Method for preparing tufted pile carpet and adhesive therefor
Assignee: Propex Fabrics Inc
•
Filing: 1987-10-14
•
Granted: 1989-07-04
•
Expires: 2007-10-14
Abstract
Abstract Lamination of a tufted, primary carpet backing to a secondary backing is conducted using a composite hot melt adhesive in sheet form. The composite adhesive overcomes the unfavorable temperature-viscosity gradient within the carpet structure during the lamination process, yielding tufted pile carpets with good tuft encapsulation, tuft bind strength and delamination strength. Also disclosed are hot melt adhesive compositions suitable for use in sheet form in such a process.
Inventors
- 👤 Robert A. Reith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 03:53
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; B32B37/00; B32B37/12; B32B37/1207; B32B5/02; B32B5/06; B32B7/00; B32B7/04; B32B7/12; C; C09; C09J; C09J7/00; C09J7/10; D; D06; D06N; D06N7/00; D06N7/0063; D06N7/0071; D06N7/0078; B32B2262/00; B32B2262/02; B32B2262/0246; B32B2262/0253; B32B2262/0261; B32B2262/0276; B32B2471/00; B32B2471/02; D06N2201/00; D06N2201/02; D06N2201/0245; D06N2201/0254; D06N2201/0263; D06N2203/00; D06N2203/04; D06N2203/042; Y; Y10; Y10T; Y10T428/00; Y10T428/23907; Y10T428/23993
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
206 words
A method for preparing a tufted pile carpet comprising (A) contacting an unmelted composite hot melt adhesive in sheet form, and comprising a primary adhesive layer bonded to a secondary adhesive layer, with a tufted primary carpet backing and a secondary carpet backing fabric such that a stitched surface of the tufted primary carpet backing contacts the primary adhesive layer and the secondary adhesive layer contacts the secondary backing fabric, wherein the primary adhesive layer comprises a first adhesive composition and the secondary adhesive layer comprises a second adhesive composition, said first adhesive composition having a viscosity, at a temperature effective to activate the first and second adhesive compositions without damaging the tufted primary backing or the secondary carpet backing fabric, that is lower than the viscosity of the second adhesive composition at said temperature; (B) heating the contacted composite hot melt adhesive, tufted primary carpet backing and secondary carpet backing fabric to a temperature effective to activate the first and second adhesive compositions without damaging the backings under pressure effective to press the backings into the activated first and second adhesive compositions, and (C) cooling the activated first and second adhesive compositions in contact with the backings to solidify the first and second adhesive compositions.
Claim 2
Independent Claim
206 words
A method for preparing a tufted pile carpet comprising (A) contacting an unmelted composite hot melt adhesive in sheet form, and comprising a primary adhesive layer bonded to a secondary adhesive layer, with a tufted primary carpet backing and a secondary carpet backing fabric such that a stitched surface of the tufted primary carpet backing contacts the primary adhesive layer and the secondary adhesive layer contacts the secondary backing fabric, wherein the primary adhesive layer comprises a first adhesive composition and the secondary adhesive layer comprises a second adhesive composition, said first adhesive composition having a viscosity, at a temperature effective to activate the first and second adhesive compositions without damaging the tufted primary backing or the secondary carpet backing fabric, that is lower than the viscosity of the second adhesive composition at said temperature; (B) heating the contacted composite hot melt adhesive, tufted primary carpet backing and secondary carpet backing fabric to a temperature effective to activate the first and second adhesive compositions without damaging the backings under pressure effective to press the backings into the activated first and second adhesive compositions, and (C) cooling the activated first and second adhesive compositions in contact with the backings to solidify the first and second adhesive compositions.
Claim 3
Dependent Claim
114 words
The method of claim 1 wherein the first adhesive composition comprises about 25 to about 40 weight percent low density polyethylene having a melt index of about 15 to about 30 grams per ten minutes; about 25 to about 40 weight percent of a polyterpene resin having a ring and ball softening point of about 90 to about 105° C.; and about 10 to about 20 weight percent of a paraffin wax having a melting point of about 140° F. to about 165° F.; and about 10 to about 20 weight percent polybutene having a viscosity of about 500 to about 5000 centistokes at 210° F. and up to about 1 weight percent antioxidant.
Claim 4
Dependent Claim
112 words
The method of claim 1 wherein the composite hot melt adhesive comprises an ethylene-vinyl acetate copolymer-based adhesive composition comprising about 30 to about 40 weight percent ethylene-vinyl acetate copolymer containing about 10 to about 35 weight percent vinyl acetate; about 30 to about 40 weight percent polyterpene resin having a ring and ball softening point of about 90° C. to about 105.increment. C.; about 10 to about 25 weight percent microcrystalline wax having a melting point of about 175° F. to about 195°; about 5 to about 15 weight percent polybutene having a viscosity of about 500 to about 5000 centistokes at 210° F.; and up to about two weight percent antioxidant.
Claim 5
Dependent Claim
51 words
The method of claim 3 wherein the ethylene-vinyl acetate copolymer has a melt index of about 100 to about 400 grams per ten minutes and the first adhesive composition contains about 60 to 100 weight percent of said ethylene-vinyl acetate copolymer-based adhesive composition and up to about 40 weight percent filler.
Claim 6
Dependent Claim
53 words
The method of claim 3 wherein the ethylene-vinyl acetate copolymer has a melt index of about 1 to about 5 grams per ten minutes and the second adhesive composition contains about 25 to about 50 weight percent of said ethylene-vinyl acetate copolymer-based adhesive composition and about 75 to about 5 weight percent filler.
Claim 7
Dependent Claim
115 words
The method of claim 5 wherein the first adhesive composition comprises about 25 to about 40 weight percent low density polyethylene having a melt index of about 15 to about 30 grams per ten minutes; about 25 to about 40 weight percent of a polyterpene resin having a ring and ball softening point of about 90° C. to about 105° C.; about 10 to about 20 weight percent of a paraffin wax having a melting point of about 140° F. to about 165° F.; about 10 to about 20 weight percent of a polybutene having a viscosity of about 500 to about 5000 centistokes at 210° F.; and up to about one weight percent antioxidant.
Claim 8
Dependent Claim
144 words
The method of claim 5 wherein the first adhesive composition comprises (A) about 60 to 100 weight percent of an ethylene-vinyl acetate copolymer-based adhesive composition comprising about 30 to about 40 weight percent ethylene-vinyl acetate copolymer containing about 10 to about 35 weight percent vinyl acetate and having a melt index of about 100 to about 400 grams per ten minutes; about 30 to about 40 weight percent polyterpene resin having a ring and ball softening point of about 90° C. to about 105° C.; about 10 to about 25 weight percent microcrystalline wax having a melting point of about 175° F. to about 195° F.; about 5 to about 15 weight percent polybutene having a viscosity of about 500 to abut 5000 centistokes at 210° F.; and up to about two weight percent antioxidant; and (B) up to about 40 weight percent filler.
Claim 9
Dependent Claim
15 words
The method of claim 1 wherein the tufted primary backing comprises a woven polyolefin fabric.
Claim 10
Dependent Claim
20 words
The method of claim 1 wherein the tufts comprise yarns of nylon, polyester, polyolefin, acrylic polymer or a combination thereof.
Claim 11
Dependent Claim
14 words
The method of claim 1 wherein the secondary backing comprises a woven polypropylene fabric.
Claim 12
Independent Claim
215 words
A method for preparing a tufted pile carpet comprising (A) contacting an unmelted composite hot melt adhesive comprising separate sheets of first and second adhesive compositions with a tufted primary carpet backing and a secondary carpet backing fabric such that a stitched surface or the tufted primary carpet backing contacts a first surface of the sheet of first adhesive composition, the secondary carpet backing fabric contacts a first surface of the sheet of second adhesive composition and a second surface of the sheet of first adhesive composition contacts a second surface of the sheet of second adhesive composition, wherein the first adhesive composition has a viscosity, at a temperature effective to activate the first and second adhesive compositions without damaging the tufted primary backing or the secondary carpet backing fabric, that is lower than the viscosity of the second adhesive composition at said temperature; (B) heating the contacted composite hot melt adhesive, tufted primary carpet backing and secondary carpet backing fabric to a temperature effective to activate the first and second adhesive compositions without damaging the backings under pressure effective to press the backings into the activated first and second adhesive compositions, and (C) cooling the activated first and second adhesive compositions in contact with the backings to solidify the first and second adhesive compositions.
Claim 13
Independent Claim
215 words
A method for preparing a tufted pile carpet comprising (A) contacting an unmelted composite hot melt adhesive comprising separate sheets of first and second adhesive compositions with a tufted primary carpet backing and a secondary carpet backing fabric such that a stitched surface or the tufted primary carpet backing contacts a first surface of the sheet of first adhesive composition, the secondary carpet backing fabric contacts a first surface of the sheet of second adhesive composition and a second surface of the sheet of first adhesive composition contacts a second surface of the sheet of second adhesive composition, wherein the first adhesive composition has a viscosity, at a temperature effective to activate the first and second adhesive compositions without damaging the tufted primary backing or the secondary carpet backing fabric, that is lower than the viscosity of the second adhesive composition at said temperature; (B) heating the contacted composite hot melt adhesive, tufted primary carpet backing and secondary carpet backing fabric to a temperature effective to activate the first and second adhesive compositions without damaging the backings under pressure effective to press the backings into the activated first and second adhesive compositions, and (C) cooling the activated first and second adhesive compositions in contact with the backings to solidify the first and second adhesive compositions.
Claim 14
Dependent Claim
113 words
The method of claim 11 wherein the first adhesive composition comprises about 25 to about 40 weight percent low density polyethylene having a melt index of about 15 to about 30 grams per ten minutes; about 25 to about 40 weight percent of a polyterpene resin having a ring and ball softening point of about 90° C. to about 105° C.; about 10 to about 20 weight percent of a paraffin wax having a melting point of about 140° F. to about 165° F.; about 10 to about 20 weight percent polybutene having a viscosity of about 500 to about 5000 centistokes at 210° F. and up to about one weight percent antioxidant.
Claim 15
Dependent Claim
113 words
The method of claim 11 wherein the composite hot melt adhesive comprises an ethylene-vinyl acetate copolymer-based adhesive composition comprising about 30 to about 40 weight percent ethylene-vinyl acetate copolymer containing about 10 to about 35 weight percent vinyl acetate; about 30 to about 40 weight percent polyterpene resin having a ring and ball softening point of about 90° C. to about 105° C.; about 10 to about 25 weight percent microcrystalline wax having a melting point of about 175° F. to about 195° F.; about 5 to about 15 weight percent polybutene having a viscosity of about 500 to about 5000 centistokes at 210° F.; and up to about two weight percent antioxidant.
Claim 16
Dependent Claim
51 words
The method of claim 13 wherein the ethylene-vinyl acetate copolymer has a melt index of about 100 to about 400 grams per ten minutes and the first adhesive composition contains about 60 to 100 weight percent or said ethylene-vinyl acetate copolymer-based adhesive composition and up to about 40 weight percent filler.
Claim 17
Dependent Claim
53 words
The method of claim 13 wherein the ethylene-vinyl acetate copolymer has a melt index of about 1 to about 5 grams per ten minutes and the second adhesive composition contains about 25 to about 50 weight percent of said ethylene-vinyl acetate copolymer-based adhesive composition and about 75 to about 50 weight percent filler.
Claim 18
Dependent Claim
113 words
The method of claim 15 wherein wherein the first adhesive composition comprises about 25 to about 40 weight percent low density polyethylene having a melt index of about 15 to about 30 grams per ten minutes; about 25 to about 40 weight percent of a polyterpene resin having a ring and ball softening point of about 90° C. to about 105° C.; about 10 to about 20 weight percent paraffin was having a melting point of about 140° F. to about 165° F.; about 10 to about 20 weight percent of a polybutene having a viscosity of about 500 to 5000 centistokes at 210° F.; and up to about one weight percent antioxidant.
Claim 19
Dependent Claim
144 words
The method of claim 15 wherein the first adhesive composition comprises (A) about 60 to 100 weight percent of an ethylene-vinyl acetate copolymer-based adhesive composition comprising about 30 to about 40 weight percent ethylene-vinyl acetate copolymer containing about 10 to about 35 weight percent vinyl acetate and having a melt index of about 100 to about 400 grams per ten minutes; about 30 to about 40 weight percent polyterpene resin having a ring and ball softening point of about 90° C. to about 105° C.; about 10 to about 25 weight percent microcrystalline wax having a melting point of about 175° F. to about 195° F.; about 5 to about 15 weight percent polybutene having a viscosity of about 500 to about 5000 centistokes at 210° F.; and up to about two weight percent antioxidant; and (B) up to about 40 weight percent filler.
Claim 20
Dependent Claim
15 words
The method of claim 11 wherein the tufted primary backing comprises a woven polyolefin fabric.
Claim 21
Dependent Claim
20 words
The method of claim 11 wherein the tufts comprise yarns of nylon, polyester, polyolefin, acrylic polymer or a combination thereof.
Claim 22
Dependent Claim
14 words
The method of claim 11 wherein the secondary backing comprises a woven polypropylene fabric.
References Cited (Backward Citations)
US3110905A
Cited
US3542613A
Cited
US3542612A
Cited
US3645948A
Cited
US3551231A
Cited
US3583936A
Cited
US3684600A
Cited
US3734800A
Cited
US3676280A
Cited
US3734812A
Cited
US3900361A
Cited
US3733226A
Cited
US3745054A
Cited
US3914489A
Cited
US3911185A
Cited
US4012547A
Cited
US3940525A
Cited
US4243568A
Cited
US4191798A
Cited
US4508771A
Cited
US4434261A
Cited
US4552794A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-03 | 1993-01-02 | 1993-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-03 | 1997-01-02 | 1997-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-03 | 2001-01-02 | 2001-07-04 | $7700.00 | Window Closed / Lapsed |