Abstract The non-flammable rigid foam e.g. used as a building material complies with the requirements of DIN 4102 and which provides a non-toxicity of the combustion fumes according to DIN 53436. It has a mass ratio of resin component: filler of at least 1:2.5 and a bulk density amounting to 50 kg/m 3 to 450 kg/m 3 . The resin component is formed by reaction of 50-62 mass parts resolic resin 0-15 mass parts furane resin 25-40 mass parts furfuryl alcohol 0.5-11.5 mass parts foam stabilizer including 14-17 mass parts per 100 mass parts of resin component plus filler of a curing agent mixture of phosphoric acid, boronhydrofluoric acid, p-toluene sulphonic acid and water. The filler used is a mixture of 40-55 mass % aluminium hydroxide 10-35 mass parts boric acid 2-7 mass parts sodium tetraborate 5-10 mass parts manganese dioxide 1-5 mass parts copper-II-oxide 1-4 mass parts magnesium hydroxysilicate 1-2 mass parts aluminium silicate.
A non-flammable rigid foam on the basis of phenolic resin and for furane resin, containing aluminium hydroxide as a filler, the resin component being formed by reaction of phenolic resin, furfuryl alcohol and a sulpho acid as curing agent, wherein the mass ratio of resin substance: filler substance is at least 1:2,5 and up to 1:3,2 and the bulk density is from 50 kg/m 3 to 450 kg/m 3 and the resin compound is the reaction product obtained by the reaction with one another of 50-62 mass parts resolic resin 0-15 mass parts furanic resin 25-40 mass parts furfuryl alcohol 0.5-1.5 mass parts foam stabiliser including 14-17 parts by mass per 100 parts by mass of resin component+filler substance of a curing agent mixture composed of '-50 mass parts phosphoric acid 12-17 mass parts boron hydrofluoric acid 6-7 mass parts p-toluene sulphonic acid or p-phenol sulphonic acid and 32-35 mass parts water.
Claim 2
Dependent Claim
152 words
A non-flammable rigid foam on the basis of phenolic resin and for furane resin, containing aluminium hydroxide as a filler, the resin component being formed by reaction of phenolic resin, furfuryl alcohol and a sulpho acid as curing agent, wherein the mass ratio of resin substance: filler substance is at least 1:2,5 and up to 1:3,2 and the bulk density is from 50 kg/m 3 to 450 kg/m 3 and the resin compound is the reaction product obtained by the reaction with one another of 50-62 mass parts resolic resin 0-15 mass parts furanic resin 25-40 mass parts furfuryl alcohol 0.5-1.5 mass parts foam stabiliser including 14-17 parts by mass per 100 parts by mass of resin component+filler substance of a curing agent mixture composed of '-50 mass parts phosphoric acid 12-17 mass parts boron hydrofluoric acid 6-7 mass parts p-toluene sulphonic acid or p-phenol sulphonic acid and 32-35 mass parts water.
Claim 3
Dependent Claim
58 words
A non-flammable rigid foam according to claim 1, wherein the filler substance is composed of 40-55 mass parts aluminium hydroxide 10-35 mass parts boric acid 2-7 mass parts sodium tetraborate 5-10 mass parts manganese dioxide 1-5 mass parts copper-II oxide 1-4 mass parts magnesium hydroxide silicate 1-2 mass parts aluminium silicate the ratio of borate:boric acid being 1:5.
Claim 4
Dependent Claim
16 words
A non-flammable rigid foam according to claim 1 wherein the foam stabiliser is pyrogenic silicic acid.
Claim 5
Dependent Claim
33 words
A non-flammable rigid foam according to claim 1, wherein the aluminium hydroxide has a screen analysis curve according to the following screen passing data 25% 5.5 μm 50% 52.0 μm 75% 80.0 μm.