Foamed plastic materials

Claim 1

A method for the production of a foamed phenolic resin material comprising (i) effecting a curing reaction between (a) a liquid phenolic resole containing not more than 35% by weight of water and having a reactivity number of at least 1, where reactivity number is defined as 10/x where x is the time in minutes required for a mixture of 5 ml of the resole and 10% by weight of the resole of a 66-67% aqueous solution of p-toluene sulfonic acid to become hard to the touch after the mixture has been prepared in a test tube and the test tube containing the mixture has been immersed in a water bath which is at 60° C., and (b) an amount of a strong acid suitable as a hardener for said resole which is equivalent to 2 to 20 parts, per 100 parts of the phenol/aldehyde condensation product in the resole, by weight, of p-toluene sulfonic acid, in the presence of (c) a finely divided inert and insoluble particulate solid which has a particle size of 0.5 to 800 microns and is present in an amount of from 20 to 250% by weight of the liquid resole and is substantially uniformly dispersed through the mixture of resole and hardener; and optionally (d) a compound having two active hydrogen atoms and capable of reacting with the phenol/aldehyde condensation product in the resole, the temperature of the mixture containing resole and hardener due to any applied heat not exceeding 85° C. and said temperature and the concentration of the acid hardener being such that at least one compound present in the resole or generated as a by-product of the curing reaction is volatilized within the mixture whereby to cause the mixture to foam before the mixture sets, and (iii) recovering a foamed phenolic resin product having a cellular texture of substantially uniform cell size and being substantially free of blow holes, wherein the mixture of liquid phenolic resole, hardener and particulate solid includes an added blowing agent in a small amount insufficient to have an adverse effect on the foaming reaction and insufficient to achieve a foamed product when used by itself.

Claim 2

A method for the production of a foamed phenolic resin material comprising (i) effecting a curing reaction between (a) a liquid phenolic resole containing not more than 35% by weight of water and having a reactivity number of at least 1, where reactivity number is defined as 10/x where x is the time in minutes required for a mixture of 5 ml of the resole and 10% by weight of the resole of a 66-67% aqueous solution of p-toluene sulfonic acid to become hard to the touch after the mixture has been prepared in a test tube and the test tube containing the mixture has been immersed in a water bath which is at 60° C., and (b) an amount of a strong acid suitable as a hardener for said resole which is equivalent to 2 to 20 parts, per 100 parts of the phenol/aldehyde condensation product in the resole, by weight, of p-toluene sulfonic acid, in the presence of (c) a finely divided inert and insoluble particulate solid which has a particle size of 0.5 to 800 microns and is present in an amount of from 20 to 250% by weight of the liquid resole and is substantially uniformly dispersed through the mixture of resole and hardener; and optionally (d) a compound having two active hydrogen atoms and capable of reacting with the phenol/aldehyde condensation product in the resole, the temperature of the mixture containing resole and hardener due to any applied heat not exceeding 85° C. and said temperature and the concentration of the acid hardener being such that at least one compound present in the resole or generated as a by-product of the curing reaction is volatilized within the mixture whereby to cause the mixture to foam before the mixture sets, and (iii) recovering a foamed phenolic resin product having a cellular texture of substantially uniform cell size and being substantially free of blow holes, wherein the mixture of liquid phenolic resole, hardener and particulate solid includes an added blowing agent in a small amount insufficient to have an adverse effect on the foaming reaction and insufficient to achieve a foamed product when used by itself.

Claim 14

A method of obtaining a foamed phenolic resin by curing a phenolic resole comprising phenol/aldehyde condensation product under conditions such that at least one volatilisable compound which is a component of the resole and/or is formed as a by-product of the curing reaction is volatilised before the resole has solidified, and wherein the boiling of the resole which leads to the production of a coarse and non-uniform cellular structure containing blow holes is at least substantially suppressed by employing a liquid phenolic resole containing not more than 35% by weight by water and having a reactivity number of at least 1, where reactivity number is defined as 10/x, and x is the time in minutes required for a mixture of 5 ml of the resole and 10% by weight of the resole of a 66-67% weight aqueous solution of p-toluene sulfonic acid to become hard to the touch after the mixture has been prepared in a test tube and the test tube containing the mixture has been immersed in a water bath which is at 60° C., and effecting a curing reaction between said resole and an amount of a strong acid hardener equivalent to from 2 to 20 parts, per 100 parts of the phenol/aldehyde condensation product in the resole, by weight, of p-toluene sulfonic acid, in the presence of an amount in the range of 20% to 250% by weight of the liquid phenolic resole of a finely divided inert and insoluble particulate solid which has a particle size in the range of 0.5 to 800 microns and which is substantially uniformly dispersed through the mixture of resole and hardener, further in the presence of an added blowing agent in an amount insufficient to have an adverse effect on the foaming reaction and insufficient to achieve a foamed product when used by itself, and optionally in the presence of a compound having two active hydrogen atoms and capable of reacting with the phenol/aldehyde condensation product in the resole, the temperature of the mixture containing said resole and said acid hardener due to any applied heat being in the range 10° to 65° C., whereby a solid foamed phenolic resin product having a cellular texture of substantially uniform cell size substantially free of blow holes is formed.

Claim 15

A method of obtaining a foamed phenolic resin by curing a phenolic resole comprising phenol/aldehyde condensation product under conditions such that at least one volatilisable compound which is a component of the resole and/or is formed as a by-product of the curing reaction is volatilised before the resole has solidified, and wherein the boiling of the resole which leads to the production of a coarse and non-uniform cellular structure containing blow holes is at least substantially suppressed by employing a liquid phenolic resole containing not more than 35% by weight by water and having a reactivity number of at least 1, where reactivity number is defined as 10/x, and x is the time in minutes required for a mixture of 5 ml of the resole and 10% by weight of the resole of a 66-67% weight aqueous solution of p-toluene sulfonic acid to become hard to the touch after the mixture has been prepared in a test tube and the test tube containing the mixture has been immersed in a water bath which is at 60° C., and effecting a curing reaction between said resole and an amount of a strong acid hardener equivalent to from 2 to 20 parts, per 100 parts of the phenol/aldehyde condensation product in the resole, by weight, of p-toluene sulfonic acid, in the presence of an amount in the range of 20% to 250% by weight of the liquid phenolic resole of a finely divided inert and insoluble particulate solid which has a particle size in the range of 0.5 to 800 microns and which is substantially uniformly dispersed through the mixture of resole and hardener, further in the presence of an added blowing agent in an amount insufficient to have an adverse effect on the foaming reaction and insufficient to achieve a foamed product when used by itself, and optionally in the presence of a compound having two active hydrogen atoms and capable of reacting with the phenol/aldehyde condensation product in the resole, the temperature of the mixture containing said resole and said acid hardener due to any applied heat being in the range 10° to 65° C., whereby a solid foamed phenolic resin product having a cellular texture of substantially uniform cell size substantially free of blow holes is formed.