: A. b 2 o 3 20-35% by weight B. alkali metal oxide 4-12% by weight C. siO 2 balance essentially.

Claim 7

A process of claim 1 further comprising the subsequent step of shrinking the glass membrane by a temperature treatment such that the pores are reduced in size.

Claim 8

A process of claim 5 wherein the thermal treatment of the glass membrane is conducted at a temperature of 700° to 800° C.

Claim 9

A process for the production of a microporous tubular glass self-supporting membrane in the form of a tube comprising the steps of: I. drawing a hot endless thin walled glass tube from a melt of an alkali borosilicate glass, and then immediately, Ii. directly cooling the hot tube sufficient to fix its external shape and internal structure, and then Iii. heating the tube to a temperature sufficient to effect phase separation into A. a coherent, silicon dioxide phase, which is substantially insoluble in mineral acid, and, B. a boron oxide phase rich in alkali borate and then Iv. extracting the tube with mineral acid by circulating the acid along the inside wall and the outside wall of the hollow fiber thereby dissolving out the boron oxide phase, thereby forming a microporous tubular glass membrane of the substantially insoluble silicon dioxide phase, and then V. shrinking the glass membrane by a temperature treatment at 700° to 800° C such that the pores are reduced in size, wherein the temperature treatment is effected from both sides of the glass membrane at different temperatures in order to produce pores having a different pore size on one side of the membrane compared to the pore size on the other side of the membrane, wherein the tube has wall thickness between 5 and 30 microns and initial pore sizes between 11 A and 50 A and wherein the glass has the following composition by weight: A. b 2 o 3 20-35% by weight B. alkali metal oxide 4-12% by weight C. siO 2 balance essentially.

Claim 10

A process for the production of a microporous tubular glass self-supporting membrane in the form of a tube comprising the steps of: I. drawing a hot endless thin walled glass tube from a melt of an alkali borosilicate glass, and then immediately, Ii. directly cooling the hot tube sufficient to fix its external shape and internal structure, and then Iii. heating the tube to a temperature sufficient to effect phase separation into A. a coherent, silicon dioxide phase, which is substantially insoluble in mineral acid, and, B. a boron oxide phase rich in alkali borate and then Iv. extracting the tube with mineral acid by circulating the acid along the inside wall and the outside wall of the hollow fiber thereby dissolving out the boron oxide phase, thereby forming a microporous tubular glass membrane of the substantially insoluble silicon dioxide phase, and then V. shrinking the glass membrane by a temperature treatment at 700° to 800° C such that the pores are reduced in size, wherein the temperature treatment is effected from both sides of the glass membrane at different temperatures in order to produce pores having a different pore size on one side of the membrane compared to the pore size on the other side of the membrane, wherein the tube has wall thickness between 5 and 30 microns and initial pore sizes between 11 A and 50 A and wherein the glass has the following composition by weight: A. b 2 o 3 20-35% by weight B. alkali metal oxide 4-12% by weight C. siO 2 balance essentially.

Claim 11

A process according to claim 7 wherein the temperature difference is between 10° and 100° C.

Claim 12

A process of claim 4 further comprising the step of reducing the pore size.

Claim 13

A process of claim 9 further comprising the steps of V. shrinking the pores and then Iv. asymmetrically enlarging the pores by partially dissolving the silicon dioxide structure.

Claim 14

A process for the production of a microporous tubular glass self-supporting membrane in the form of a hollow fiber comprising the steps of: I. drawing a hot endless thin walled glass hollow fiber from a melt of an alkali borosilicate glass, and then immediately, Ii. directly cooling the hot hollow fiber sufficient to fix its external shape and internal structure, and then Iii. heating the hollow fiber to a temperature sufficient to effect phase separation into A. a coherent, silicon dioxide phase, which is substantially insoluble in mineral acid, and B. a boron oxide phase rich in alkali borate and then Iv. extracting the hollow fiber with mineral acid by circulating the acid along the inside wall and the outside wall of the hollow fiber thereby dissolving out the boron oxide phase, thereby forming a microporous tubular glass membrane of the substantially insoluble silicon dioxide phase, V. heating the outside of the hollow fibers at a temperature between 700°-800° C. while maintaining the inside of the hollow fibers 10° to 100° C. cooler by flushing with air at a temperature 10° to 100° C. cooler than the outside heating temperature, wherein the hollow fiber has wall thickness between 5 and 30 microns and initial pore sizes between 11 A and 50 A and the pore size on the outside of the hollow fiber is reduced after the heating, and wherein the glass has the following composition by weight: A. b 2 o 3 20-35% by weight. B. alkali metal oxide 4-12% by weight. C. siO 2 balance essentially.

Claim 15

A process for the production of a microporous tubular glass self-supporting membrane in the form of a hollow fiber comprising the steps of: I. drawing a hot endless thin walled glass hollow fiber from a melt of an alkali borosilicate glass, and then immediately, Ii. directly cooling the hot hollow fiber sufficient to fix its external shape and internal structure, and then Iii. heating the hollow fiber to a temperature sufficient to effect phase separation into A. a coherent, silicon dioxide phase, which is substantially insoluble in mineral acid, and B. a boron oxide phase rich in alkali borate and then Iv. extracting the hollow fiber with mineral acid by circulating the acid along the inside wall and the outside wall of the hollow fiber thereby dissolving out the boron oxide phase, thereby forming a microporous tubular glass membrane of the substantially insoluble silicon dioxide phase, V. heating the outside of the hollow fibers at a temperature between 700°-800° C. while maintaining the inside of the hollow fibers 10° to 100° C. cooler by flushing with air at a temperature 10° to 100° C. cooler than the outside heating temperature, wherein the hollow fiber has wall thickness between 5 and 30 microns and initial pore sizes between 11 A and 50 A and the pore size on the outside of the hollow fiber is reduced after the heating, and wherein the glass has the following composition by weight: A. b 2 o 3 20-35% by weight. B. alkali metal oxide 4-12% by weight. C. siO 2 balance essentially.

Claim 16

A process for the production of a microporous tubular glass self-supporting membrane in the form of a hollow fiber comprising the steps of: I. drawing a hot endless thin walled glass hollow fiber from a melt of an alkali borosilicate glass, and then immediately, Ii. directly cooling the hot hollow fiber sufficient to fix its external shape and internal structure, and then Iii. heating the hollow fiber to a temperature sufficient to effect phase separation into A. a coherent, silicon dioxide phase, which is substantially insoluble in mineral acid, and, B. a boron oxide phase rich in alkali borate and then Iv. extracting the hollow fiber with mineral acid by circulating the acid along the inside wall of the hollow fiber thereby dissolving out the boron oxide phase, thereby forming a microporous tubular glass membrane of the substantially insoluble silicon dioxide phase, V. treating the glass hollow fiber with a chlorosilane, wherein the hollow fiber has initial pore sizes between 11 A and 50 A and the pore size on the outside of the hollow fiber is reduced after the heating, and wherein the glass has the following composition by weight: A. b 2 o 3 20-35% by weight B. alkali metal oxide 4-12% by weight C. siO 2 balance essentially.

Claim 17

A process for the production of a microporous tubular glass self-supporting membrane in the form of a hollow fiber comprising the steps of: I. drawing a hot endless thin walled glass hollow fiber from a melt of an alkali borosilicate glass, and then immediately, Ii. directly cooling the hot hollow fiber sufficient to fix its external shape and internal structure, and then Iii. heating the hollow fiber to a temperature sufficient to effect phase separation into A. a coherent, silicon dioxide phase, which is substantially insoluble in mineral acid, and, B. a boron oxide phase rich in alkali borate and then Iv. extracting the hollow fiber with mineral acid by circulating the acid along the inside wall of the hollow fiber thereby dissolving out the boron oxide phase, thereby forming a microporous tubular glass membrane of the substantially insoluble silicon dioxide phase, V. treating the glass hollow fiber with a chlorosilane, wherein the hollow fiber has initial pore sizes between 11 A and 50 A and the pore size on the outside of the hollow fiber is reduced after the heating, and wherein the glass has the following composition by weight: A. b 2 o 3 20-35% by weight B. alkali metal oxide 4-12% by weight C. siO 2 balance essentially.

Claim 18

A process for the production of a microporous tubular glass self-supporting membrane in the form of a hollow fiber comprising the steps of: I. drawing a hot endless thin walled glass hollow fiber from a melt of an alkali borosilicate glass, and then immediately, Ii. directly cooling the hot hollow fiber sufficient to fix its external shape and internal structure, and then Iii. heating the hollow fiber to a temperature sufficient to effect phase separation into A. a coherent, silicon dioxide phase, which is substantially insoluble in mineral acid, and, B. a boron oxide phase rich in alkaki borate and then Iv. extracting the hollow fiber with mineral acid by circulating the acid along the inside wall and the outside wall of the hollow fiber thereby dissolving out the boron oxide phase, thereby forming a microporous tubular glass membrane of the substantially insoluble silicon dioxide phase, V. treating the hollow fiber with an organic silane in which the organic end is bound to the silanol group of the glass, Vi treating the terminal end of the organic silane in a photo reaction with halogen resulting in a halogen group to be situated at the terminal end, Vii. treating the terminal end of the organic silane with a compound containing a hydrophilic group so as to attach the hydrophilic group to the terminal end of the organic silane, and wherein the hollow fiber has initial pore sizes between 11 A and 50 A and wherein the glass has the following composition by weight: A. b 2 o 3 20-35% by weight, B. alkali metal oxide 4-12% by weight, C. siO 2 balance essentially.

Claim 19

A process for the production of a microporous tubular glass self-supporting membrane in the form of a hollow fiber comprising the steps of: I. drawing a hot endless thin walled glass hollow fiber from a melt of an alkali borosilicate glass, and then immediately, Ii. directly cooling the hot hollow fiber sufficient to fix its external shape and internal structure, and then Iii. heating the hollow fiber to a temperature sufficient to effect phase separation into A. a coherent, silicon dioxide phase, which is substantially insoluble in mineral acid, and, B. a boron oxide phase rich in alkaki borate and then Iv. extracting the hollow fiber with mineral acid by circulating the acid along the inside wall and the outside wall of the hollow fiber thereby dissolving out the boron oxide phase, thereby forming a microporous tubular glass membrane of the substantially insoluble silicon dioxide phase, V. treating the hollow fiber with an organic silane in which the organic end is bound to the silanol group of the glass, Vi treating the terminal end of the organic silane in a photo reaction with halogen resulting in a halogen group to be situated at the terminal end, Vii. treating the terminal end of the organic silane with a compound containing a hydrophilic group so as to attach the hydrophilic group to the terminal end of the organic silane, and wherein the hollow fiber has initial pore sizes between 11 A and 50 A and wherein the glass has the following composition by weight: A. b 2 o 3 20-35% by weight, B. alkali metal oxide 4-12% by weight, C. siO 2 balance essentially.