Process for providing isolation between CMOS devices
Assignee: Motorola Solutions Inc
•
Filing: 1988-09-12
•
Granted: 1989-07-11
•
Expires: 2008-09-12
Abstract
Abstract A process is disclosed for the selective oxidation of MOS devices which preferentially removes implanted field doping from selected silicon substrate regions. In one embodiment, a CMOS substrate is provided with an overlying layer of silicon oxide and a layer of polycrystalline silicon. Active and field regions are defined in each of the CMOS device regions. A blanket boron implantation dopes both the N-type and P-type field regions. The N-type field region is selectively oxidized at a greater oxidation rate than is the P-type field region to cause a greater segregation of boron impurities into the growing oxide over the N-type field region. Regions of enhanced boron doping are thus formed under the field oxide in the P-type region, but not in the N-type region.
Inventors
- 👤 James R. Pfiester
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 06:23
CPC Classifications
H; H10; H10D; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0165; H10D84/0188; H10D84/02; H10D84/03; H10D84/038; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/0125; H10W10/0126; H10W10/0127; H10W10/10; H10W10/13; H10D84/80; H10D84/82; H10D84/83; H10D84/85; H10D84/859; Y; Y10; Y10S; Y10S438/00; Y10S438/981
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
135 words
A method for fabricating a CMOS device which comprises the steps of: providing a silicon substrate having a first P-type region and a second N-type region at a surface thereof; forming a thin first layer of oxide overlying said surface; forming a second layer of silicon overlying said first layer; forming a patterned third layer of an oxidation resistant material overlying said second layer, said third layer overlying active portions of said first and second regions; implanting boron ions into those portions of said first and second regions which are not overlaid by said third layer; selectively implanting halogen ions into a portion of said second layer overlying said second region and not overlaid by said third layer; and thermally oxidizing said second layer and said substrate to form field oxide regions at said surface.
Claim 2
Independent Claim
135 words
A method for fabricating a CMOS device which comprises the steps of: providing a silicon substrate having a first P-type region and a second N-type region at a surface thereof; forming a thin first layer of oxide overlying said surface; forming a second layer of silicon overlying said first layer; forming a patterned third layer of an oxidation resistant material overlying said second layer, said third layer overlying active portions of said first and second regions; implanting boron ions into those portions of said first and second regions which are not overlaid by said third layer; selectively implanting halogen ions into a portion of said second layer overlying said second region and not overlaid by said third layer; and thermally oxidizing said second layer and said substrate to form field oxide regions at said surface.
Claim 3
Dependent Claim
65 words
The method of claim 1 wherein said step of forming a patterned third layer comprises the steps of: depositing a layer of silicon nitride; depositing a patterned layer of resist material overlying said layer of silicon nitride; etching said layer of silicon nitride using said patterned layer of resist as an etch mask; and retaining said patterned layer of resist as an ion implantation mask.
Claim 4
Dependent Claim
30 words
The method of claim 2 wherein said step of selectively implanting halogen ions comprises the step of implanting chlorine atoms using said patterned layer of resist as an implantation mask.
Claim 5
Independent Claim
136 words
A method for fabricating a CMOS device which comprises the steps of: providing a silicon substrate having a first P-type region and a second N-type region at a surface thereof; forming a thin first layer of oxide overlying said surface; forming a second layer of silicon overlying said first layer; forming a patterned third layer of an oxidation resistant material overlying said second layer, said third layer overlying active portions of said first and second regions and exposing said second layer over field portions of said first and second regions; implanting boron ions into those portions of said first and second regions which are not overlaid by said third layer; selectively removing said second layer overlying said field portions of said second region; and thermally oxidizing said second layer and said field portions of said substrate.
Claim 6
Independent Claim
136 words
A method for fabricating a CMOS device which comprises the steps of: providing a silicon substrate having a first P-type region and a second N-type region at a surface thereof; forming a thin first layer of oxide overlying said surface; forming a second layer of silicon overlying said first layer; forming a patterned third layer of an oxidation resistant material overlying said second layer, said third layer overlying active portions of said first and second regions and exposing said second layer over field portions of said first and second regions; implanting boron ions into those portions of said first and second regions which are not overlaid by said third layer; selectively removing said second layer overlying said field portions of said second region; and thermally oxidizing said second layer and said field portions of said substrate.
Claim 7
Independent Claim
117 words
A method for fabricating a CMOS device which comprises the steps of: providing a silicon substrate having a first P-type region and a second N-type region at a surface thereof; forming a thin first layer of insulator overlying said surface; forming a second layer of silicon overlying said first layer; defining field areas and active areas in each of said first and second regions; ion implanting boron ions into said field areas of each of said first and second regions; and selectively differentially oxidizing field portions of said second region relative to field portions of said first region by removing portions of said second layer overlying said second region; and oxidizing said second layer and said substrate.
Claim 8
Independent Claim
117 words
A method for fabricating a CMOS device which comprises the steps of: providing a silicon substrate having a first P-type region and a second N-type region at a surface thereof; forming a thin first layer of insulator overlying said surface; forming a second layer of silicon overlying said first layer; defining field areas and active areas in each of said first and second regions; ion implanting boron ions into said field areas of each of said first and second regions; and selectively differentially oxidizing field portions of said second region relative to field portions of said first region by removing portions of said second layer overlying said second region; and oxidizing said second layer and said substrate.
Claim 9
Independent Claim
119 words
A method for fabricating a CMOS device which comprises the steps of: providing a silicon substrate having a first P-type region and a second N-type region at a surface thereof; forming a thin first layer of insulator overlying said surface; forming a second layer of silicon overlying said first layer; defining field areas and active areas in each of said first and second regions; ion implanting boron ions into said field areas of each of said first and second regions; and selectively differentially oxidizing field portions of said second region relative to field portions of said first region by selectively implanting halogen ions into said second layer of silicon; and thermally oxidizing said second layer and said silicon substrate.
Claim 10
Independent Claim
119 words
A method for fabricating a CMOS device which comprises the steps of: providing a silicon substrate having a first P-type region and a second N-type region at a surface thereof; forming a thin first layer of insulator overlying said surface; forming a second layer of silicon overlying said first layer; defining field areas and active areas in each of said first and second regions; ion implanting boron ions into said field areas of each of said first and second regions; and selectively differentially oxidizing field portions of said second region relative to field portions of said first region by selectively implanting halogen ions into said second layer of silicon; and thermally oxidizing said second layer and said silicon substrate.
Claim 11
Dependent Claim
29 words
The method of claim 6 wherein said step of selectively implanting comprises the step of implanting chlorine ions into said second layer overlying field areas of said second region.
Claim 12
Independent Claim
131 words
A method for fabricating a CMOS device which comprises the steps of: providing a silicon substrate having a first P-type region and a second N-type region; forming a layer of oxidation resistant material overlying said silicon substrate; patterning said layer of oxidation resistant material to leave said material overlying active portions of said first and second regions and exposing field portions of said first and second regions; ion implanting boron ions into said field portions of said substrate; forming a layer of polycrystalline silicon overlying said P-type region; and selectively differentially oxidizing said substrate by thermally oxidizing said polycrystalline silicon and said exposed field portions of said silicon substrate, the presence of said polycrystalline silicon layer causing said N-type region to be oxidized to a greater extent than said P-type region.
Claim 13
Independent Claim
131 words
A method for fabricating a CMOS device which comprises the steps of: providing a silicon substrate having a first P-type region and a second N-type region; forming a layer of oxidation resistant material overlying said silicon substrate; patterning said layer of oxidation resistant material to leave said material overlying active portions of said first and second regions and exposing field portions of said first and second regions; ion implanting boron ions into said field portions of said substrate; forming a layer of polycrystalline silicon overlying said P-type region; and selectively differentially oxidizing said substrate by thermally oxidizing said polycrystalline silicon and said exposed field portions of said silicon substrate, the presence of said polycrystalline silicon layer causing said N-type region to be oxidized to a greater extent than said P-type region.
Claim 14
Dependent Claim
23 words
The method of claim 8 wherein said step of forming a layer of oxidation resistant material comprises depositing a layer of silicon nitride.
Claim 15
Dependent Claim
23 words
The process of claim 8 wherein said step of forming a layer of polycrystalline silicon comprises depositing a layer of undoped polycrystalline silicon.
References Cited (Backward Citations)
JPS5840839A
Cited
US4447290A
Cited
US4407696A
Cited
US4481705A
Cited
US4570325A
Cited
US4743563A
Cited
JPH06181649A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-10 | 1993-01-09 | 1993-07-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-10 | 1997-01-09 | 1997-07-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-10 | 2001-01-09 | 2001-07-11 | $7700.00 | Window Closed / Lapsed |