US4849045A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Extrusion casting method
Assignee: Motors Liquidation Co
•
Filing: 1988-05-05
•
Granted: 1989-07-18
•
Expires: 2008-05-05
Abstract
Abstract A method of producing a profiled strip of polymeric material having a desirable surface finish on the outer periphery of the strip. The method comprising the steps of first extruding a profile strip of polymeric material through an extrusion die in a plastic extruder, laminating a sheet layer having a desirable surface finish on the surface facing the profiled strip to a predetermined area on the outer periphery of the profile strip and then cooling the profiled strip together with the laminated sheet layer such that the laminated sheet layer can be removed from the profiled strip to expose the desirable finish reproduced from the surface of the sheet layer.
Inventors
- 👤 Fred K. Schmidt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 19:10
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/04; B32B15/08; B32B15/082; B44; B44C; B44C3/00; B44C3/08; B29; B29C; B29C48/00; B29C48/03; B29C48/07; B29C48/12; B29C48/15; B29C48/154; B29C48/155; B32B15/20; B32B7/00; B32B7/04; B32B7/06; B32B2307/00; B32B2307/40; B32B2307/406; B32B2311/00; B32B2311/24; B32B2327/00; B32B2327/06; Y; Y10; Y10T; Y10T156/00; Y10T156/11
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
186 words
A method of using a plastic extruder equipped with an extrusion die to produce a profiled strip of polymeric material and removably laminating a sheet layer having a desirable surface finish to cover a predetermined area on the outer periphery of the profiled strip with the surface having said desirable finish facing said strip such that said desirable surface finish is reproduced on said surface area of said strip when said removably laminated sheet layer is removed prior to the final use of said profiled strip, said method comprising the steps of: extruding a profiled strip of polymeric material through said extrusion die; removably laminating a sheet layer having a desirable surface finish on the surface facing said profiled strip to a predetermined area on the outer periphery of said profiled strip, said sheet layer having a softening temperature at least 20° F. higher than the softening temperature of said polymeric material; cooling said profiled strip together with said laminated sheet layer such that said laminated sheet layer can be removed from said profiled strip to expose said desirable surface finish reproduced from said sheet layer.
Claim 2
Independent Claim
186 words
A method of using a plastic extruder equipped with an extrusion die to produce a profiled strip of polymeric material and removably laminating a sheet layer having a desirable surface finish to cover a predetermined area on the outer periphery of the profiled strip with the surface having said desirable finish facing said strip such that said desirable surface finish is reproduced on said surface area of said strip when said removably laminated sheet layer is removed prior to the final use of said profiled strip, said method comprising the steps of: extruding a profiled strip of polymeric material through said extrusion die; removably laminating a sheet layer having a desirable surface finish on the surface facing said profiled strip to a predetermined area on the outer periphery of said profiled strip, said sheet layer having a softening temperature at least 20° F. higher than the softening temperature of said polymeric material; cooling said profiled strip together with said laminated sheet layer such that said laminated sheet layer can be removed from said profiled strip to expose said desirable surface finish reproduced from said sheet layer.
Claim 3
Independent Claim
198 words
A method of using a plastic extruder equipped with an extrusion die to produce a profiled strip of polymeric material and removably laminating a sheet layer having a desirable surface finish to cover a predetermined area on the outer periphery of the profiled strip with the surface having said desirable finish facing said strip such that said desirable surface finish is reproduced on said surface area of said strip when said removably laminated sheet layer is removed prior to the final use of said profiled strip, said method comprising the steps of: extruding a profiled strip of polymeric material through said extrusion die; removably laminating a sheet layer having a desirable surface finish on the surface facing said profiled strip to a predetermined area on the outer periphery of said profiled strip while surface temperature of said strip is no less than 200° F., said sheet layer having a softening temperature at least 20° F. higher than the softening temperature of said polymeric material; cooling said profiled strip together with said laminated sheet layer such that said laminated sheet layer can be removed from said profiled strip to expose said desirable surface finish reproduced from said sheet layer.
Claim 4
Independent Claim
198 words
A method of using a plastic extruder equipped with an extrusion die to produce a profiled strip of polymeric material and removably laminating a sheet layer having a desirable surface finish to cover a predetermined area on the outer periphery of the profiled strip with the surface having said desirable finish facing said strip such that said desirable surface finish is reproduced on said surface area of said strip when said removably laminated sheet layer is removed prior to the final use of said profiled strip, said method comprising the steps of: extruding a profiled strip of polymeric material through said extrusion die; removably laminating a sheet layer having a desirable surface finish on the surface facing said profiled strip to a predetermined area on the outer periphery of said profiled strip while surface temperature of said strip is no less than 200° F., said sheet layer having a softening temperature at least 20° F. higher than the softening temperature of said polymeric material; cooling said profiled strip together with said laminated sheet layer such that said laminated sheet layer can be removed from said profiled strip to expose said desirable surface finish reproduced from said sheet layer.
Claim 5
Independent Claim
209 words
A method of using a plastic extruder equipped with an extrusion die to produce a profiled strip of polymeric material and removably laminating a sheet layer having a desirable surface finish to cover a predetermined area on the outer periphery of the profiled strip with the surface having said desirable finish facing said strip such that said desirable surface finish is reproduced on said surface area of said strip when said removably laminated sheet layer is removed prior to the final use of said profiled strip, said method comprising the steps of: extruding a profiled strip of polymeric material through said extrusion die; removably laminating a sheet layer having a desirable surface texture on the surface facing said profiled strip to a predetermined area on the outer periphery of said profiled strip while the temperature of said profiled strip is no less than 200° F., said sheet layer being made of a material dissimilar to that of the profiled strip such that no permanent bond occurs between said sheet layer and said profiled strip, and cooling said profiled strip together with said laminated sheet layer such that said laminated sheet layer can be removed from said profiled strip to expose said desirable surface finish reproduced from said sheet layer.
Claim 6
Independent Claim
209 words
A method of using a plastic extruder equipped with an extrusion die to produce a profiled strip of polymeric material and removably laminating a sheet layer having a desirable surface finish to cover a predetermined area on the outer periphery of the profiled strip with the surface having said desirable finish facing said strip such that said desirable surface finish is reproduced on said surface area of said strip when said removably laminated sheet layer is removed prior to the final use of said profiled strip, said method comprising the steps of: extruding a profiled strip of polymeric material through said extrusion die; removably laminating a sheet layer having a desirable surface texture on the surface facing said profiled strip to a predetermined area on the outer periphery of said profiled strip while the temperature of said profiled strip is no less than 200° F., said sheet layer being made of a material dissimilar to that of the profiled strip such that no permanent bond occurs between said sheet layer and said profiled strip, and cooling said profiled strip together with said laminated sheet layer such that said laminated sheet layer can be removed from said profiled strip to expose said desirable surface finish reproduced from said sheet layer.
Claim 7
Independent Claim
201 words
A method of using a plastic extruder equipped with an extrusion die to produce a profiled strip of polymeric material and removably laminating a sheet layer having a desirable surface finish to cover a predetermined area on the outer periphery of the profiled strip with the surface having said desirable finish facing said strip such that said desirable surface finish is reproduced on said surface area of said strip when said removably laminated sheet layer is removed prior to the final use of said profiled strip, said method comprising the steps of: extruding a profiled strip of polymeric material through said extrusion die; removably laminating a sheet layer having a desirable surface finish on the surface facing said profiled strip to a predetermined area on the outer periphery of said profiled strip while the surface temperature of said profiled strip is no less than 200° F., said sheet layer having a softening temperature at least 20° F. higher than the softening temperature of said polymeric material; cooling said profiled strip together with said laminated sheet layer, and removing said laminated sheet layer from said profiled strip to expose said desirable surface finish on said profiled strip reproduced from said sheet layer.
Claim 8
Independent Claim
201 words
A method of using a plastic extruder equipped with an extrusion die to produce a profiled strip of polymeric material and removably laminating a sheet layer having a desirable surface finish to cover a predetermined area on the outer periphery of the profiled strip with the surface having said desirable finish facing said strip such that said desirable surface finish is reproduced on said surface area of said strip when said removably laminated sheet layer is removed prior to the final use of said profiled strip, said method comprising the steps of: extruding a profiled strip of polymeric material through said extrusion die; removably laminating a sheet layer having a desirable surface finish on the surface facing said profiled strip to a predetermined area on the outer periphery of said profiled strip while the surface temperature of said profiled strip is no less than 200° F., said sheet layer having a softening temperature at least 20° F. higher than the softening temperature of said polymeric material; cooling said profiled strip together with said laminated sheet layer, and removing said laminated sheet layer from said profiled strip to expose said desirable surface finish on said profiled strip reproduced from said sheet layer.
Claim 9
Dependent Claim
29 words
In a method claimed in claim 1, said surface finish on said sheet layer being a high gloss finish having a 20° gloss reading of no less than 60.
Claim 10
Dependent Claim
30 words
In a method claimed in claim 4, said surface finish on said sheet layer being a high gloss finish having a 20 degree gloss reading of no less than 60.
References Cited (Backward Citations)
US3843475A
Cited
US3811989A
Cited
US4167431A
Cited
US4081504A
Cited
US4368224A
Cited
DE2908487A1
Cited
JPS5714026A
Cited
JPS57207038A
Cited
JPS57207042A
Cited
JPS58116140A
Cited
US4478663A
Cited
US4698193A
Cited
JPH0699633A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-17 | 1993-01-16 | 1993-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-17 | 1997-01-16 | 1997-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-17 | 2001-01-16 | 2001-07-18 | $7700.00 | Window Closed / Lapsed |